Alumina Silica Fire Brick G94 for Coke Oven

Alumina Silica Fire Brick G94 for Coke Oven System 1

Alumina Silica Fire Brick G94 for Coke Oven System 2

Alumina Silica Fire Brick G94 for Coke Oven

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 500000 pc/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Product Description:

General Information of Silica Brick For Coke Oven-G94

Our corporation produces a comprehensive range of silica bricks, with high silica content, all of these bricks exhibit excellent performance.

Our Silica bricks are the final result of blending excellent tridymite and cristobalite, as the main raw materials with cutting-edge technology, after mixing, drying, forming, in the high temperature shuttle kiln. There are also little quartz and vitreous within. We ensure you that the silica bricks made by us possess high quality standard and have gone through all the complicated quality control parameters. Their durability and strength adds life to the structure and they have the capacity of bearing high temperature.

Our competitive Advantage:

1.Competitive Price. Make the products competitive in your market.

2.Abundant Experience. Prevent cracks and twist in bricks.

3.Different Moulds. Save mould fees for you.

4.Lower ferric Oxide,porosity,higher refractoriness,density,higher CCS and exact tolerance.

5.Strict Quality Control. Meet clients’ quality requirement.

6.Safty packing,prompt delivery time,and excellent after-sales services.

7.Large stocks. Guarantee prompt delivery.

8.Professional Packing. Avoid damage and secure the goods in transportation

Silica Brick For Coke Oven---G94
Physical Properties:
Permanent Linear Change(1450℃×2h)%	%	±0.5
Apparent Porosity, %	%	≤24
Cold Crushing Strength	Mpa	30
Refractoriness Under Load (T0.6)	℃	≥1630
Thermal Expansion	%	≤1.3
Density	g/cm³	-
Chemical Analysis:
SiO₂	%	≥95
Fe₂O₃	%	≤1.5
Al₂O₃	%	≤0.8
Residual Quartz	%	≤1
Note: Technical Data are typical average results from test pieces. The technical data is offered solely for your consideration. And we reserve the right to modify the technical data without any prior notice. Users of our products should make their own tests to determine the suitability of each product for their particular purposes.

Q: The introduction of silica brick: Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature.

Q: The hot blast stove when the temperature did not rise against the brick interface decreased: Different insulation methods can be adopted according to the length of the stop time and the location and equipment of the overhaul. Gold, refractory material factory specializing in the production of various specifications of brick

Q: Why will expand when heated brick: After high temperature after the formation of tridymite and cristobalite and quartz and a small amount of residual glass phase, quartz heating to 220-240 DEG C, in a certain degree of thermal expansion, brick maximum expansion occurs in 100~300 DEG C, 300 expansion before the total amount of expansion is about 70%~75%.

Q: The specific content is what gb/t2608-2012 brick: The provisions of the brick classification, technical requirements, test methods,

Q: The introduction of silica brick: Brick refers to the content of more than 93% products SiO2. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system. The higher the content of SiO2 in silica raw material, the higher the refractoriness of the product. According to the use of brick varieties, divided into: coke oven silica brick, brick for hot blast stove, electric stove with brick, brick for glass furnaces. According to the transformation is divided into: standard bricks, tiles, bricks and general special brick etc..

Q: What is acid refractory?: Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.

Q: The high thermal conductivity of silica brick and traditional brick what is the difference?: The scale quartz is a spear shaped double crystal structure, very compact and favorable to the increase of thermal conductivity. The high thermal conductivity of silica brick in improving thermal conductivity and other performance indicators and traditional coke silicabrick agreement.That is to say, the high thermal conductivity of silica brick all inherited the traditional advantages of coke oven silica brick, on the basis of further highlight the characteristics of high thermal conductivity

Q: The difference between clay refractory bricks and refractory brick in the application.: Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.

Q: What is the silica refractory products?: Refractory brick with silica content greater than 90%.

Q: Physical solid waste disposal: Preparation of silica brick pug, a certain amount of waste silica brick used to add ingredients, for the purpose of expansion and stress reduction products when firing, reduce cracks, improve the rate of finished products.