FAQ

What brand of easy cutting and deformation of aluminum bar?

Aluminum Alloy with the grade increased, the hardness is gradually rising, can try the next 6 series such as 6061, the machining deformation with selection of cutting fluid, because the process will produce high temperature, Aluminum Alloy heating become soft, resulting in deformation and sticking to the knife and other issues, semi synthetic cutting fluid has good cooling, lubrication and cleaning effect of processing, the most suitable Aluminum Alloy,

What is the difference between aluminum bar LF21 (Y2) and 7005?

The general law is used in the first round, to strive for speed. The law is min and added. As for the vampire, it was the most you can have 5 skills, skills, suitable for their own play book.

What are the specifications of aluminum bars?

Aluminum, aluminum rod, aluminum, aluminum strip, material: 5056, 5052, 5050, 6061-T3, 6061-T5, 6061-T6, 6063-T3, 6063-T5, 6063-T6, LF10, LY11, LY12, 1100, 1060, 1070, 5356, 700570097075, 2011, 2017, 2024, 3003, 5154, 5005, 6011, 6082. 70030.

What are the elements of the national standard aluminum rod 6063t5?

The method is available through water or water quenching of the thin-walled parts (6<3mm. You can also implement the wind quenching).Good weldability and corrosion resistance, no tendency to stress corrosion cracking. Al-Mg-Si alloy is the only alloy that has not found stress corrosion cracking in heat treated reinforced aluminum alloyAfter processing, the surface is very smooth and easy to anodizing and coloring. Its disadvantage is that if it is stayed at room temperature for a period of time after quenching, it will have an adverse effect on the strength (parking effect)

Imported 7075 aluminum plate, 7075 aluminum alloy, 7075 aluminum bar, original quality guarantee, Shanghai where to sell?

Guangdong Nanyang metal material Co. Ltd. (domestic) direct selling a variety of imported aluminum / aluminum / aluminum / aluminum / rod with rust proof aluminum / aluminum / aluminum and other varieties complete specifications, such as 70757075-T67075-T65150835083-H1125083-H325083-H2260616061-T66061-T65160636063-T46063-T4516063-T650525052-T145052-T24, 1A30, 1A99, 1a97, 1a95, 1a93, 1a90, 1a85, 1A80, 1a80a, 10701100, 2A04, 2A06, 2A10 2A12, 2A162011201420172017A, 211722182618221920242124, 3A2130033103300430053105, 4A0140044032, 5A01, 5A02, 5A03, 5A05, 5A12, 5A30, 5A33500550505251505250545054a, 54545554575450565356545650825182508351835086, 6A02, 6A516005, 6. 060606160636082, 7A01, 7A03, 7A04, 7A05, 7A52700370057009702070227050707570727075707971747475, 8A0680118089, LF2, LF3, LF5, LC4, LD2, LD4, LD5, LD7, LD9, LY12 etc. all kinds of aluminum, aluminum rod, aluminum strip, Aluminum Alloy.

Negative effects of zinc on aluminum bars

The equilibrium phase diagram of Al-Zn alloy shows that the solubility of zinc in aluminium is 31.6%, while the solubility of aluminum decreases to 5.6% at 125 when the rich aluminum fraction reaches 275.When zinc is added to aluminum alone, the strength of aluminum alloy increases very much under the condition of deformation, and the tendency of stress corrosion cracking exists at the same time, which limits its application.The addition of zinc and magnesium to aluminum forms a strengthening phase, Mg/Zn2, which has an obvious strengthening effect on the alloy.

Is the LC4 aluminum bar the same as the 7075 aluminum bar?

LC4 is the old name for 7A04 aluminum bars. The chemical composition is a little different, but the performance should be the same

What can make the aluminum bar surface shiny?

Aluminum is more complex. Aluminum itself is soft. Hand polishing is difficult to reach the mirror surface. Generally, the grinding force of the machine at high speed is used to reach the mirror surface