High Alumina Brick for Steel Ladle - High Alumina Brick Solution

High Alumina Brick for Steel Ladle - High Alumina Brick Solution System 1

High Alumina Brick for Steel Ladle - High Alumina Brick Solution System 2

High Alumina Brick for Steel Ladle - High Alumina Brick Solution System 3

High Alumina Brick for Steel Ladle - High Alumina Brick Solution System 4

High Alumina Brick for Steel Ladle - High Alumina Brick Solution

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 1 pallet

Supply Capability:: 5000 pallet/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$High Alumina Brick UAL48 - High Quality Refractory Material$

High Alumina Brick UAL48 - High Quality Refractory Material

High Alumina Brick for Mining Industry - 92% Alumina Content

$glass furnace fire brick price for sale, Sintered zirconia corundum,high aluminum refractory brick$

glass furnace fire brick price for sale, Sintered zirconia corundum,high aluminum refractory brick

$High Alumina Brick Industrial Pizza Stone Refractory Pizza Stone$

High Alumina Brick Industrial Pizza Stone Refractory Pizza Stone

High Alumina Bricks with Superior Resistance

$High Alumina Refractory Bricks for Steel Industry$

High Alumina Refractory Bricks for Steel Industry

High Alumina Brick - Insulating Fire Brick for Foundry Furnace

High Alumina Magnesite Brick for Cement and Glass Plant

Brief discription for High Alumina Brick for steel ladle

CMAX High Alumina Brick for steel ladle are classified according to alumina content ranging from 48% to 90%.

CMAX High Alumina Brick for steel ladle are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln,regenerator, etc.

Brief features for High Alumina Brick for steel ladle

◆Low thermal conductivity

◆Excellent acid and base slagging resistance

◆High refractoriness

◆Excellent thermal shock resistance

◆Excellent mechanical strength

◆Good spalling resistance and wear resistance.

◆Good corrosion resistance.

◆High-temperature creep rate is quite low.

◆Good volume stability at high temperature.

◆Low bulk density, low thermal conductivity, good thermal insulation performance.

Technical data for High Alumina Brick for steel ladle

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories,at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time,seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:How to slove the quality problems?

A:If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.

Q: What is the heat preservation material used in a laboratory furnace?: Thermal insulation cotton is a high-purity clay clinker, alumina powder, silica powder, chromium sand and other raw materials in the industrial furnace melting at high temperature, forming fluid. Then, compressed air is used to blow or use the wire throwing machine to turn the yarn into a fiber shape. After the cotton collector is collected, the cotton is formed into a heat preservation cotton.The high alumina brick is usually made of high alumina clinker with small amount of clay. After grinding, the high alumina brick is poured and shaped in the form of slurry by the way of gas generation or foam, and it is burnt at 1300~1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.

Q: What are the grades of high alumina bricks?: High alumina brick according to the aluminum content is generally divided into: super high alumina brick, a high aluminum brick, two high alumina brick, three high alumina brick

Q: How much is one ton of high alumina refractory brick?: Three high aluminum refractory brick Zhengzhou Kuwait is generally around 800. 32 years of experience, good.

Q: What's the difference between a well type annealing furnace and a box type annealing furnace?: Box annealing furnace application: mainly used for quenching, normalizing, annealing and other conventional heat treatment equipment for steel parts. Features: 1, electric loading, high productivity, heat treatment is especially suitable for small and medium-sized parts, such as 30%, uniform temperature, intelligent digital display meter PID (pictured) automatic temperature control, high precision; 2, electric discharge loading convenient, as good; 3, door and seal the oven body is sealed automatically, without manual seal; 4, equipped with electric interlock protection device, and can prevent the fault accident due to the error. Bell type annealing furnace four bell type annealing furnace bell type annealing furnace is mainly used for annealing sheet metal in natural atmosphere and normalizing treatment of steel parts. 1, special steel, precision alloy large all fiber trolley type resistance furnace, strip, wire bright annealing. 2 、 annealing of special steel casting and forging. 3. Annealing of silicon steel sheet. 4, metal and non metal powder sintering pieces etc..

Q: Aluminum content 38, silicon content 55 What refractory bricks?: Semisilica brick: the content of Al2O3 is 15% ~ 30% of aluminium silicate refractory products. Manufacturing products are semi silica quartz containing impurities or native clay kaolin, refractory clay or kaolin beneficiation tailings and the pyrophyllite

Q: Difference between low creep high alumina brick and ordinary high alumina brick: The question is good, these two belong to the high aluminum brick products, when many manufacturers buy, I do not know how to distinguish.

Q: How high can aluminum bricks expand at 80O degrees of heat?: The expansion of high alumina brick is not only related to temperature, but also related to its material composition. The refractory temperature of high alumina brick is above 1770 centigrade. The temperature of 800 DEG C has little influence on the expansion of high alumina brick.

Q: Use of high alumina refractory bricks?: Because of the high Al2O3 high aluminum products, low impurity content, the formation of fusible vitreous body less so than the clay brick high load softening temperature, but because mullite crystallization has not formed the network organization, so the load softening temperature is not high silica brick.

Q: How does the physicochemical index change when the high alumina brick is used at high temperature?: If the range of softening temperature exceeds the load, the constants of other physical and chemical indexes will also increase or decrease.

Q: What is the high temperature limit of refractory bricks and refractory soil?: Refractory bricks are stone powder and clay paste. They are fired in a kiln of 1300 degrees. The upper limit is 1500 degrees above normal pressureRefractory bricks - refractory materials of a specified shape and size.