1. Silica brick is the main refractory bricks used in glass melting furnace;its main crystal phase is Tridymite.
2. Silica brick for glass melting furnace is used in building checker chamber, chute, combustion chamber,coking chamber,and furnace arch etc.
3. Silica brick for glass furnace have following characters:
(1)High refractoriness under load.
(2)High heat conductivity.
(3)Good thermal shock resistance.
(4)Solidity stable of capacity in high temperature.
Tech Data
Silica brick for glass furnace | |||||
Item: | GF-96A | GF-96B | GF-95A | GF-95B | |
SiO 2 | ≥96 | ≥96 | ≥95 | ≥95 | |
Fe 2 O 3 | ≤0.8 | ≤1.0 | ≤1.2 | ≤1.2 | |
Apparent porosity % | ≤22(24) | ||||
Cold Crushing Strength MPa | Brick below20KG | ≥35(30) | |||
Brick ≥20KG | ≥30(25) | ||||
Refractoriness under load ºC | ≥1680 | ≥1670 | ≥1660 | ≥1650 | |
True density g/cm ³ | ≤2.34 | ≤2.34 | ≤2.35 | ≤2.35 | |
Silica brick for coke oven | ||
Item: | CO-94A | CO-94B |
SiO2: % | ≥94 | ≥94 |
Al 2 O 3 : % | ≤ 1.5 | ≤ 1.5 |
Fe2O3: % | ≤ 1.5 | ≤ 1.5 |
Refractoriness under load 0.2Mpa | ≥ 1650ºC | ≥ 1650ºC |
Apparent porosity: % | ≤ 22 | ≤ 24 |
Bulk density: g/cm ³ | ≤ 2.34 | ≤ 2.35 |
Cold crushing strength: MPa | ≥30 | ≥25 |
Permanent linear change % (1450ºC ×2h) | 0~0.2 | 0~0.2 |
Thermal expansion(1000ºC) | ≤1.28 | ≤1.30 |
Silica brick for hot blast furnace | |
Item | HBF-95 |
SiO2 | ≥ 95 |
Al2O3 | ≤ 1.0 |
Fe2O3 | ≤1.3 |
Apparent porosity % | ≤22(24) |
Cold crushing strength MPa | ≥45(35) |
Remaining quarts % | ≤1.0 |
Refractoriness under load ºC | ≥1650 |
Creep(0.2Mpa ×1550ºC×50h) % | ≤0.8 |
Thermal expansion coefficient (1000ºC) % | ≤1.25 |
Apparent density g/cm ³ | ≤2.32 |
- Q: Common bond brick?
- Manufacturing for silica brick binder hi-li sulfate pulp waste liquid and lime milk. When lime milk is used as a bond, it acts as a plasticizer. To increase the strength of lime brick in the drying process, as mineralizer in the firing, promote the transformation of quartz.
- Q: Why will expand when heated brick
- After high temperature after the formation of tridymite and cristobalite and quartz and a small amount of residual glass phase, quartz heating to 220-240 DEG C, in a certain degree of thermal expansion, brick maximum expansion occurs in 100~300 DEG C, 300 expansion before the total amount of expansion is about 70%~75%.
- Q: What is the effect of the content of silicon nitride in silicon nitride bonded silicon carbide brick on the use of electrobath? Thank you
- The main damage of silicon carbide side wall brick is stress damage, not chemical erosion. Chemical damage is formed prior to the formation of the groove, and the damage to the chemical erosion is little after the formation of the groove.
- Q: The introduction of silica brick
- Brick refers to the content of more than 93% products SiO2. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system. The higher the content of SiO2 in silica raw material, the higher the refractoriness of the product. According to the use of brick varieties, divided into: coke oven silica brick, brick for hot blast stove, electric stove with brick, brick for glass furnaces. According to the transformation is divided into: standard bricks, tiles, bricks and general special brick etc..
- Q: What is acid refractory?
- Acid refractory material usually refers to refractories with SiO2 content greater than 93%. Its main characteristic is that it can resist acid slag corrosion at high temperature, but it is easy to react with alkaline slag.
- Q: Semisilica brick, clay brick, high alumina brick and what is the difference?
- The share of A12O3 and SiO2 is different
- Q: How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?
- Mainly depends on the color and density of brick. Another black clay brick and brick with iron oxide formation and how much the size of bricks
- Q: Brick
- The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on.
- Q: The chemical composition of silica brick and its physicochemical index?
- Brick refers to the refractory products in more than 93% of the content of SiO2
- Q: What is the silica refractory products?
- High silicon content in high temperature expansion sintering temperature between 1390-1410 in furnace arch
Send your message to us
Silica Lime Bricks for Coke Oven CMAX-1
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches