High Alumina Brick - Refractory High-Alumina Bricks (Al2O3 48%~99%)
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 30 m.t.
- Supply Capability:
- 20000 m.t./month
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
Product Description
Alumina bricks are made from bauxite of super quality, bonding chamotte and additives. The main Al203 content is 48%-99%. The advantages of high alumina bricks are high refractoriness, anti alkaline/acid erosions, good strength under high temperature and good thermal shock resistance. High alumina bricks were widely accepted in thermal equipment of metallurgy, petroleum, chemical industry, construction materials, machinery and militaries etc.
Various Grades Products for Your Different Industries & Furnaces
High Alimina Bricks for blast furnaces
Corundum Mullite Bricks For Blast Furnaces
Mullite Bricks for Blast Furnaces
High alumina bricks for hot blast furnaces
Low Creeping High Alumina Bricks series for Hot Blast Stove
Low Creeping Andalusite Bricks for Hot Blast Stove
Low Creeping and Anti-Thermal Shock Alumina Bricks for Hot Blast Furnaces
High Alumina Bricks for Blast Stove Burner
High Alumina Bricks for EAF Roof
High Alumina Bricks for Ladles
Anti-Spalling High Alumina Bricks for Cement Kilns
Unfired High Alumina Bricks for Cement Kilns
High Alumina Bricks for General Uses
Good Price & Fast Delivery & OEM Service
Usually we can finish the production within 30 days. Some stardard products we have stocks in China or abroad which can make the delivery time very fast and short.
We supply not only the standard size products, we also produce basing customers' drawings, after we check your furnace application and drawings, we will give you the most cost efficient solutions.
Long Life Span and Best After-sales Serivice.
Our advanced production equipment and good educated workers & most strict quality control process make sure the best quality bricks to be made from our production lines. We also supply good technical support after sales and grow together with our customers.
Specification:
Item Specifications | LZ-48 | LZ-55 | LZ-65 | LZ-75 | LZ-80 | LZ-85 | |
Al2O3 % | ≥48 | ≥55 | ≥65 | ≥75 | ≥80 | ≥85 | |
Fe2O3 % | ≤2.5 | ≤2.5 | ≤2.0 | ≤2.0 | ≤2.0 | ≤1.8 | |
Refractoriness°C | 1760 | 1760 | 1770 | 1770 | 1790 | 1790 | |
Bulk Density≥ g/cm3 | 2.30 | 2.35 | 2.40 | 2.45 | 2.63 | 2.75 | |
Apparent porosity % | ≤23 | ≤23 | ≤23 | ≤23 | ≤22 | ≤22 | |
Refractoriness under load 0.2MPa°C | 1420 | 1470 | 1500 | 1520 | 1530 | 1550 | |
Cold crushing strength MPa | 45 | 45 | 50 | 60 | 65 | 70 | |
Permanent linear chang % | 1500°C×2h | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 |
why us
1. We are a manufacturer, which can control the cost easilier than trade company also can give you anwer more quickly.
2. As a manufacturer, we know much in technique and can give you more support in technique problem.
3.We establish the company and began to produce refractory materials since 1988. We have longtime and mature experience for entire production.
4.Our products are complete in specifications with various of sizes.
5. We enjoy a good reputation in the customers in domestic and overseas markets.
- Q: In 2016, a few of the traditional refractory materials will be able to survive
- In short, the overall market of refractory enterprises is in a turbulent adjustment process, but the volume is still in place. Elimination is inevitable, as to how many can be eliminated, dare not assert.
- Q: What's the difference between high alumina refractory bricks and high alumina refractory bricks?
- High alumina refractory brick in all thermal shock properties except performance are better than clay refractory brick, masonry in furnace and thermal equipment, such as clay bricks can be competent the work environment is not high aluminum brick masonry.
- Q: The difference between aluminium refractory and magnesia refractory
- Therefore, the difference between the two is a neutral, one is alkaline, the original product is different naturally.
- Q: Can high alumina brick resist carburizing?
- It is heavy brick mullite brick, brick to do the heavy weight to more than 2.4 manufacturers can achieve a few feeling
- Q: How much is one ton / ton of high alumina refractory brick?
- The market price of about super high aluminium brick price at 3000 yuan / ton, a high aluminum brick at around 2500 yuan / ton, two high aluminum bricks at around 2100 yuan / ton three grade high alumina bricks at around 1850 yuan / ton for reference, choose to buy the area is not the same as the prices are not the same.
