Silica brick for coke oven

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

The silica bricks for HBS
Silica fire brick for coke oven
High density silica fire brick
Semi-silics fire brick for coke oven

1.Silica brick manufature.
2.High refractoriness under load.
3.High heat conductivity.
4.Good thermal shock resistance.

Tech Data

Silica brick for glass furnace
Item:		GF-96A	GF-96B	GF-95A	GF-95B
SiO 2		≥96	≥96	≥95	≥95
Fe 2 O 3		≤0.8	≤1.0	≤1.2	≤1.2
Apparent porosity %		≤22(24)
Cold Crushing Strength MPa	Brick below20KG	≥35(30)
	Brick ≥20KG	≥30(25)
Refractoriness under load ºC		≥1680	≥1670	≥1660	≥1650
True density g/cm ³		≤2.34	≤2.34	≤2.35	≤2.35

Silica brick for coke oven
Item:	CO-94A	CO-94B
SiO2: %	≥94	≥94
Al 2 O 3 : %	≤ 1.5	≤ 1.5
Fe2O3: %	≤ 1.5	≤ 1.5
Refractoriness under load 0.2Mpa	≥ 1650ºC	≥ 1650ºC
Apparent porosity: %	≤ 22	≤ 24
Bulk density: g/cm ³	≤ 2.34	≤ 2.35
Cold crushing strength: MPa	≥30	≥25
Permanent linear change % (1450ºC ×2h)	0~0.2	0~0.2
Thermal expansion(1000ºC)	≤1.28	≤1.30

Silica brick for hot blast furnace
Item	HBF-95
SiO2	≥ 95
Al2O3	≤ 1.0
Fe2O3	≤1.3
Apparent porosity %	≤22(24)
Cold crushing strength MPa	≥45(35)
Remaining quarts %	≤1.0
Refractoriness under load ºC	≥1650
Creep(0.2Mpa ×1550ºC×50h) %	≤0.8
Thermal expansion coefficient (1000ºC) %	≤1.25
Apparent density g/cm ³	≤2.32

Q: Because of the recent relates to this industry, by way of learning to name for all raw materials, I hope knowledgeable friends exhibitions, thank you.: Acidic materialMainly siliceous materials, such as quartz, tridymite and cristobalite, chalcedony, flint, opal, white quartzite, silica sand, diatomaceous earth, silicon oxide contained in these siliceous materials (SiO2) at least 90%, pure raw materials are silicon oxide as high as 99% or more. Siliceous materials at high temperature is the acidic nature of chemical dynamics, when the presence of metal oxide, or when in contact with the chemical reaction, and combined with a fusible silicate. Therefore, if there is a small amount of metal oxide in siliceous material, it will seriously affect its thermal resistance.

Q: The hot blast stove when the temperature did not rise against the brick interface decreased: Different insulation methods can be adopted according to the length of the stop time and the location and equipment of the overhaul. Gold, refractory material factory specializing in the production of various specifications of brick

Q: The specific content is what gb/t2608-2012 brick: Quality assessment procedures, packaging, marking, transport, storage, and quality certificates. Suitable for siliceous refractory bricks.

Q: What is the main material of silica brickIt's common, the kind we see so often!: Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into phosphorus and quartz. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.

Q: Glass kiln brick for physical and chemical indicators?: Glass kiln with high quality silica brick products according to the standard JC/T615-1996, the single brick is divided into 3 grades: XBG-96, ZBG-96, DBG-96.

Q: Which material is good for furnace refractory?: Neutral refractory is mainly composed of alumina, chromium oxide or carbon. Corundum products containing more than 95% of alumina are a kind of high quality refractory materials with a wide range of uses. Chrome brick with chromium oxide as its main component has good corrosion resistance, but its thermal shock resistance is poor, and its deformation temperature is lower at high temperature. Carbon refractories with carbon bricks, graphite and silicon carbide products, low coefficient of thermal expansion, high thermal conductivity, good thermal shock resistance, high strength, resistance to acid and salt corrosion, especially weak acid has good resistance, without wetting of the metal and slag, light. It is widely used as lining material of high temperature, and also used as lining of autoclave in petroleum and chemical industry.

Q: What role does silica play in refractories?: Low fractory refers to the alumina content between 10%~30%, SiO2 content is less than 85%, semisilica brick SiO2 = 65%,The SiO2 content of not less than 93%, refractory material to natural quartz rock as the main raw materials are called silica, silica brick, silica brick, quartz glass and special products. China's literature generally put this type of product is called "siliceous refractory products", which is the most important brick.

Q: The United States of our brick anti-dumping duties?: . According to the relevant legal procedures, the United States International Trade Commission will make a final ruling on the anti dumping industrial injury before January 6, 2014, if an affirmative determination, the U.S. Department of Commerce will be involved in product release tax anti-dumping order.

Q: The difference between clay refractory bricks and refractory brick in the application.: Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.

Q: Physical solid waste disposal: The amount of addition is related to the shape and weight of the brick. The bricks can be added to 20% weight less than 25kg; bricks above 25kg can be added to 30%; for the specific type of brick can be added 30%. into waste silica brick should pay attention to this problem