Raw Materials for Refractory:Dead Burnt Magnesite 0-30mm

Ref Price:

Loading Port:: Dalian

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 2000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Item	MgO	SiO₂	CaO	LOI	B.D.(g/cm³)
DBM-97	97	0.7	1.4	0.2	3.2
DBM-96	96	1.5	1.5	0.2	3.2
DBM-95	95	2.2	1.6	0.3	3.2
DBM-94	94	3	1.6	0.3	3.2
DBM-93	93	3.5	1.6	0.3	3.2
DBM-92	92	4	1.6	0.3	3.18
DBM-92	92	4	1.6	0.3	3.18
DBM-91	91	4.5	1.6	0.3	3.18
DBM-90	90	4.8	2	0.3	3.18
DBM-87	87	7	2.2	0.3	3.2

Our factory produce the products of the Dead-burned magnesite are selected natural magnesite, it is produced by mine-selecting, purifying, calcimine in shaft kiln. It is an ideal material for unshaped refractory material, the final products are used in open hearth furnace, electric furnace bottom and furnace's lining tamping.

Q: Who knows what is the standard of insulation material whose fire proof is level A?: Level A is distinct from B in coefficient of fire proofing. Level A is non combustible, while Level B is divided into B1( flame retardant), B2(combustible) and B3( inflammable). Currently in the market, level A materials are as follows: phenolic, rock wool, insulation mortar, ceramic foam, foam glass, and foamed concrete. The most advantageous of level A material at present is foamed concrete, also known as foamed cement. Xuzhou Lvchuang Construction company is working on this, you can search fro it on the internet, it has high cost performance.

Q: Who can introduce the difference between galvanized fireproof?coatings and steel structure fireproof materials?: There is no difference between them because they are the coating with the same texture. But generally galvanized treatment is not necessarily needed for brushing fireproof coating. Fireproof coating and galvanized surface have relatively poor bond strength. So it is advisable to bursh trasitional lacquer or micaceous iron on galvanized surface.

Q: What are the requirements of refractory temperature of refractory brick?: Oxygen fluctuation of load once happened during operation. Sometimes oxygen control valve will cause oxygen fluctuation of load, and sometimes large particles will block valve of high pressure coal slurry pump. The sudden drop in flow of coal slurry may cause relative excess of oxygen. Oxygen fluctuations directly cause fluctuations in furnace temperature. The range of oxygen fluctuations is 500m?-600m?. The maximum can reach about 1000m?. A sudden increase in oxygen causes a sudden increase in furnace temperature, which will suddenly burn out high-temperature thermocouple. The situation has a great influence on refractory brick and should be avoided. Furnace temperature is very inportant to life of lining of refractory bricks, so it should be strictly controlled not to overheat. There is a cinder layer on the surface of refractory bricks under the condition of normal production. In fact, cinder layer is dynamic. If the temperature is low, cinder layer is thick. If the temperature is high, cinder layer is thin. Appropriate cinder layer may slow the scour of high temperature gas and molten slag. The requirement of refractory brick is higher than that of stoves which use heavy oil as raw material. The main reason is permeability and corrosion of molten slag to refractory material. When replacing refractory bricks, it is found that penetration thickness is 10mm-20mm. After slag penetrates, strength decreases significantly. If temperature is high, erosion intensifies. According to the relevant information, when the operating temperature exceeds 1400 ℃, etching effect multiplies.

Q: Which are fireproofing external wall materials?: 1. Acording to national standard GB8624-97, the combustion performance of construction materials are classified as: Grade-A: incombustible building material: Grade-A WW thermal insulation material which hardly burns. Grade-B1: nonflammable building material: nonflammable building material has good flame resistance. It is difficult to burn or spread in the air or at high temperature. Grade-B1: nonflammable building material: nonflammable building material has good flame resistance. It is easy to burn in the air or at high temperature, thus spreading the fire, such as wooden column, timber roof truss, timber beam and wooden stairway. Grade-B3: inflammable building material. Without fire resistance, inflammable building material is easy to burn and thus cause a fire. 2. According to fireproofing performance, external wall thermal insulation materials can be classified as: 1. Thermal insulation material with Grade-A combustion performance: WW inorganic thermal insulation material, rock wool, glass wool, foam glass, foamed ceramics and foam cement. 2. Thermal insulation material with Grade-B1 combustion performance: XPS panel after special treatment/ PU, phenolic aldehyde, gelatine powder polyphenyl granule after special treatment. 3. Thermal insulation material with Grade-B2 combustion performance: EPS, XPS, PU, PE, ETC.

Q: What type of firebrick does TZ-3 represent?: Height is 65mm, length is 230mm, and width is 114mm, that is the t-3 firebricks which meet the national standard.

Q: which kind of material should be used in fireproofing cabinet?: Here are a few good materials: 1. The mineral wool board, glass wool board: it mainly tales mineral wool, glass wool as insulation materials. It's non-combustible, light weight and has good high temperature resistance, but there are shortcomings ① short?fiber will harm the human respiratory system, ② poor sheet strength, ③ poor barrier property of sheet for smoke of fire disaster, ④ poor decorative properity, ⑤large installment and construction work. Thus, most of the boards were sheets that take inorganic anchoring material as base material, glass wool as reinforcing material. 2. cement board: Cement board has high strength and wide sources. It is often used in fireproof suspended?ceiling and partition in the past, but it has poor fire resistance and is easy to burst and lose protective function , which will limit it's applications. Cement concrete component has good thermal insulation and sound insulation properties, and it can be used as partition and roof board. Fiber reinforced cement board and other improved varieties appear in the construction?materials market, and they are high strength and have good fire resistance, but their disadvantages are poor toughness, large alkalinity and poor decoration effect. 3. perlite board, cenosphere board, vermiculite board: It's a kind of hollow plate that takes low alkalinity cement as base material, perlite, glass beads, vermiculite as the aerated filling material, and is made by adding some auxiliary. It has characteristics of light weight, high strength, good toughness, fireproofing and thermal insulation, easy for construction,etc. and it can be widely used in high-rise building frame compartment, household, bathroom, kitchen, communication pipe and other non-load bearing areas.

Q: What is the most reasonable drying heating curve of magnesia refractories? Products of less than 0.5T: You'd better oxidize magnesia preformed unit at room temperature for a longer period of time, then bake it, during which, it's enough to control the maximum temperature within 300 degrees. During the middle process, usually heating up for 4 hours and keep warm for 3 hours. The entire heating up process takes about 20 hours. If it is the site operation magnesia-based castable, it should be heated slowly in the early stage, and pay attention to keeping warm at 80 degrees Celsius. Every manufacturers has their own heating curves, so do not blindly adopt existing curves, try to make your own heating curve.

Q: How many external wall thermal insulation fireproof material are there: Class A exterior wall insulation: Rock wool, glass wool, silicate, aluminum silicate, calcium silicate, phenolic foam, foam glass

Q: How is the development of Xinmi refractories industry? What's its advantages and disadvantages?: The advantages are largest scale, top production amout in the country, accounting for one-third of the national market, having technology, strength and the market. The disadvantages are the lack of mineral resources, serious environmental pollution,

Q: Pals who know something about fire resistant material please tell me how many types of refractory material there are: There are a variety of refractory materials, each of different use. It is necessary to make resonable classification for refractory materials so as to facilitate scientific research, rational selection and management. There are many kinds of classification methods for refractory materials, including classification based on chemical property, chemical mineral composition, production process, material form and other methods. 1, according to the capacity of fire resistance: ordinary refractory materials: 1580 degrees C ~1770 C Advanced Refractory Materials: 1770 degrees ~2000 degrees c: Classification according to product shape and size: standard 230mm×113mm×65mm no more than 4 scales

Send your message to us

*Email

*TEL

*Quantity

*Unit