hot-dipped galvanized steel sheet steelcoils

hot-dipped galvanized steel sheet steelcoils System 1

hot-dipped galvanized steel sheet steelcoils

Ref Price:

Loading Port:: Shanghai

Payment Terms:: TT OR LC

Min Order Qty:: 25 m.t.

Supply Capability:: 3000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

galvanized steel coil
1.Thickness:0.135-4.0mm
2.Width:600-1500mm
3.Zinc:40g-275g
4.Material:SGCC,DX51D,G550,SPGC,etc.

product name	Galvanized steel coils
thickness	0.135mm-4.0mm
width	600mm-1500mm762mm,914mm,1000mm,1200mm,1219mm,1250mm
zinc coating	40g,60g, 80g, 90,100g, 120g, 140g,180g, 200g, 250g, 275g and so on.
standard	ASTM, AISI, DIN, GB
material	SGCC,DC51D,DX51D,DX52D,,SGCD,Q195,Q235,SGHC,DX54D, S350 GD, S450 GD,S550 GD
spangle	zero spangle, regular spangle or normal spangle
surface treatment	chromated and oiled, chromated and non-oiled
packing	export standard.
payment	T/T, L/C or DP
min order	25 tons (one 20ft FCL)
coil weight	3-8ton or as client requirement.
quality	soft or hard quality

Galvanized steel coils

STEEL GRADE	CHEMICAL COMPOSITION %						MECHANIC PROPERTY				C.B OF COATING		COATING
	C	Si	Mn	S	P	T.S		Y.S	E.L
	x103	x103	x102	x103	x103	Mpa		Mpa	%	d=0 180°		G/M²
JIS G3302 SGCC	12	30	41	31	21	480		300	13	OK		Z60-150
JIS G3302 SGCH	12	10	21	18	8	680		650		OK		Z60-150
ASTM A653 CS.B	20	30	60	35	30	386		205~380	20	OK		Z80-275
DX51D+Z	29	21	18	1.8	11	355		245	38	OK		Z80-275
G550	20	6	73	5	17	715		654	8	OK		Z80-275

Q: How are steel coils used in the manufacturing of storage systems?: Steel coils are an essential component in the manufacturing of storage systems due to their durability, strength, and versatility. These coils are typically made from high-quality steel and are created by rolling the steel into a coil shape. In the manufacturing process of storage systems, steel coils serve various purposes. One of the primary uses of these coils is for the construction of shelves, racks, and frames. These components provide the structural support necessary to hold and organize items within the storage system. The strength of the steel coils ensures that the storage system can withstand heavy loads and remain stable over time. Additionally, steel coils are also used in the production of storage system accessories such as brackets, hooks, and dividers. These accessories provide additional functionality and customization options for the storage system, allowing users to optimize their storage space based on their specific needs. Moreover, steel coils are often used as the material for doors and panels in storage systems. The coils are molded and shaped to create sturdy and secure doors that provide easy access to the stored items while maintaining the overall integrity of the system. These doors can be designed with various locking mechanisms to enhance security and prevent unauthorized access. Furthermore, steel coils are crucial in the manufacturing of mobile storage systems. These systems, such as mobile shelving units or compactors, are designed to maximize storage capacity in limited space. The flexibility and versatility of steel coils allow for the creation of movable components that can be easily adjusted and reconfigured to accommodate changing storage requirements. Overall, steel coils play a vital role in the manufacturing of storage systems by providing the necessary strength, durability, and versatility required for these structures. Whether it is for shelves, accessories, doors, or mobile systems, steel coils ensure that storage systems are reliable, secure, and efficient in organizing and storing various items.

Q: which metals have a higher density than steel? and how does the density compare to steel( example: tungsten carbide is 2x [i think] more dense than steel.): This Site Might Help You. RE: what metals are more dense than steel? which metals have a higher density than steel? and how does the density compare to steel( example: tungsten carbide is 2x [i think] more dense than steel.)

Q: How are steel coils protected during transportation?: Steel coils are protected during transportation through various measures to ensure their safety and prevent damage. One common method is the use of high-quality packaging materials such as heavy-duty plastic wrapping or waterproof paper. These materials provide a protective barrier from external elements like moisture, dust, and debris. Additionally, steel coils are often placed on wooden pallets or skids to elevate them from the ground and prevent direct contact with surfaces that could potentially cause scratches or dents. To further safeguard the coils, they are securely strapped or banded to the pallets using strong, corrosion-resistant metal strapping or bands. This helps to keep the coils in place and prevent any movement or shifting during transportation, minimizing the risk of damage. Moreover, steel coils are often loaded and secured onto flatbed trailers or shipping containers using specialized equipment like coil cradles, coil racks, or coil bunks. These devices are designed to hold the coils firmly in place and distribute the weight evenly to avoid any stress or strain during transit. In addition to physical protection, steel coils may also undergo various surface treatments before transportation to prevent corrosion. This can include applying a protective coating or oiling the coils to create a barrier between the steel and the surrounding environment. This process helps to prevent rust or other forms of corrosion during transit, especially when the coils are exposed to adverse weather conditions or long shipping durations. Overall, a combination of proper packaging, secure strapping, and appropriate loading techniques are employed to protect steel coils during transportation, ensuring their safe arrival at their destination without any significant damage.

