High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
- Ref Price:
-
- Loading Port:
- Qingdao Port
- Payment Terms:
- TT or LC
- Min Order Qty:
- 25M.T. m.t.
- Supply Capability:
- 200000M.T./Year m.t./month
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
You Might Also Like
1. Sizes of High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
Item | SIZES | |||||||||||||
φ17 | φ20 | φ25 | φ30 | φ40 | φ50 | φ60 | φ70 | φ80 | φ90 | φ100 | φ110 | φ120 | φ130 | |
Tolerance | +1.0 | +2.0 | +3.0 | +3.5 | ||||||||||
-1.0 | -1.0 | -1.0 | -1.5 | |||||||||||
Difference between max diam and min diam | ≤1.0 | ≤2.0 | ≤3.0 | |||||||||||
2. Chemical Composition of High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
|
Material |
C |
Si |
Cr |
Mn |
S |
P |
X-5 | Cr-22-32% | 2.0-2.8 | ≤1.0 | 22-32 | 0.5-2.0 | ≤0.06 | ≤0.08 |
X-6 | Cr-17-22% | 2.0-2.8 | ≤1.0 | 17-22 | 0.5-2.0 | ≤0.06 | ≤0.08 |
X-7 | Cr-15-17% | 2.2-3.0 | ≤1.0 | 15-17 | 0.5-2.0 | ≤0.06 | ≤0.08 |
X-8 | Cr-11-14% | 2.2-3.2 | ≤1.0 | 11-14 | 0.5-2.5 | ≤0.06 | ≤0.08 |
X-9 | Cr-5-10% | 2.1-3.2 | ≤1.2 | 5-10 | 0.5-1.5 | ≤0.06 | ≤0.08 |
X-10 | Cr-1-3% | 2.2-3.5 | ≤1.2 | 1.5-3.0 | 0.5-1.5 | ≤0.06 | ≤0.08 |
3. Physical Property of High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
Name
|
Material
|
Impact Test Ak.J/cm |
Endurance Test times (5m) | Hardness (HRC) | |||
Diam25-60mm | Diam70-100mm | ||||||
Quenching | Unquenching | Quenching | Unquench ing | ||||
X-5 | Cr-22-32% | ≥4 | ≥10000 | ≥60 | ≥49 | ≥60 | ≥48 |
X-6 | Cr-17-22% | ≥4 | ≥10000 | ≥60 | ≥49 | ≥60 | ≥48 |
X-7 | Cr-15-17% | ≥4 | ≥10000 | ≥60 | ≥49 | ≥58 | ≥48 |
X-8 | Cr-11-14% | ≥3 | ≥10000 | ≥58 | ≥49 | ≥56 | ≥48 |
X-9 | Cr-5-10% | ≥3 | ≥8000 | - | ≥48 | - | ≥48 |
X-10 | Cr-1-3% | ≥2 | ≥8000 | - | ≥48 | - | ≥45 |
4.Applied Field of High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
1) Metal mining in mines,2) power stations,3) Chemical engineering
5. Photos of High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
- Q:What's the density of the cast iron? The density is thin and the density is thin
- Uneven casting density is caused by uneven shrinkage of the casting during solidification.
- Q:Would you please tell me how to use casting parts for a year?The cast of an aircraft wing needs to be put aside for a year before it breaks;Does anyone know why?
- There are various casting stresses after casting, which can be divided into two kinds: thermal stress and shrinkage stress. In a long time placed in the atmosphere, called aging treatment.Aging treatment is an effective measure to eliminate casting stress. Aging is divided into natural aging, thermal aging and resonance aging.1, the so-called natural aging, the casting is placed in the open field for more than half a year, so that the internal stress relief.
- Q:our factory now produces steel castings in the use of polishing directly after spraying processing, but the powder sprayed 15But the spray powder touched off what is the reason we are not very strict requirements not only need to peel off bubbles can also, because our products are steel castings so we use steam hole sludge put on. Do not know if this spray treatment has no effect to thank friends with us!
- The pre treatment temperature and the quality of plastic powder are likely to be problems
- Q:the parts of the threaded hole is casting, casting the hole directly, and then tapping or casting, and then punch 10When the casting is ready, punch it again before tapping it Is the hole casting good or is it punched and tapped on the drilling machine after casting?
- Single for this problem, the direct casting out of course good. But many times because of the limitations of the process, so we choose the post-processing hole
- Q:Why do casting parts have air holes?
- First, from the source, tools, raw material drying, in the process of melting into the reaction gas, another influence is pouring process, such as high temperature solidification gas dissolved too much after not excluded. The method can adjust the pouring temperature properly, control the source of gas (drying and controlling the inoculant, especially the content of magnesium), and add cooling iron to change the solidification mode. It depends on what kind of casting you are. You can't make it clear at once. And molding sand relationship is mainly water content and permeability, brush coating resin content.
