Silica Fire Bricks for Coke Oven and Hot Blast Stove

Silica Fire Bricks for Coke Oven and Hot Blast Stove System 1

Silica Fire Bricks for Coke Oven and Hot Blast Stove System 2

Silica Fire Bricks for Coke Oven and Hot Blast Stove

Ref Price:

Loading Port:: Shanghai

Payment Terms:: TT OR LC

Min Order Qty:: 15 pallet

Supply Capability:: 30000 pallet/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$High Alumina Brick SK38 - High Quality Refractory Material$

High Alumina Brick SK38 - High Quality Refractory Material

Alumina Silicate Fire Brick for Glass Furnace Silica Bricks

Silica Brick for Glass Industry

$Alumina Silica Refractory Silica Brick for Carbon Furnace$

Alumina Silica Refractory Silica Brick for Carbon Furnace

High Alumina Brick and Insulation Brick for Kinds of Glass Furnaces

Cement Kiln Magnesite Bricks

Fireclay Brick for Hot Blast Stove

High Chrome Magnesite Chrome Brick for Glass Industry

General Information

The silica brick can be widely used in coke oven, hot blast furnace, glass furnace and carbon furnace. In glass industry, it is mainly employed to build the doghouse crown, suspended wall of channel, top crown and inlet sealing. In metallurgy industry, it is adopted as the nozzle brick

Features

1.High purity

2.Long service life

3.Accurate size tolerance

4.Pure color

5. Luster appearance

6..Good thermal conductivity
7.Good creep resistance

Application of the Acid refractory silica bricks

Silica brick is mainly used for Coke oven, glass kiln, hot-blast stove, tunnel kiln,Acidic furnace non-ferrous metal smelting and some other thermotechnical equipment in good furnace building materials.

Physical & chemical indexes of the refractory silica bricks

General silica brick:Siliceous refractory products used for various large coke oven, glass kiln stove, hot air stove, etc.
Item	GZ-96	GZ-95	GZ-94
SiO2 % ≥	96	95	94
Fe2O3 % ≤	1	1.2	1.4
Refractoriness °C≥	1710	1710	1690
Apparent porosity % ≤	22	22	24
Cold crushing strength Mpa ≥	29.4	24.5	19.6
Refractoriness under load, 0.2MPa, °C≥	1660	1650	1640
True density g/cm3 ≤	2.34	2.35	2.35

Q:What is the main material of silica brickIt's common, the kind we see so often!: An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.

Q:How to improve the thermal conductivity of the coke silicabrick rate?: To improve the thermal conductivity of silica brick for coke oven rate method:Manufacture of high density and high thermal conductivity of silica brick, adding additives such as CuO, Cu2O, TiO2, Fe2O3, (FeO), can improve the thermal conductivity of silica brick.

Q:Why will expand when heated brick: In the process of SiO2 drying, the four crystalline transformation points of 117, 163, 180~270 and 573 DEG C are found, among which the volume expansion caused by the 180~270 is the largest.

Q:Such purpose and scope please give me detailed points thank you because I am learning stage: Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on. The properties and process of silica crystal with SiO2 transformation is closely related, therefore, the proportion of it is one of the important quality indexes of silica brick. General requirements below 2.38, high quality silica brick should be less than 2.35. The true density is small, reflecting a large number of scale quartz and square quartz in the brick, the residual quartz is small, so the residual line expansion is small, and the strength is decreased in useThe raw materials for the manufacture of silica brick. The higher the SiO2 content of silica raw material, the higher the refractoriness. The most harmful impurities are Al2O3, K2O, Na2O and so on. They seriously reduce the refractoriness of refractory products. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer (e.g. millscale, lime) and binder (such as molasses, sulfite pulp waste liquid), after mixing, molding, drying, sintering and other processes in the system.

Q:Glass kiln brick for physical and chemical indicators?: Glass kiln with high quality silica brick products according to the standard JC/T615-1996, the single brick is divided into 3 grades: XBG-96, ZBG-96, DBG-96.

Q:High temperature refractory material?: Basic refractories in Magnesium Oxide and calcium oxide as the main component, the main products are magnesia brick, magnesia chrome brick, magnesia zirconia brick, magnesia brick, magnesia spinel brick, magnesia calcium brick, dolomite brick and the latest development of magnesia spinel brick and so on. With Magnesium Oxide (MgO) more than 80% of the refractory brick called magnesia brick,

Q:The specific content is what gb/t2608-2012 brick: Quality assessment procedures, packaging, marking, transport, storage, and quality certificates. Suitable for siliceous refractory bricks.

Q:The hot blast stove when the temperature did not rise against the brick interface decreased: Insulation of hot blast stove, key insulation silica brick hot stove, hot blast stove is shutdown or need repairing in blast furnace.

Q:The United States of our brick anti-dumping duties?: . According to the relevant legal procedures, the United States International Trade Commission will make a final ruling on the anti dumping industrial injury before January 6, 2014, if an affirmative determination, the U.S. Department of Commerce will be involved in product release tax anti-dumping order.

Q:How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?: Mainly from the impurities to determine how much, generally less impurity single color brick.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range