Q: Don't ask me why, but I took my stainless steel ring and I heated it up with my gas stove. I stuck it in there til the metal turned red, and the flame which is normally blue turned orange for some reason when the metal turned red. Anyway, afterwards i cooled it off in water and now it's all discolored and it feels different. It's weighs less and it doesn't feel the same. Plus, it's ugly cause it's all black and blue. What happened? Someone help: Stainless steel has a rating. I don't know what your ring's stainless steel rating is. If you know, you can look it up. The rating will tell you how much steel vs other metal it has (usually Cr and Ni). But usually when you heat the stainless steel to extreme temperature it will discolor due to oxidation. What is worse is that you cooled it off in water (I assumed that you did it while it was still hot). By rapid cooling, you have changed the physical structure of the steel itself. It will change the hardness of the steel. That is why it feels different. Look up on annealing, normalizing, quenching and tempering under heat treatment for steel.

Q: What are the common standards and specifications for steel coils?: In the industry, there are various widely recognized and utilized standards and specifications for steel coils. Some notable ones include: 1. ASTM A36/A36M: This specification is concerned with carbon structural steel shapes, plates, and bars of structural quality. It is intended for use in constructions that involve riveting, bolting, or welding. 2. ASTM A572/A572M: This specification focuses on high-strength low-alloy columbium-vanadium structural steel shapes, plates, sheet piling, and bars. It is applicable for constructions involving bolting, riveting, or welding. 3. ASTM A653/A653M: This specification pertains to steel sheet that is zinc-coated (galvanized) or zinc-iron alloy-coated (galvannealed) through the hot-dip process. 4. ASTM A1011/A1011M: This specification covers various types of steel sheet and strip in coils, such as hot-rolled, carbon, structural, high-strength low-alloy, high-strength low-alloy with improved formability, and ultra-high strength. 5. JIS G3302: This Japanese Industrial Standard specifies the requirements for hot-dip zinc-coated steel sheet, also known as galvanized steel sheet, and strip. 6. EN 10111: This European standard outlines the requirements for continuously hot-rolled low carbon steel sheet and strip that are suitable for cold forming. 7. ISO 3575: This International Organization for Standardization standard lays down the requirements for hot-dip zinc-coated and zinc-iron alloy-coated steel sheet and strip. These are just a few instances of the prevalent standards and specifications employed for steel coils. It is crucial to note that different industries and applications may have specific demands, thus consulting the relevant standards and specifications for the particular application is always advisable.

Q: What are the dimensions of steel coils used in the building materials industry?: The dimensions of steel coils used in the building materials industry can vary depending on the specific requirements of the project. However, common dimensions for steel coils in this industry range from 0.15mm to 3.5mm in thickness and 600mm to 2000mm in width. The length of the coils can also vary, typically ranging from 1000mm to 6000mm.

Q: What is the maximum stacking height for steel coils?: The maximum stacking height for steel coils depends on various factors such as the weight and size of the coils, the strength of the supporting structure, and the safety regulations and guidelines in place. It is recommended to consult the manufacturer's specifications and industry standards to determine the appropriate maximum stacking height for steel coils in a specific situation.

Q: What is the shelf life of steel coils?: The shelf life of steel coils is indefinite if they are stored properly. Steel coils are known for their durability and long-lasting nature, making them suitable for extended storage periods without any degradation in quality. However, it is important to store them in a dry and well-ventilated area, away from moisture and corrosive substances to prevent any potential damage.

Q: How do steel coils contribute to energy efficiency in buildings?: Steel coils contribute to energy efficiency in buildings through their use in HVAC systems. Steel coils are commonly used in air conditioning and heating units as a part of the heat exchanger. The coils help to transfer heat between the indoor and outdoor environments, allowing for efficient temperature control. By efficiently transferring heat, steel coils help to reduce energy consumption and ensure that the building's HVAC system operates at optimal levels. This ultimately contributes to energy savings and increased energy efficiency in buildings.

Q: How are steel coils used in the production of HVAC equipment?: Steel coils are used in the production of HVAC equipment as they serve as the primary components for heat transfer. These coils are responsible for facilitating the transfer of heat between the air and refrigerant, ensuring efficient cooling or heating of the air circulating within the HVAC system.

Send your message to us

*Email

*TEL

*Quantity

*Unit