- Q:What is the difference between casting and stamping parts?
- Separation process is also called blanking, the purpose is to make the stamping parts along a certain contour line from the sheet metal separation, at the same time guarantee the quality requirements of the separation section. Stamping is a highly efficient production methods, the use of compound die, especially the multi station progressive die stamping process can be completed in a multi machine, realized by belt uncoiling, leveling, punching, forming and finishing automatic production. High production efficiency, good working conditions, low production costs, can produce hundreds of parts per minute.
- Q:After reaming, the roughness can reach several levels, that is to say, the sample.Casting parts in rocker arm drilling, reaming, roughness, block. After reaming, the roughness can reach several levels, that is to say, the sample.
- Radial drilling machine can achieve boring, reaming function, but as much as you want, according to your requirements and material to determine!
- Q:What is normalizing, annealing, tempering, quenching? What is the difference between forging parts and casting parts?
- For the nodular cast iron, the hardness, strength and wear resistance are improved, such as used in the manufacture of automobile, tractor, diesel engine crankshaft, connecting rod and other important parts. A normalizing and hypereutectoid ball annealing before, can eliminate the mesh two cementite spheroidizing annealing, to ensure that all spheres of cementite. Annealing is a metal heat treatment process, which means the metal is slowly heated to a certain temperature, sufficient for a long time, and then cooled at an appropriate speed. The purpose is to reduce hardness, improve machinability, eliminate residual stress, stabilize size, reduce deformation and crack tendency, refine grain, adjust microstructure and eliminate tissue defects. Its purpose: (1) reduce hardness and improve machinability; (2) eliminate residual stress, stabilize size, reduce deformation and crack tendency; (3) refine grain, adjust microstructure and eliminate tissue defects. In production, annealing process is widely used.
- Q:What kind of casting process is used for cast iron parts? And what are the cast steel parts adopted?
- The types and uses of foundry sand according to the mineral composition of different silica sand and non siliceous sand is divided into two categories. The main mineral composition of silica SiO2.: natural silica sand used for non-ferrous metal casting, cast iron and steel castings in small sand and core sand. The selection of natural silica sand: used in organic matter as the binder of various sand and core sand. The artificial sand for sand and core sand castings. Non siliceous sand and non siliceous sand have many kinds and different uses. Limestone sand: crushed by limestone, the main mineral composition is CaCO3, used for casting sand and core sand. Zirconium sand: the main mineral composition is ZrO2 SiO2, used for large steel castings and alloy steel pieces of core sand or sand surface sand, or powder used as coating. Magnesia: the main mineral composition is MGO, used for high manganese steel casting surface sand, core sand, and its powder can be used as coating. Chromite ore: the main mineral composition is chromite FeO. Cr2O3, used for large or special casting steel surface sand, core sand, its powder can be used as coating.
- Q:Is 316 casting better than 304 casting?
- It is comprehensive. There is no simple comparison of the material to determine the degree of difficulty in processing
CMD is one of the largest manufacturers and professional exporters of forged grinding balls and cast grinding balls in China, with an annual output of 50,000 tons. Now, there are 180 employees in our company, with an area of 20,000 square meters. Our products are mainly exported to more than 20 countries in the world, such as Africa, South America, Asia, and Australia.
1. Manufacturer Overview |
|
|---|---|
| Location | Shandong, China |
| Year Established | 1983 |
| Annual Output Value | Above US$100 Million |
| Main Markets | South Asia, South Asia, Central America, Western Europe, Eastern Asia, Mid East, Oceania, Africa |
| Company Certifications | ISO9001;IS014001 Certificate |
2. Manufacturer Certificates |
|
|---|---|
| a) Certification Name | |
| Range | |
| Reference | |
| Validity Period | |
3. Manufacturer Capability |
|
|---|---|
| a)Trade Capacity | |
| Nearest Port | Qingdao Port |
| Export Percentage | |
| No.of Employees in Trade Department | 3-5 People |
| Language Spoken: | English；Chinese；Japanese；Korean |
| b)Factory Information | |
| Factory Size: | Above 20,000 square meters |
| No. of Production Lines | 8 |
| Contract Manufacturing | Grinding steel balls;Grinding steel cylpebs;Grinding media;Grinding meida ball |
| Product Price Range | Average |
Send your message to us
High Chromium Cast Grinding Ball made in China with Top Quality Steel as Raw Material for Mines and Cement Plant
- Ref Price:
-
- Loading Port:
- Qingdao Port
- Payment Terms:
- TT or LC
- Min Order Qty:
- 25M.T. m.t.
- Supply Capability:
- 200000M.T./Year m.t./month
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
Similar products
High Chromium Cast Grinding Ball with Top Quality Steel as Raw Material withch can be uesed in Mines