High-Performance Zirconia Ceramic Filter Plate

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Ceramic Filter Plate Insulation Flexible Mica Paper Roll

Zirconia Ceramic Filter Plate Roller Product

Stainless Steel Zirconia Ceramic Filter Plate

High Silica Ceramic Fiberglass Casting Filter Plate

Ceramic Foam Filter Plate

Zirconia Ceramic Filter Plate for Steel Casting

Silicon Carbide Ceramic Foam Filter Plate

Alumina Ceramic Filter Plate for Steel Industry

Zirconia ceramic foam filter

Application:For the filtration of molten steel and alloy,large scale iron casting

Product standard:China national GB/T 25139-2010

Zirconia ceramic foam filters are determined for filtering of steel and steel alloys up to the temperature of 1700 °C.
Filters are recommended especially for high quality grades of alloys.

-Drop turbulent of molten steel and alloy

-Improve accepted rate of steel casting

-Reduce foreign matter of steel casting

-Drop twice oxide flaw

-Reduce second-face flaw after machine process

PHYSICAL PROPERTY:

Main material:ZrO2

Applied Temperature:≤1700℃

Color:Yellow

Hole density (PPI):10/20PPI(PPI=pores per inch)

Porosity(%):80-87

Bending strength（Mpa）:≥1.0

Compressive Strength(MPa):≥1.75

Bulk Density(g/cm3):0.7-0.85

DIMENSIONS:

Length*width*height=(40-100)*(40-100)*(20-35)mm

With round,square and rectangle shape.

Size tolerance:±1mm

Pore size: 10/20PPI

PPI tolerance:±2PPI

CHEMICAL COMPOSITION:

Al2O3 MgOSiO2 Fe2O3 ZrO2

≤1.8% ≥3.0% ≤0.5% ≤0.1% ≥94.00%

APPEARANCE REQUIREMENTS:

-No cracking allowed across the full length of the edge

-Any fine cracks within the filter matrix may not be through-going

-Filters should be free from loose debris

Q: The ultrasonic wave of ceramic filter is not good. What's going on?: The earliest filtration was mostly gravity filtration, which was followed by pressure filtration to increase the rate of filtration, followed by vacuum filtration. The drum vacuum filter invented in the early twentieth Century realized the continuous operation of the filter. Since then, various types of continuous filters have appeared. Intermittent operating filters (such as plate and frame press filters) are developed for automatic operation, and the filtration area is becoming larger and larger. In order to obtain the filter residue with low moisture content, the mechanical press filter has been developed.

Q: Influence factors of ceramic filter: (1) the particle size and the distribution of the material match the microporous of the ceramic filter plate. Although the ceramic filter plate aperture is bigger, easy to suck the pulp, but easy to cause the ceramic filter board to block up.(2) the ceramic filter plate with the same ceramic filter plate with high pore permeability and high water permeability is selected with high water permeability and good slurry absorption performance. The spindle speed is slow, the formation time of growth in the area of vacuum filter cake, production capacity increased gradually, but because the unit time of grout thickness and spindle speed slow is proportional to, so the ceramic filter capacity in a range of showing the highest.

Q: What are the causes of the powder moisture in the ceramic filter?: The main speed of the ceramic filter is too fast.The vacuum of ceramic filter is not enough.The cleaning of ceramic filter has not met the requirement.The ceramic filter plate has a near life and a serious blockage.The selection of ceramic filter plate is different.Too much residual of ceramic scraper after discharge.

Q: What's the reason for high water content in filtration copper concentrate?: Ceramic filter plate1) the service life of the ceramic filter plate has arrived.2), ceramic filter plate uneven in quality on the market, the production capacity of some ceramic products difference (table mask size is too large or pore size uniformity is poor as a result of suction effect is poor, short life), but the price is low, but some users in order to reduce the operation cost of ceramic machine, tend to choose low price the ceramic plate, sometimes a ceramic machine ceramic filter plate with several may be different, so do not get the expected effect in normal use.In addition, the concentrator slurry, especially metal slurry, is very powerful on the wear of ceramic filter plate, the mechanical strength and wear resistance of ceramic filter plate requirements (corundum has high mechanical strength, good abrasion resistance, especially suitable for metal slurry dehydration).When selecting ceramic filter boards, these two points should be taken as a reference.

Q: Why does not the iron filter of the ceramic filter work?: You should make it clear that the filter cake has always been dry or suddenly dry, and now how much moisture? Generally, the ceramic filter is used to filter iron powder, and the water content of the filter cake is about 10%.

Q: Ceramic filter capacity.: You ask too general, to say processing capacity (ie capacity), at least to provide material conditions, such as: material name, concentration, particle size distribution. In addition, the basic conditions of equipment operation should be taken into account.

Q: Does the ceramic factory use hydrochloric acid?: Ceramic filter comes with a combined cleaning system, usually to ensure backwashing normal, combined cleaning (nitric acid + ultrasonic + backwash) in place.

Q: Excuse me, what's the reason that all ceramic filters do not attract ore?: After the joint cleaning, 0~2 hours of suction effect may be good, 2~4 may drop slightly, 4 hours later will become worse and worse, or even suck. This case should first check the backwash water pressure (instantaneous maximum pressure should not be less than 0.08MPa) is to meet the requirements, should also advance down (to ensure normal and ultrasonic cleaning combined with nitric acid dosage sufficient) and prolong the cleaning time.

Q: What are the reasons for the program alarm of ceramic filter?: If you say "lean" is the ceramic filter suction when the ceramic filter plate into a cake of thin, high water content, is the ceramic filter for their own reasons, can from the following aspects: the investigation considering this phenomenon is always so recently or just happened, if you have been so, probably because your selection is not suitable for pulp the ceramic filter (such as mud content, fine grain size, ceramic filter plate selection such as inconsistent or unqualified ceramic filter). If this anomaly has occurred recently, it is possible to change the ore condition, and the operation parameters of ceramic filters or the cleaning are not up to standard. You can check the vacuum system (vacuum generally ranges from -0.09 to -0.075MPa), backwashing system (generally refers to the filtered water recoil 0.07 ~ 0.12MPa), acid (HNO3 system standards), ultrasonic system is normal.

Q: What is the reason that the whole ceramic filter does not attract ore?: Vacuum system failure, no vacuum or vacuum can not meet the requirements. Should check the vacuum pump and vacuum piping, distribution head, ceramic plate, such as failure or leakage.Whether the ore conditions are changed, such as pulp type, mud content, fineness, concentration, etc..

Send your message to us

*Email

*TEL

*Quantity

*Unit