FeSi For Metallurgical Deoxidizer

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

FeSi
1.13 years' professional experience
2.Controlled composition&size
3.ISO&SGS QA
4.High energy

FeSi

Description

Ferro Silicon is a kind of ferroalloy which is composed of ferrum and silicon. Ferro Silicon uses coke, quartz (or silica) as raw materials and is made by electric furnace. Because silicon and oxygen are easily compound into SiO2, the ferrosilicon is often used as deoxidizer in steelmaking.

Application

1. Ferrosilicon is often used as deoxidizer in steel- making.

2. Ferrosilicon also can be used as alloy elements join agent, which is widely used in low alloy steel, non-ferrous metal, bearing steel, heat-resistant steels and electrician silicon-steel.

3. It can be used as a reductant in ferroalloy production and chemical industry.

4. In iron industry it can be used as inoculant and nodulizer.

Specification

Brand	Chemical Composition (%)
	Si	Al	Ca	P		S		C		Fe
		<=
FeSi75-A	74.0-80.0	1.5	1		0.035		0.02		0.2		Balance
FeSi75-B	72.0-80.0	1.5	1		0.04		0.02		0.2		Balance
FeSi72	72	1.5	1		0.04		0.02		0.2		Balance
FeSi70	70	1.5	1		0.04		0.02		0.2		Balance
FeSi65	65.0-72.0	2	1		0.04		0.02		0.2		Balance
FeSi45	40.0-47.0	2	2		0.04		0.02		0.2		Balance

Size:0-3mm,3-10mm,10-100mm or as the customers’ requirements

FeSi For Metallurgical Deoxidizer

Q: suitable for processing the whole alloy drilling, milling, reaming and other cutting tools. This alloy tungsten, cobalt content, how many of you?: Just found the carbide under YK15, its cobalt content in 10%.According to its brand, YK15 should be used to process cast iron, so the main ingredient should be WC+Co.So its WC component should be in 89-90% (just for inference, for reference only)Based on the molar mass of WC, the mass fraction of the W content is deduced

Q: hard alloy ball tooth, sand making machine, high quality and inexpensive alloy (*^__^*)I am now in great demand of cemented carbide rods, hard alloy blade, hard alloy ball tooth, sand making machine alloy strip, the old customers are not do, now I want to find a long-term cooperation partners, we have not recommended ~ ~ ~ thank you pull: Hello, I'm from Zhuzhou CREE cemented carbide Co., Ltd.We are specializing in the production of various specifications of hard alloy, Zhuzhou cemented carbide, Zhuzhou hard alloy, sand making machine alloy strip, hard alloy ball tooth, carbide blade, hard alloy bars, welding blade, milling cutter, long and thin; manufacturers selling cheaper price; all kinds of hard alloy, Zhuzhou cemented carbide, Zhuzhou hard alloy sand making machine alloy, hard alloy ball tooth, carbide blade, hard alloy bars, welding blade, milling cutter, long and thin, everything, quality assurance; welcome you to come to the consultation, to serve you is our honor.

Q: Does the hard alloy belong to the composite material?: 1. carbide is based on tungsten carbide as matrix, cobalt as binder, according to the needs of the titanium, tantalum, niobium and other metals to obtain the "alloy" material.2. because this alloy is relatively hard, so called him "carbide", people often used to do machining tools.3., from the definition of "composite material", "alloy" belongs to "composite material"". Therefore, cemented carbide belongs to composite material.

Q: What material is that ultrafine cemented carbide?: You mean the ultra-fine grain cemented carbide, generally we have 0.6 alloy grain size is fine, which belongs to the tungsten carbide base hard alloy, ordinary tungsten carbide base hard alloy strength and hardness are higher than the same cobalt content. The process is mainly mixing, wetting, drying, forming, sintering, finishing, such as sand blasting, CVD/PVD coating, heat treatment, etc.

Q: the blade is hard alloy, the processing material is QT600, the plane lower tool margin is 4mm, the speed and the knife: This belongs to the category of ductile iron, more difficult to process, because the material is hard particles, it is recommended around S=1200 F=400

Q: One kind of steel is called T10, and another is carbon steel. What kind of hardness and strength do they have?: Uncertain.Carbon content is different, and some trace elements contain different categories.Alloy steel, which means hardening can harden even when cooled in air, and very sharp. It is a complex alloy steel, containing tungsten, molybdenum, chromium, vanadium and other carbide forming elements. The total amount of alloy elements is about 10 to 25%. It can maintain high hardness at high temperature (about 500 DEG C) in high speed machining, and HRC can be higher than 60.Carbon steel, also called carbon steel, mainly refers to the mechanical properties of carbon depending on the content of steel, and generally do not add a large number of alloy elements of steel, sometimes referred to as general carbon steel or carbon steel. Of iron carbon alloys containing carbon less than 2% WC. Carbon steel, in addition to carbon, usually contains a small amount of silicon, manganese, sulfur and phosphorus.

Q: Is nickel base alloy hard alloy?: 2, YT--- tungsten cobalt titanium alloy products, applicable to coarse, carbon steel and alloy steel uneven section in interrupted cutting when the YT5 rough planing, semi finishing, discontinuous surface rough milling and drilling.

Q: The milling of hard cutting workpiece hard alloy cutter knife edge collapse and Countermeasures of reason: Hard to turn materials require different speeds and special turning tools. There is a reasonable amount of feed. Ordinary alloy knives are very easy to break

Q: How are cemented carbides separated from the cutting tools?: The hard alloy cutter head and the tool body junction part are heated to 600~800 degrees, and the solder can be melted, and the cutter head and the cutter body of the carbide cutter can be separated.Cemented carbide is a kind of alloy material made by powder metallurgy process of hard metal and bonding metal of refractory metal.Hard alloy with high hardness, strength and toughness, good wear resistance, heat resistance, corrosion resistance and a series of excellent performance, especially high hardness and wear resistance of it, even at a temperature of 500 DEG C also remained unchanged, at 1000 degrees C still have high hardness.Hard alloy is widely used as a tool material, such as turning, milling, planing, drilling, boring, used for cutting cast iron, non-ferrous metals, plastics, chemical fiber, graphite, glass, stone and steel, can also be used for cutting steel, stainless steel, high manganese steel, tool steel and other hard processing materials.

Q: Is it hard to make carbide cutting tools for aluminum alloy?: High speed tool steel is essentially tool steel, but heat resistance is betterHard alloy is made of tungsten carbide, titanium carbide materials such as superhard materials. From the hardness and red hardness, high speed tool steel paima couldn't catch up. Although the name as "alloy" two words, it is actually a kind of metal ceramic.