High Alumina Brick for Industrial Furnaces

High Alumina Brick for Industrial Furnaces System 1

High Alumina Brick for Industrial Furnaces System 2

High Alumina Brick for Industrial Furnaces

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 2 m.t

Supply Capability:: 5000 m.t/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

High Alumina Brick UAL65 - High Alumina Brick

$High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)$

High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)

High Alumina Brick Rectangular Cordierite Pizza Oven for Pizza Cooking

High Alumina Bricks (48% to 90% Alumina Content)

$High Alumina Refractory Bricks for Electric Furnace$

High Alumina Refractory Bricks for Electric Furnace

High Alumina Magnesite Brick for Cement and Glass Plant

High Alumina Bricks for Nonferrous Metals

$High Alumina Refractory Bricks for Iron and Steel Industry$

High Alumina Refractory Bricks for Iron and Steel Industry

Brief discription for High Alumina Bricks for industrial stoves

CMAX High Alumina Bricks for industrial stoves are classified according to alumina content ranging from 48% to 90%.

CMAX High Alumina Bricks for industrial stoves are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln,regenerator, etc.

Brief features for High Alumina Bricks for industrial stoves

◆Low thermal conductivity

◆Excellent acid and base slagging resistance

◆High refractoriness

◆Excellent thermal shock resistance

◆Excellent mechanical strength

◆Good spalling resistance and wear resistance.

◆Good corrosion resistance.

◆High-temperature creep rate is quite low.

◆Good volume stability at high temperature.

◆Low bulk density, low thermal conductivity, good thermal insulation performance.

Technical data for High Alumina Bricks for industrial stoves

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories,at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time,seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:After an order is confirmed,when to deliver?

A:15-25days after deposit.

Q6:Is your company accept customization?

A:We have own factory and excellent technical team,and we accept OEM service.

Q: What is the heat preservation material used in a laboratory furnace?: Thermal insulation cotton is a high-purity clay clinker, alumina powder, silica powder, chromium sand and other raw materials in the industrial furnace melting at high temperature, forming fluid. Then, compressed air is used to blow or use the wire throwing machine to turn the yarn into a fiber shape. After the cotton collector is collected, the cotton is formed into a heat preservation cotton.The high alumina brick is usually made of high alumina clinker with small amount of clay. After grinding, the high alumina brick is poured and shaped in the form of slurry by the way of gas generation or foam, and it is burnt at 1300~1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.

Q: What's the difference between a well type annealing furnace and a box type annealing furnace?: Box annealing furnace application: mainly used for quenching, normalizing, annealing and other conventional heat treatment equipment for steel parts. Features: 1, electric loading, high productivity, heat treatment is especially suitable for small and medium-sized parts, such as 30%, uniform temperature, intelligent digital display meter PID (pictured) automatic temperature control, high precision; 2, electric discharge loading convenient, as good; 3, door and seal the oven body is sealed automatically, without manual seal; 4, equipped with electric interlock protection device, and can prevent the fault accident due to the error. Bell type annealing furnace four bell type annealing furnace bell type annealing furnace is mainly used for annealing sheet metal in natural atmosphere and normalizing treatment of steel parts. 1, special steel, precision alloy large all fiber trolley type resistance furnace, strip, wire bright annealing. 2 、 annealing of special steel casting and forging. 3. Annealing of silicon steel sheet. 4, metal and non metal powder sintering pieces etc..

Q: Can high alumina brick resist carburizing?: It is heavy brick mullite brick, brick to do the heavy weight to more than 2.4 manufacturers can achieve a few feeling

Q: Corundum, high alumina and fireclay refractory difference is what: Corundum is unknown. The high alumina brick has higher aluminum content than the clay brick, and the temperature resistance is higher than 300 degrees. It is more durable and durable than the clay brick. The production process of high alumina brick is better than that of clay brick. For example, the weight of good clay brick is 3.7kg, and that of high alumina is 4.2kg. Good density. But the price of high aluminum is too high: ordinary clay brick (standard brick example) in 1.1--2.5 yuan / block, high aluminum to 4.5 yuan / block, or even more expensive. The extra high aluminum has reached 5000 tons. Say straight white point is: under the same conditions, clay brick for a period of one year, then the high aluminum for more than three years.

Q: What are the high temperature refractory mortars made of?: Siliceous mud, mineral composition and chemical composition is similar with silica, excellent corrosion resistance, water glass slurry, drying shrinkage, but also can be used for bonding fiber products, sealing furnace wall.

Q: What are the specifications for bricks?: Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels. Clay brick materials, cheap, durable, and fire prevention, heat insulation, sound insulation, moisture absorption and other advantages, is widely used in civil engineering. Waste brick can also be used as aggregate of concrete. In order to improve the shortcomings of ordinary clay bricks, such as small, self important and waste of soil, they are developing in the direction of light weight, high strength, hollow and big blocks.

Q: Are there any differences between insulating bricks and refractory bricks?: The refractoriness of insulating bricks is generally below 1400 tons, while the refractoriness of refractory bricks is above 1400 degrees. 3. density insulation bricks are generally lightweight insulation materials, the density is generally in 0.8-1.0g/cm3, and the density of refractory bricks are basically above 2.0g/cm3.

Q: The difference between ordinary and diatomite brick refractory brick: To say the difference, the material is the biggest difference. There are diatomite brick density, compressive strength of small brick kiln belongs to the outer thermal insulation, and heavy refractory brick kilns for multi village in direct contact with the flame, high temperature resistance, good compressive strength, but no insulation. Hope to help you.

Q: What does refractory consist of?: According to the chemical characteristics of refractory raw materials can be divided into acidic refractory materials, such as silica, zircon etc.; neutral refractory raw material, such as corundum, bauxite, mullite (acidic) (acidic), Ge (alkaline) iron and graphite; alkaline refractory materials, such as magnesite, dolomite, magnesium sand calcium sand.

Q: The difference between light high alumina brick and heavy aluminum brick: Lightweight high alumina bricks, commonly called insulating refractory bricks, also known as insulating refractory bricks. First of all, literally, lightweight aluminum bricks and heavy aluminum bricks are very different in weight. Lightweight high alumina bricks, also called insulated high alumina bricks, are designed for insulation and heat preservation. In normal use, the utility model is not directly contacted with the furnace temperature, and is a refractory brick product which is close to the furnace wall and has the function of heat insulation and heat preservation.

Send your message to us

*Email

*TEL

*Quantity

*Unit