High Alumina Insulating Fire Brick for Boiler/Furnace
- Ref Price:
-
- Loading Port:
- China main port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 10 m.t.
- Supply Capability:
- 100000 m.t./month
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
Quick Details
| Place of Origin: | Henan, China (Mainland) | Shape: | Brick | Material: | Mullite |
| SiO2 Content (%): | 0 | Al2O3 Content (%): | 52-72% | MgO Content (%): | 0 |
| CaO Content (%): | 0 | Refractoriness (Degree): | 1770°< Refractoriness< 2000° | CrO Content (%): | 0 |
| SiC Content (%): | 0 | Brand Name: | Lite | Size: | 230*114*65mm |
| Fe2O3 /%: | 0.8-1.0 | Bulk Density g/cm3: | 1.0~1.2 | Cold crushing strength/ Mpa: | 2.5~5.0 |
| Reheating Linear Change(%)°C X 12H: | ≤1 (1350℃-1650°C) | Thermal Conductivity(W/m.k)(350°C): | 0.32-0.44 | Weight of brick: | 1.0-2.0kg |
| Working temperature: | less than 1600°C | Sample: | free |
Packaging & Delivery
| Packaging Details: | 1.On wooden pallets with plastic cover 2.According to customer's demands |
| Delivery Detail: | Within 30 days |
Brick Shape and Mullite Material high temperature light weight high alumina insulating fire brick for boiler/furnace
Product Description
1.Description
High alumina insulating fire brick, using high pure mullite as raw material, is made by adding alumina powder according to different type and then sintering in high temperature. The Al2O3 content is 50-85%.
2.Feature
1.Low levels of iron and other impurities
2.High mechanical intensity
3.High refractoriness, can contact with the flame directly, suitable for various atmosphere
4.High porosity, low volume density, low thermal conductivity
5.Good heat insulating performance and energy-efficient
6.Low creep rare at high temperature,good thermal shock stability
7.Chemical corrosion resistance
8.Long service life
3.Technical Data
Item | High alumina insulating fire brick | |||||
1.0 | 1.0 | 1.0 | 1.0 | 1.2 | 1.2 | |
Al2O3/% | ≥52 | ≥55 | ≥60 | ≥65 | ≥65 | ≥72 |
Fe2O3/% | ≤1.0 | ≤0.8 | ≤0.8 | ≤0.8 | ≤0.8 | ≤0.8 |
Bulk Density(g/cm3) | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.2 | ≤1.2 |
Cold Crushing Strength Mpa | ≥3.5 | ≥3.5 | ≥4.0 | ≥3.0 | ≥5.0 | ≥2.5 |
Reheating Linear Change (%)°C X 12H | 1350℃ ≤1 | 1400℃ ≤1 | 1500℃ ≤1 | 1550℃ ≤1 | 1550℃ ≤1 | 1650℃ ≤1 |
Thermal Conductivity(W/m.k)(350°C) |
0.33 |
0.33 |
0.33 |
0.32 |
0.35 |
0.44 |
4.Application
High alumina insulating fire brick can be in direct contact with the flame,this insulating brick can be used as linings or as thermal preservation layers in various industrial furnaces and kilns in metallurgical industry, ceramic industry, chemical industry, machinery industry, such as blast furnace, hot blast stoves ,electric arc furnace, cement kiln,melting furnace, ignition furnace, flue, refining equipment, heating equipment and piping, regeneration device, gas furnace, soaking furnace, annealing furnace, heat reaction chamber and other thermal industrial equipment.
- Q: Introduction of high alumina brick
- High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.
- Q: Application characteristics of high alumina brick
- Load softening temperature. The softening temperature of high alumina brick products decreases with the increase of silica and alkali metal oxide content, but is higher than that of clay brick products, which is about 1420 - 1530 degrees centigrade. Al2O3. The softening temperature of corundum brick with content greater than 95% can reach above 1600 DEG C.
- Q: What are the common thermal insulation materials for thermal conductivity?
- Aerogels are known to be the lightest solid materials in the world. It is made of nanometer silica aerogel as main material and is compounded by special process. The utility model has the advantages of high temperature resistance, low thermal conductivity, small density, high strength, green environment protection, waterproof and non inflammable performance. At the same time, with excellent sound insulation and shock absorption performance, it is now widely used in metallurgy, chemical, national defense, aerospace and other fields, is an indispensable high-performance insulation materials.
- Q: What are the characteristics of high alumina bricks?
- High thermal stability, fire resistance above 1770. Slag resistance is good, used for masonry steel smelting furnace, glass furnace, cement rotary furnace lining. High R.U.L, low creep high alumina brick with high grade bauxite, fused corundum, fused mullite as main raw material of high-grade refractory materials.
- Q: What does refractory consist of?
- Refractory materials can be divided into main raw materials and auxiliary raw materials according to their function in the production process of refractory materials.The main raw material is the main body of refractory. Auxiliary raw materials can be divided into binders and additives. The role of bonding agent is to make the refractory body in the production and use process has enough strength. There are commonly used lignin, phenolic resin, asphalt, cement, water glass, phosphoric acid and phosphate, sulfate, some main raw material itself has the effect of binder, such as clay; additive is to improve the production of refractory materials and construction technology, or strengthen the refractory material of some properties, such as stabilizer, water reducing agent, inhibitor, plasticizer, foaming agent, dispersing agent, bulking agent, antioxidant.
- Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?
- The super high alumina brick in high alumina refractory brick has the highest refractoriness, and the corresponding production cost is higher.
- Q: How to test the aluminium bricks of high alumina refractory bricks?
- Before making bricks, the raw materials are usually tested and tested to see if the aluminum content is up to standard
- Q: What kind of material is the general metal case?
- Generally speaking, the outer surface of the case is usually made of a steel plate of more than 1 millimeters. The thickness and the material of the steel plate are directly related to the rigidity of the case, as well as the capability of sound insulation and anti electromagnetic radiation. The regular manufacturers of the chassis plate thickness not less than 1.3mm, but there are also some small manufacturers with a thickness of only about 1mm steel, we do not need the ruler to the amount, as long as you put him up, the more weight in the same volume of the chassis is better, in addition, we can also use the finger bomb case shell. If you can hear the crisp percussion sound proof of the casing plate is thin and brittle, if you hear is relatively dull and heavy sound that the chassis material must be good, good general steel plate coated with a layer of thin zinc (bright part), so it can withstand high strength, impact resistance, hardness high elasticity. The frame parts of the chassis are made of high quality materials with high hardness. They are bent into angle shapes or strip shapes. We can shake the chassis frame of the case by hand. Good chassis should be relatively stable, and inferior chassis light is easy to shake. When choosing, we should also pay attention to the outer edge of the case and the edge of the inner bracket. Whether the incision is smooth or not, a good case will not appear in the case of rough edges, sharp edges, burrs and so on. While the poor case appears above phenomenon, often appear when installing the blood splattered". Generally speaking, the chassis must go through the corresponding grinding process before leaving the factory. The edge of the flat plate some burr, edges and corners are rounded, the corresponding fold some corner. When you install such a case, you don't worry about cuts, and some rough, poorly built cabinets tend to scratch your hands.
- Q: Does the chimney have high acid resistance?
- If it is an ordinary high alumina brick, it does not meet the requirements of acid resistance, and only the chimney lined with acid resistant bricks.
- Q: Which thermal shock stability of clay brick and high alumina brick is good?
- High alumina brick is made of superfine alumina, fused corundum and fused mullite as main refractory materials.
Send your message to us
High Alumina Insulating Fire Brick for Boiler/Furnace
- Ref Price:
-
- Loading Port:
- China main port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 10 m.t.
- Supply Capability:
- 100000 m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches