Fireclay Brick - High Strength Refractory (Unf42)

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 20 m.t.

Supply Capability:: 50000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Fireclay Insulation Brick for Steel Industry

$Fireclay Brick for Refractory Applications in the Electric Power Industry$

Fireclay Brick for Refractory Applications in the Electric Power Industry

Fireclay Insulation Bricks for Electric Power Industry

$Fireclay Brick - Fire-resistant Refractory Low Porosity for Glass Furnace Regenerator$

Fireclay Brick - Fire-resistant Refractory Low Porosity for Glass Furnace Regenerator

Fireclay Brick - Strong Resistance Low Porosity Fire-Resistant

Fireclay Brick with Al2O3 Content 75-80% Composite

Fireclay Brick - DRL 125 Brick Fired Furnace Brick Lining

$DRL 120 Brick Fired Furnace Brick Lining Refractory Fireclay Brick$

DRL 120 Brick Fired Furnace Brick Lining Refractory Fireclay Brick

CLAY BRICK---UNF42

CMAX fireclay bricks are made from clinker clay. The alumina content ranges from 36% to 48%.

Application
CMAX fireclay bricks are commonly applied in blast furnace, hot blast furnace, teeming ladle, glass furnace, etc.

Features
Low thermal conductivity High refractoriness
High mechanical strength Excellent thermal shock resistance

High refractoriness under load
High mechanical strength
Excellent thermal shock resistance
Corrosion resistance.

Good resistance against acid slag
High mechanical strength
Stable performance under high temperature environment

Physical Properties:

ITEM UNF42
Refractoriness, 1730
Bulk Density, g/cm3 2.15
Apparent Porosity, % 22
C. C. S, Mpa 30
Refractories Under Load (0.2Mpa), 1400
Reheating Linear Change, % 1400x2h 0.1~-0.4
Al2O3 Content, % 42

Q: What are the release agents of refractory bricks?: Alkalinity, the production process of alkaline, acid and alkali resistant transparent instant thickening powder, you can adjust the proportion according to the cost and needs of quality, environmental protection: One: Add the preservative into water to mix, after soaking one hour, then mixing evenly the production ratio, and then add the super core release agent into water to mix, add flavor pigment masterbatch into water to mix with water mixing, ensure completely dissolved, then add the waste oil, falvor is appropriate amount= release agent. Two, the newest recipe of release agent super core release agent masterbatch, waste engine oil, water, instant acidproof and alkaliproof transparent thickening powder, wire drawing powder, preservative, flavor and pigment= release agent super core wire drawing powder with water mixing, it is the most newly developed special core masterbatch and engine oil of Chengdu Hengfeng Hongye detergent factory, and it doesn't contain toxic solvents, especially 1, it has the following features, after thickening more than half an hour or so, mix evenly is ok, in a few seconds will waste oil and alkali: 10% of waste engine oil, 20% of release agent core masterbatch, 88% of water, 500g instant acidproof alkaliproof transparent thickening powder, 80g wire drawing powder, 1g pigment and preservative and lubricating oil and industrial grease, these integrate with water.

Q: Why can earth make bricks?: Therefore, it is still widely used in masonry projects such as walls, foundations and columns. However, due to the production of traditional clay brick to destroy the field, large amount of soil sampling, high energy consumption, brick from the major, high labor intensity and low efficiency in construction, it is necessary to gradually reform and replace with new materials. Some cities have banned the use of clay bricks in buildings. Brick for sintering brick and non sintered brick in accordance with the production process; according to the raw materials used for clay brick, shale, coal gangue brick, fly ash brick, slag brick and lime sand brick; according to whether the hole is divided into hollow brick, brick. In addition to clay, or as raw materials for preparation of brick by using fly ash, coal gangue and shale, which is due to their chemical composition similar to clay, but because of the fineness of less clay, so the poor plastic bricks often to be mixed with a certain amount of clay, in order to increase the plasticity. The use of coal gangue and fly ash and other industrial waste residue brick, not only can reduce the environmental pollution, saving large areas of farmland clay, and can save a lot of fuel coal.

Q: how heavy are boiler of six tons plus refractory bricks?: The total weight is about 60 tons, 6 tons of bulk boiler steel, insulation materials, sealing materials, refractory material

Q: What are the differences between thermal?insulation?bricks and refractory bricks?: Thermal insulation brick is thermal insulative; refractory brick is high temperature resistant.

Q: What are the reasons for the production of waste in the formation of fireclay bricks?: The reasons for the production of waste when form fireclay bricks: Tile size is unqualified. This is due to the mold installation is not firm, the template transfers when molding; if the amount of material being added fluctuates largely, also can cause the body size changing. Ji Yangon Chi lie charge generation layer containing decyl poke pull and crack. The molding operation does not according to the principle of the light first and the thick later. At the initial pressure, the air doesn't releases, which causes the elastic aftereffect by repressing. Too much mud water, uneven mixture and inequal template all can make the body produce layer crack or crack. Twist. The template is used for too long, the template deforms, so raw brick deforms, the amount of water is too large, brick naturally deforms, causing the body twist. Miss edge and angle. Because of poor plasticity of mud, particles segregate, feeding back corner is not real, the body will appear side missing and angle modulation phenomenon. Bias voltage. Due to the deflection of the die head or the uneveness of mold bottom. Loose。 Due to insufficient feeding amount or insufficient pressure times.

Q: What raw materials can be added to fireclay brick to respond to the urgent cold and urgent heat?: The effect of adding andalusite is better

Q: How to use the firebrick to build crucible furnace? How to calculate its furnace's width and depth?: 1, classify according to the smelting method : Open-hearth?furnace steel: Including carbon and low-alloy steel. According to the different lining material, there are acidic and basic open hearth steel two types. Converter steel: Including carbon and low-alloy steel. According to different positions of blowing oxygen, there are bottom blowing, side blowing and BOF steel three types. Electric furnace steel: Mainly alloy steel. According to the different types of electric furnace and electric arc nail fixed Li modified cool boat to raise spending whale steel, induction furnace...

Q: What are the differences and uses of non clay bricks, non clay bricks and ordinary red bricks?: Just bricks without claySuch as foam hollow bricks, straw bricks, and some other cement bonded solid, hollow bricks and so on

Q: The service life of the refractory brick of the intermediate frequency electric furnace, how long is the replacement period.: There is no standard. As long as the induction coil can be fixed and furnace lining can be built, the service life will be different. Replace it if it's broken, and there is no problem to take it apart. Buy a backup. And the textures of refractory brick are not the same in different places.