- Q: How to distinguish the good or bad of the high aluminum brick?
- The general high alumina bricks used in the steel, steelmaking, hot blast furnace, electric furnace, blast furnace, reverberatory furnace, rotary kiln lining of industrial furnace in China, mainly composed of a bauxite; sillimanite minerals (including kyanite, andalusite, sillimanite etc.); synthetic material, such as alumina synthesis of mullite, corundum, etc.. High aluminum brick has good quality, high refractoriness, long life and other characteristics, is the main use of refractory brick kiln products, commonly used units can not distinguish the quality and grade of high aluminum brick right in the procurement time, caused by the high prices to buy low grade products, thereby reducing the furnace life therefore, Zhengzhou's Sindh yuan refractory material factory in here is simple to introduce how to identify the quality when purchasing brick high alumina brick.Color: in the purchase of high alumina brick, first of all to see the color, high quality aluminum brick surface smooth, yellow color white, four sides smooth, no broken angle, no cracksWeight: the weight of a block of bricks to be called, according to the standard weight level, high aluminum brick weight of 4.5 kg. Two grade high alumina brick weighs 4.2 kg, three high aluminum brick weighs 3.9 kg, the same level, the same parameters can reach this standard can be regarded as high-quality high aluminum bricks, the opposite is not up to the weight that the quality is good, if there is a crack, four angle uneven, off angle phenomenon, then substandard products, some of the above points to help to the purchaser
- Q: What is the apparent porosity of high alumina brick?
- Total porosity is porosity refers to the total volume of sample porosity in the percentage of total volume of samples. Apparent porosity refers to the percentage of the total volume of openings, pores, and total specimens in the sample.
- Q: What kind of material is the general metal case?
- Generally speaking, the outer surface of the case is usually made of a steel plate of more than 1 millimeters. The thickness and the material of the steel plate are directly related to the rigidity of the case, as well as the capability of sound insulation and anti electromagnetic radiation. The regular manufacturers of the chassis plate thickness not less than 1.3mm, but there are also some small manufacturers with a thickness of only about 1mm steel, we do not need the ruler to the amount, as long as you put him up, the more weight in the same volume of the chassis is better, in addition, we can also use the finger bomb case shell. If you can hear the crisp percussion sound proof of the casing plate is thin and brittle, if you hear is relatively dull and heavy sound that the chassis material must be good, good general steel plate coated with a layer of thin zinc (bright part), so it can withstand high strength, impact resistance, hardness high elasticity. The frame parts of the chassis are made of high quality materials with high hardness. They are bent into angle shapes or strip shapes. We can shake the chassis frame of the case by hand. Good chassis should be relatively stable, and inferior chassis light is easy to shake. When choosing, we should also pay attention to the outer edge of the case and the edge of the inner bracket. Whether the incision is smooth or not, a good case will not appear in the case of rough edges, sharp edges, burrs and so on. While the poor case appears above phenomenon, often appear when installing the blood splattered". Generally speaking, the chassis must go through the corresponding grinding process before leaving the factory. The edge of the flat plate some burr, edges and corners are rounded, the corresponding fold some corner. When you install such a case, you don't worry about cuts, and some rough, poorly built cabinets tend to scratch your hands.
- Q: What causes breakage of refractory bricks?
- Refractory brick is a non metal mineral products can be used in the high temperature of 1550 DEG C under belongs to a class of inorganic, used in high-temperature furnace lining materials as protection kiln, which causes damage, usually have these points.Furnace temperature is not clear, there is no corresponding choice of refractory bricks.Physical impact, abrasion and erosion cause damageChemical factors, especially chemical industry, should be made of refractory bricks, which should be resistant to penetration and erosionIV: products from the factory when the factory did not pass the quality inspection standards
- Q: What is the difference between fireclay bricks and high alumina refractory bricks?
- A neutral refractory with an alumina content of more than 48%. Made from alumina or other raw materials of high alumina content; formed and calcined. High thermal stability, fire resistance above 1770. Slag resistance is good, used for masonry steel smelting furnace, glass furnace, cement rotary furnace lining.
Send your message to us
High Alumina Brick - Refractory High-Alumina Bricks (Al2O3 48%~99%)
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 30 m.t.
- Supply Capability:
- 20000 m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords