Fused Cast Chrome Magnesite Bricks for Dry Processing
- Ref Price:
-
- Loading Port:
- Qingdao
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 10 m.t.
- Supply Capability:
- 100000 m.t./month
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
Dry processing direct bonded chrome magnesite bricks Advantage:
1) Silicon oxide is above 95%.
2) Good acid erosion resistance.
3) High softening point
Dry processing direct bonded chrome magnesite bricks Applications:
Light weight silica bricks are primarily used for furnaces and kilns in metallurgy, steel, power, chemical industry, and electric power and machine building etc areas
Dry processing direct bonded chrome magnesite bricks specifications:
Direct-Bonded Magnesia-Chrome Brick
Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
DBMGe-8A | ≥74 | ≥8 | ≤1.5 | ≤18 | 2.98 | ≥40 | 1660 |
DBMGe-8B | ≥74 | ≥8 | ≤2.0 | ≤18 | 2.98 | ≥35 | 1600 |
DBMGe-12A | ≥66 | ≥12 | ≤1.5 | ≤18 | 3.1 | ≥40 | 1660 |
DBMGe-12B | ≥66 | ≥12 | ≤2.0 | ≤18 | 3.1 | ≥35 | 1600 |
DBMGe-16A | ≥60 | ≥16 | ≤1.5 | ≤18 | 3.15 | ≥40 | 1660 |
DBMGe-16B | ≥60 | ≥16 | ≤2.0 | ≤18 | 3.15 | ≥35 | 1600 |
Rebonded Magnesia-Chrome Brick
Main Application:It’s suitable for lining of the slag zone area of refining furnaces of VOD,SKF.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
RBMG-16A | ≥65 | ≥16 | ≤1.2 | ≤16 | 3.1 | ≥45 | 1750 |
RBMG-16B | ≥60 | ≥16 | ≤1.6 | ≤16 | 3.1 | ≥40 | 1700 |
RBMG-20A | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥45 | 1750 |
RBMG-20B | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥40 | 1700 |
Semi-Rebonded Magnesia-Chrome Brick
Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L ℃ |
SBMG-16A | ≥60 | ≥16 | ≤1.5 | ≤17 | 3.1 | ≥40 | 1750 |
SBMG-16B | ≥60 | ≥16 | ≤1.8 | ≤17 | 3.1 | ≥35 | 1700 |
SBMG-20A | ≥55 | ≥20 | ≤1.5 | ≤17 | 3.15 | ≥40 | 1750 |
SBMG-20B | ≥55 | ≥20 | ≤1.8 | ≤17 | 3.15 | ≥35 | 1700 |
FAQ
Q4: What is the minimum quantity?
A4: There is no minimum order quantity. Depending on the item and processing, there may be a minimum production required, however we can offer a quotation based only on the quantity you need.
Q5: Can you give me a brief introduction of the application of your products?
A5: CNBM (China National Building Material) core refractory business comprises the production, sale and installation of high-grade refractory products, the development and implementation of customized system solutions as well as rendering outstanding services for the key industries in Glass, Iron& Steel, Petrochemical, Cement, Ceramic and Nonferrous Metals..
offer a quotation based only on the quantity you need.
- Q: What are the forming methods of refractory materials?
- Casting molding is suitable for casting brick, electric melting brick and so on. And the machine press forming is the most widely used. The common refractory brick, clay brick and other sintered brick are adopted this method.
- Q: Zirconium corundum 25 content and 40 content, how to distinguish in appearance?
- The fused zirconia corundum brick is mainly made of fused zirconia and corundum. ZrO2-Al2O3-SiO2 three element system fused brick, containing Al2O3:40% to 50%, ZrO2:30% to 50%, SiO2:10% to 17%.From the point of view of data analysis, there is no radioactive substance in it, and it will not cause harm to the human body.
- Q: What is the face brick
- You should be talking about refractory bricksThe refractory brick brick. Referred to as refractory material has a certain shape and size. According to the preparation process can be divided into bricks, brick, electric melting brick, refractory insulating bricks (Rong Zhuzhuan);
- Q: Just what is in the furnace material?
- Referred to as refractory brick. Refractory made from refractory clay or other refractory material. Light yellow or brownish. The utility model is mainly used for laying smelting furnaces, and can withstand high temperature between 1580 DEG C and 1770 DEG C.
- Q: What are kiln bricks?
- Refractory materials are generally divided into two kinds, namely unshaped refractory and shaped refractory. Unshaped refractory castable is also called, is composed of a variety of aggregate or aggregate and one or more adhesive powder particles, and must use one or more liquid with stirring, has strong liquidity. Refractory materials generally refers to the shape of a refractory brick, standard rules, can also according to need to be cut when the temporary processing.
- Q: Is the wall around the fire area using a firewall? What's the difference between a fireproof brick and a regular brick?
- Not always。Referred to as refractory brick. Refractory made from refractory clay or other refractory material. Light yellow or brownish. The utility model is mainly used for laying smelting furnaces, and can withstand high temperature between 1580 DEG C and 1770 DEG C. Also called brick. Refractory material of a certain shape and size. According to the preparation process can be divided into bricks, brick, electric melting brick (Rong Zhuzhuan), the refractory insulating bricks; according to the shape and size can be divided into standard brick, brick, brick and other specific type. It can be used as high temperature building materials and structural materials for construction kilns and various thermal equipments, and can undergo various physical, chemical and mechanical changes at high temperature. For example, refractory clay brick, high alumina brick, brick, brick etc..
- Q: Outside wall tile (whole body smooth surface has small hole split brick) has cement pollution, with what product cleaning (cement, mortar, cleaning agent)?
- Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels. Clay brick materials, cheap, durable, and fire prevention, heat insulation, sound insulation, moisture absorption and other advantages, is widely used in civil engineering. Waste brick can also be used as aggregate of concrete. In order to improve the shortcomings of ordinary clay bricks, such as small, self important and waste of soil, they are developing in the direction of light weight, high strength, hollow and big blocks.
- Q: What material is good for refractory bricks?
- 1, silicon aluminum refractory bricks mainly include the following.(a) is the main varieties of acidic silica brick, refractory brick. It is mainly used for coke oven building, also used in furnaces all kinds of glass, ceramic and carbon calciner, refractory brick arches and other load-bearing parts, is also used in high temperature bearing part of hot blast stove, but should not be used in thermal equipment below 600 DEG C and the temperature fluctuation in the.(two) clay brick is a refractory brick commonly used in blast furnaces, hot blast furnaces, heating furnaces, power boilers, lime kilns, rotary kilns, ceramics and refractory bricks.(three) the mineral composition of high alumina refractory brick and high alumina refractory brick is corundum, mullite and glass phase. The raw materials are high alumina and sillimanite natural ore. They are also made of fused alumina, sintered alumina, synthetic mullite and calcined alumina in different proportions with clay. It is produced by sintering process. But the products are casting brick, brick, brick fused grain and unshaped refractory brick. High alumina refractory brick is widely used in iron and steel industry, non-ferrous metal industry and other industries.
- Q: Can the fire clay be reused?
- According to the preparation process can be divided into bricks, brick, electric melting brick (Rong Zhuzhuan), the refractory insulating bricks; according to the shape and size can be divided into standard brick, ordinary brick, specific rotation. It can be used as high temperature building materials and structural materials for construction kilns and various thermal equipments, and can undergo various physical, chemical and mechanical changes at high temperature.
- Q: What's the weight of the refractory bricks?
- Fireclay refractory bricks: 3.4kg-3.8kg - according to the quality of raw materials, prices ranging from 1 yuan to 2.7 yuan, high alumina refractory brick: three, high aluminum in 3.9kg or so. Ordinary T-3 firebrick weight calculation method: 230*114*65*2.2/2.1.
Send your message to us
Fused Cast Chrome Magnesite Bricks for Dry Processing
- Ref Price:
-
- Loading Port:
- Qingdao
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 10 m.t.
- Supply Capability:
- 100000 m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords