High Alumina Brick for Furnace for Steel

High Alumina Brick for Furnace for Steel

Ref Price:
get latest price
Loading Port:
Tianjin
Payment Terms:
TT OR LC
Min Order Qty:
1 m.t.
Supply Capability:
10000 m.t./month

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Description:

High Alumina Fire Brick for Furnace for Steel is widely used in the lining of blast furnace,hot blast furnace,glass furnace and other industrial furnace,it has good performance of high-temperature resistance, corrosion resistance , abrasion resistance  and spalling resistance. Meanwhile, as the forming process is advanced,this product has very compact structure and small reheating linear change.

 

Advantages of High Alumina Fire Brick:

High refractoriness.

Good spalling resistance and wear resistance.

Good corrosion resistance.

Good thermal shock resistance.

 

Applications:
High Alumina Fire Brick is highly applied in below:

Steel furnaces

Iron making furnaces

Glass kiln

Ceramic tunnel kiln

Cement kiln

 

Payment term:T/T 30 deposit after order confirmed,the balance after goods ready before shipping,or L/C, or Western Uninon for small amount.

Lead time:Normally in 5-10 days after deposit received

Sample apolicy:Sample are always available for each modle

Shipping port: Tianjing

 

Technical Data Sheet of High Alumina Fire Brick:

PARAMETER

XR-CZ-01

XR-CZ-02

XR-CZ-03

Drawer

Pushing pedal

Al2O3 %

SiO2 %

MgO %

K2O %

NaO %

38-46

42-45

40-48

43-52

48-50

50-52

5-8

5-6

5-6

1.7

1.7

2.1

0.5

0.9

0.5

0.5

0.7

0.3

0.5

Modulus of rupture Mpa

18

20

24

----

----

Refractoriness under load 

1410

1410

13900

1390

1400

Apparent porosity %

22

26

30

27-30

25

Bulk density %

2.15

2.0

1.9

2.05

2.15

Thermal expansion coefficient

3.0

3.0

2.3

2.3-2.6

2.5-3.0

Thermal conductivity W/M.K

1.0-1.5

Highest working temperature

1300

1350

1300

 

 

 

 

 

 

Q: What are the high aluminum bricks made of?
It's OK to use corundum bricks and alumina hollow ball bricks to build a furnace,
Q: Introduction of high alumina brick
High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.
Q: What are the requirements for Rubble backfill height?
Backfill should be filled with large stones, big face, small face upward, the decoration is stable, and then use small stones leveling, the gap between the stones can be swept into the slag, gravel, so that the gap filled.
Q: Application characteristics of high alumina brick
Slag resistance. Due to the high alumina brick products in the three oxidation of two aluminum is neutral and high content, so this material products for acid-base slag corrosion resistance.
Q: The difference between aluminium refractory and magnesia refractory
Aluminum refractory belongs to neutral refractory material, usually refers to silicon aluminum refractory materials, such as: high alumina brick, clay brick, high alumina castable and other products, the production of raw materials is mainly bauxite.
Q: How are the high alumina bricks fired?
According to the quality requirements of different grades of high alumina brick, choose different grades of bauxite raw materials, it is conducive to rational use, fine materials, fine distribution, as far as possible not to use mixed grade severe raw materials. The quality of the clinker depends on the calcination temperature, calcination temperature, sintering temperature should be generally reached or slightly higher than that of alumina clinker sintering, to ensure the full and possible high volume density, and the two secondary Mullitization and sintering shrinkage effect in calcination process. Lightweight high alumina brick, also known as high aluminum insulation brick (high-aluminium heat insulating brick). A lightweight refractory consisting of mullite and glass phases or corundum in excess of 48%. The volume density is 0.4 ~ 1.35g/cm3. The porosity is 66% ~ 73%, and the compressive strength is 1 ~ 8MPa. Better thermal shock resistance.
Q: How to make refractory bricks and boiler wall adhesion more firm?
Suggest that you use fire brick to increase the length of brick or pull the amount of turn, and use high temperature mortar masonry
Q: Are there any differences between insulating bricks and refractory bricks?
As the name suggests, the main role of insulating brick is used to preserve heat and reduce the loss of heat. Such as: Molai S; and the firebrick is mainly used to withstand flame burn. Bricks usually do not contact fire directly, while refractory bricks usually contact the flame directly.
Q: What are the requirements for refractory materials in heat treatment furnace?
Refractoriness is the property of a refractory against high temperature, which means the temperature at which a refractory is softened to some extent after heating, but not its melting point. According to the degree of refractory, refractory materials can be divided into: General refractories, refractory degree is 1580 to 1770 DEG C; advanced refractories, refractory degree is 1770 to 2000 DEG C; special refractory material, refractory degree is greater than 2000 DEG C.
Q: How high can aluminum bricks expand at 80O degrees of heat?
When an object is heated, the particle moves faster and thus occupies additional space. This phenomenon is called dilation.