Best Price For Prepainted Galvalume Steel Coil-EN 10169

Best Price For Prepainted Galvalume Steel Coil-EN 10169 System 1

Best Price For Prepainted Galvalume Steel Coil-EN 10169

Ref Price:

Loading Port:: China Main Port

Payment Terms:: T/T or L/C

Min Order Qty:: 50mt m.t.

Supply Capability:: 100,000 mt/year m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Best Quality for Hot Dipped Galvanized Steel Coil

Hot Rolled Steel Coil Best Quality from China

Hot Dip Galvanized Steel Coil-Minimum spangle-Hot Sell

Aluzinc Steel Coil-AFP

Hot dip galvanized steel coil

Steel Coil Price 2015 New Products Hot Dipped Galvanized

Color Coated galvanized Cold Rolled Steel coil

Colored Coated Galvalume Steel Coils for Building

General Information Of Prepainted Galvalume Steel Coil-EN 10169

With Aluzinc steel as base metal, after pretreatment (degrease and chemical treatment) and liquid dope with several layers of color, then after firing and cooling, finally the plate steel is called pre-painted aluzinc steel. Pre-painted aluzinc steel is good capable of decoration, molding, corrosion resistance. It generally displays superior workability, durability and weather resistance.

Thickness 0.23-1.2mm (BMT)

Zinc Coating 50-150g/m2

Color According to RAL color fan

Internal Diameter 508mm or 610mm

Coil Weight 4-8MT

Quality Commercial and structural quality

Paint Polyester paint for topside, epoxy for reverse

Standard JIS G 3322, ASTM A755M, EN 10169

Base Steel Grade

SGCC,SGCD,DX51D+Z,DX52D+Z;S200GD,S220GD, S280GD,S350GD,CS,FS,SS

Chemical Composition Of Prepainted Galvalume Steel Coil-EN 10169

C	Si	Mn	P	S
0.04-0.06%	0.01-0.03%	0.18-0.22%	0.014-0.016%	0.006%-0.009%

Technical Data Of Prepainted Galvalume Steel Coil-EN 10169

Yield Strength	(Mpa) 280-320
Tensile Strength	(Mpa) 340-390
Elongation	20%-30%
Reverse Impact	9J
T-bending	≥2T
Pencil Hardness	≥2H
Duration Of Salt Spray Test	500 H
Bending At 180 Degree	No crack, purling and fraction

Application Of Prepainted Galvalume Steel Coil-EN 10169

It can be widely used in transportation, light industry, civil usage and farming. It is also the perfect building material in construction for making steel roofing, corrugate sheet, sandwich panel for wall or roofing, facade wall, shutters and home appliance.

Packaging & Delivery Of Prepainted Galvalume Steel Coil-EN 10169

Anti-damp paper inside full wrapped with plastic film, iron sheet outside on wooden pallet in 20 feet container with 25mt.

Prepainted Galvalume Steel-EN 10169

Q: Steel used to be made in the #92;Bessemer Converter, write about how steel making processes today produce better quality steel????: how we can prepared steel by using converter? ans it

Q: I need to know how you rate the hardness of steel any ideas?: There's an instrument called a hardness tester. It has a stylus which is pressed into the surface of a sample of steel with a calibrated amount of force. The distance it penetrates tells you how hard the steel is. (This is sometimes called 'indentation hardness'). The most common scale is the Rockwell Scale. Actually it gets a little complicated because there are several scales, one for tungsten carbide (the hardest man-made material), one for aluminum and brass and soft steels, and one for hardened steels. Another scale for indentation hardness is the Brinell scale. It's a little less complicated, with one scale to measure the hardness of wood, plastic, etc. as well as steel.

Q: What are the common methods of recoiling steel coils?: There are several common methods of recoiling steel coils, depending on the specific requirements and preferences of the manufacturer or customer. One common method is known as slitting, which involves cutting the wide steel coil into narrower strips. This is achieved by passing the coil through a set of rotating circular blades that cut the steel into multiple smaller coils with desired widths. Slitting is commonly used to create coils of different sizes for various applications. Another method is called cut-to-length (CTL) recoiling, where the steel coil is cut into specific lengths as per the customer's requirements. This process involves feeding the coil through a straightening and leveling machine, followed by a flying shear that cuts the steel into desired lengths. CTL recoiling is often used in industries where precision and uniformity of steel lengths are crucial, such as construction or automotive. Additionally, there is a method called coil-to-coil recoiling, which involves rewinding the steel coil onto a new coil, with the desired dimensions and properties. This process is commonly used when the original coil needs to be resized, reconditioned, or rerolled for further processing or transportation purposes. Coil-to-coil recoiling is often done using specialized recoiling machines that ensure the proper tension, alignment, and winding of the steel coil onto the new coil. Overall, the common methods of recoiling steel coils include slitting, cut-to-length (CTL) recoiling, and coil-to-coil recoiling. Each method offers its own advantages and is chosen based on factors such as required coil dimensions, precision, efficiency, and the specific needs of the industry or customer.

Q: I have one and need info about it??....It has a wooden case around the steel necks.and 20 strings,Twin Tens.: well, it was made sometime before 1981, because that's when Fender quit making 10 string steel guitars. Without any more information than what you've given me, it could be the Pedal 2000, the PS210, or the Artist Dual 10. Fender made steel guitars from the 1950s through 1981, so it could be from any time in there. I hope you have the pedals with it. The 10-string and dual 10-string models were quite expensive in their day. Unfortunately, if you're thinking of reselling it, you're probably not going to get a lot of money for it unless you find a pedal steel player, and like I said, having all the pedals is very important in that case. Anyway, hope this helped. Good luck. If I were you I'd learn to play it. Pedal steel players are always in demand.

Q: What are the different methods of forming steel coils?: Steel coils can be formed using several methods, depending on their specific requirements and applications. These methods comprise hot rolling, cold rolling, and continuous casting. The most commonly used method for forming steel coils is hot rolling. This involves heating the steel billet or ingot to high temperatures and passing it between a series of rollers to reduce its thickness and shape it into a coil. Typically, this process is carried out above the recrystallization temperature of the steel, which allows for better shaping and improved mechanical properties. On the other hand, cold rolling is performed at or near room temperature. It entails passing the steel through a series of rollers to reduce its thickness and shape it into a coil. Cold rolling is often utilized to produce steel coils with precise dimensions and excellent surface finish. Additionally, it can enhance the strength and hardness of the steel. Another method for forming steel coils is continuous casting. This involves pouring molten steel into a continuous casting machine, where it solidifies into a strand. The strand is then continuously fed into a series of rollers, which shape it into a coil. Continuous casting offers several advantages, including improved efficiency, reduced energy consumption, and better control over the steel's composition and quality. In addition to these primary methods, there are various secondary processes involved in forming steel coils. These processes encompass pickling, annealing, and coating. Pickling is used to remove any rust or scale from the surface of the steel, ensuring a clean and smooth finish. Annealing involves heating the steel to a specific temperature and then slowly cooling it, which improves its ductility and reduces internal stresses. Coating is often applied to steel coils to provide corrosion resistance or enhance its aesthetic appeal. To summarize, steel coils can be formed using different methods such as hot rolling, cold rolling, and continuous casting. Each method offers distinct advantages and is chosen based on the specific requirements of the steel product. Additionally, secondary processes like pickling, annealing, and coating are employed to further enhance the quality and performance of the steel coils.

Q: And by how much? I'm pretty sure that sterling silver is stronger, but I'm wondering if I could still use a metal stamp to stamp into something that's stainless steel - if it would be soft enough?: No way steel is by far stronger. Tensile strength of Sterling silver 207 MPa Tensile strength of Stainless Steel 515 MPa

Q: How are steel coils used in the manufacturing of construction reinforcement bars?: Steel coils are used in the manufacturing of construction reinforcement bars by being processed and shaped into the desired size and shape. The coils are first uncoiled and straightened, then cut into shorter lengths. These shorter lengths are then bent and twisted to create the necessary patterns and shapes, which provide enhanced strength and durability to the reinforcement bars.

Q: What are the main factors that affect the strength of steel coils?: The main factors that affect the strength of steel coils are the composition of the steel, the manufacturing process, and the heat treatment applied.

Q: What are the different types of steel coil handling equipment?: Some different types of steel coil handling equipment include coil lifters, coil tongs, coil hooks, coil grabs, coil transfer carts, coil upenders, and coil cradles.

Q: Hi, does anyone know where i can find more about this topic ? fire resistant steels for structural applications. thanks: Gavin, the danger posed by steel columns and girders during a fire in a building, is not the danger of the steel melting but of the steel expanding and snapping the bolts that hold all of the steel together. Very high temperatures can be achieved in a building fire because the up-draft caused by the rising hot air, delivers a massive amount of oxygen to the burning carpet, paper and furniture. When a steel frame office tower burns, the heat expands the steel and snaps the bolts. This causes the building to fall-down and not necessarily, burn-down. I am too lazy to look-up the melting point of steel but it is not very high. That is one reason for the columns and girders in steel framed buildings, to be covered in asbestos (which is a fatally toxic material) or magnesium di-oxide.

EASTSTEEL is close to Shanghai port and Ningbo port, has be richly endowed by nature of the geographical advantage. The main color coated steel coil, galvanized steel coil etc. The company expanded after the completion of the production capacity reached 900000 tons, including 120000 tons of hot dip galvanized steel coil, line, producing 200000 tons of aluminum 450000 tons of zinc coated steel coils and 50000 tons of printing plate.

1. Manufacturer Overview

Location	Zhejiang, China
Year Established	1999
Annual Output Value	US$1 Million - US$2.5 Million
Main Markets	Europe; Africa; Mid East; Southeast Asia
Company Certifications	ISO9001；ISO14001

2. Manufacturer Certificates

a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability

a) Trade Capacity
Nearest Port	Shanghai Port
Export Percentage	41% - 50%
No.of Employees in Trade Department	50-80
Language Spoken:	Chinese, English
b) Factory Information
Factory Size:	Above 100,000 square meters
No. of Production Lines	5
Contract Manufacturing	OEM Service Offered
Product Price Range	Average