Silica Brick for Hot Blast Stove/Furnace

Silica Brick for Hot Blast Stove/Furnace

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t.

Supply Capability:: 100000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$High Alumina Brick SK38 - High Quality Refractory Material$

High Alumina Brick SK38 - High Quality Refractory Material

Lime Silica Bricks for Hot Blast Stove - S95A

Silica Mullite Wear Resistant Brick

Silica Silicate Mullite Bricks for Induction Furnace

High Alumina Brick and Insulation Brick for Kinds of Glass Furnaces

Cement Kiln Magnesite Bricks

Fireclay Brick for Hot Blast Stove

High Chrome Magnesite Chrome Brick for Glass Industry

General Information
Modern hot stoves hot blast average temperature is up to 1,250 ℃- 1,300 ℃, so there are higher requirements on refractories quality, like checker chamber upper area, combustion chamber where are key areas for stoves campaign life. Therefore, some clients and experts have proposed the goal that campaign life of hot stoves should be twice as much as the life of blast furnace. Obviously, this is a challenge to refractories quality. It has become an important task for the refractory industry to select one kind of refractory with good thermal stability, high resistance to high temperature compression creep, high refractoriness under load and reasonable price to use in the hot stove with high blast temperature. The excellent performance silica brick has the following characteristics. The low creep, high refractories under load and low residual quartz contents, silicon bricks for hot stove of our company has been successfully applied to various types of hot stoves of major steel companies at home and abroad and the quality has been recognized by the clients.

Feature
Superior resistance to acids (including oxidizing)
Resistance to chlorine
Resistance to thermal shock and pressure changes
Low thermal and chemical expansion

Technical Data

Brand Item	CGZ-95	CRG-95		CJG-94
Brand Item	CGZ-95	Dome & Wall brick	Checker	Sole & wall brick	Others
Refractoriness º C ≥	1710
Permanent liner change 1450 º C × 2h %				+0.2 0
Apparent Porosity (%) ≤	22	22	23	22	24
True Density (g/cm3) ≤	2.37	2.35	2.35	2.34	2.35
Cold Crush Strength (MPa) ≥	29.4	35	30	30	25
Thermal Expansion(1000 º C ) %		1.26	1.26	1.28	1.30
Refractoriness under Load 0.2MPa Ta( º C ) ≥	1650			1650	1650
Chemical analysis SiO 2 % ≥	95	95	95	94	94

Photos for Applications

Silicon Brick for Hot Blast Stove/Furnance

Q: The introduction of silica brick: The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass

Q: Because of the recent relates to this industry, by way of learning to name for all raw materials, I hope knowledgeable friends exhibitions, thank you.: Acidic materialMainly siliceous materials, such as quartz, tridymite and cristobalite, chalcedony, flint, opal, white quartzite, silica sand, diatomaceous earth, silicon oxide contained in these siliceous materials (SiO2) at least 90%, pure raw materials are silicon oxide as high as 99% or more. Siliceous materials at high temperature is the acidic nature of chemical dynamics, when the presence of metal oxide, or when in contact with the chemical reaction, and combined with a fusible silicate. Therefore, if there is a small amount of metal oxide in siliceous material, it will seriously affect its thermal resistance.

Q: Why will expand when heated brick: Because the production of raw materials are silica brick, brick with SiO2 content of not less than 95% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system

Q: The difference between clay refractory bricks and refractory brick in the application.: Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.

Q: Semisilica brick, clay brick, high alumina brick and what is the difference?: The share of A12O3 and SiO2 is different

Q: How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?: Mainly from the impurities to determine how much, generally less impurity single color brick.

Q: Can not use it two brick: Acidic silica brick refractory material, has good ability in acid slag erosion

Q: Brick: Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature.

Q: Why is the highest brick coke oven temperature measuring point temperature not exceeding 1450: Brick belongs to refractory materials, with strong resistance to acid slag or acid solution erosion ability, high load softening temperature are excellent properties of silica brick, usually 1640-1680 C.

Q: The chemical composition of silica brick and its physicochemical index?: Brick refers to the refractory products in more than 93% of the content of SiO2

Send your message to us

*Email

*TEL

*Quantity

*Unit