General Information
The CMAX super-duty silica bricks for glass melting tank is characterized by high purity, less impurity, good corrosion resistance, higher bulk density, complete phase transformation, lower residual quartz, high RUL, lower thermal expansion and stable volume at high temperature. This leads to increase in service life of glass furnace and reduction in energy consumption. These products have found wide application in crown and key areas and been highly appreciated by clients.
Features
1) A variety of specifications available.
2) Satisfy various technical request.
3) Lower medium spoilage.
4) Good insulation performance and high temperature resistance.
5) High compressive strength.
6) Used in all electric products and electric heating products.
7) OEM, ODM and OBM are welcomed.
Application
Glass melting tank
Glass furnace
Hot-Blast Stoves
| Performance | |||||
| Item | Unit | 95 Al2O3 | 96 Al2O3 | 99 Al2O3 | |
| Physical Characteristics | Bulk density | g/cm3 | 3.6 | 3.6 | 3.9 |
| Water absorption | % | 0 | 0 | 0 | |
| Mechanical Characteristics | Flexural strength | Mpa | 320 | 340 | 360 |
| Hardness Vickers | Gpa | 12.2 | 13.5 | 15.6 | |
| Elastic modulus | Gpa | 280 | 320 | 370 | |
| Poisson’s ratio | - | 0.22 | 0.23 | 0.23 | |
| Thermal Characteristics | Linear expansion coefficient | (200C-5000C) 10-6/0C | 7.1 | 7.2 | 8 |
| Thermal conductivity | w/(m.k) | 16 | 24 | 32 | |
| Specific Heat | *10-3J/(kg*K) | 0.78 | 0.78 | 0.9 | |
| Electrical Characteristics | Dielectric constant (1MHZ) | - | 9 | 9.4 | 9.9 |
| Dielectric loss angle | *10-4 | 15 | 5 | 1 | |
| Dielectric strength | *106V/m | 12 | 15 | 15 | |
| Processing technology | |||||
| Process range (mm) | |||||
| Outside Diameter | 1---300 | ||||
| Inside Diameter | 0.5---300 | ||||
| Length | 0.5---1200 | ||||
| Accuracy of working (mm) | |||||
| Perpendicularity | 0.01 | ||||
| Concentricity | 0.01 | ||||
| Roundness | 0.005 | ||||
| Straightness | 0.005 | ||||
| Parallelism | 0.01 | ||||
| Planeness | 0.005 | ||||
| Roughness | 0.05 | ||||
| Fit clearance | 0.005 | ||||
- Q: The hot blast stove when the temperature did not rise against the brick interface decreased
- How to keep the brick masonry temperature not lower than 600 DEG C, while the exhaust temperature is not higher than 400 DEG C.
- Q: What is acid refractory?
- Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.
- Q: How much is the highest melting point of silicon?
- Mainly used for partition, carbonization chamber of coke oven and combustion chamber open hearth furnace regenerator and a sediment chamber, soaking furnace, glass melting furnace refractories and ceramic kiln, kiln vault and other load-bearing parts. Also used for high temperature bearing part of hot blast stove and acid open hearth furnace
- Q: Glass kiln brick for physical and chemical indicators?
- Glass kiln with high quality silica brick with silicon oxide content, low melt index, mainly used for glass kiln crown, parapet, wall hanging, small furnace arch superstructure and regenerator.
- Q: Which material is good for furnace refractory?
- Neutral refractory is mainly composed of alumina, chromium oxide or carbon. Corundum products containing more than 95% of alumina are a kind of high quality refractory materials with a wide range of uses. Chrome brick with chromium oxide as its main component has good corrosion resistance, but its thermal shock resistance is poor, and its deformation temperature is lower at high temperature. Carbon refractories with carbon bricks, graphite and silicon carbide products, low coefficient of thermal expansion, high thermal conductivity, good thermal shock resistance, high strength, resistance to acid and salt corrosion, especially weak acid has good resistance, without wetting of the metal and slag, light. It is widely used as lining material of high temperature, and also used as lining of autoclave in petroleum and chemical industry.
- Q: The brick is mainly used in the place?
- Open hearth furnace regenerator and a sediment chamber, soaking furnace, glass furnace refractory materials and ceramic brick kiln, kiln vault and other load-bearing parts.
- Q: Can not use it two brick
- The softening temperature is up to 1640~1670 DEG C, and the volume is stable at high temperature for a long time.
- Q: Common bond brick?
- Manufacturing for silica brick binder hi-li sulfate pulp waste liquid and lime milk. When lime milk is used as a bond, it acts as a plasticizer. To increase the strength of lime brick in the drying process, as mineralizer in the firing, promote the transformation of quartz.
- Q: What are the main constituents of refractory bricks?
- Clay brick and clay brick are mainly composed of mullite (25% ~ 50%), glass phase (25% ~ 60%) and square quartz and quartz (up to 30%). Usually with hard clay as raw material, pre calcined mature material, and then with soft clay, semi dry or plastic molding, the temperature at 1300~1400 C fired clay brick products. Can also be added a small amount of water, glass, cement and other binders to make non burning products and amorphous materials. It is a refractory brick commonly used in blast furnaces, hot blast furnaces, heating furnaces, power boilers, lime kilns, rotary kilns, ceramics and refractory bricks.
- Q: High temperature refractory material?
- Many kinds of refractory materials, usually by refractoriness level is divided into ordinary refractory materials (1580 to 1770 DEG C), advanced refractories (1770 to 2000 DEG C) and special refractories (more than 2000 DEG C); according to the chemical characteristics into acid refractory material, refractory materials and basic refractory materials. In addition, the refractory material used for special occasions.Now the definition of refractory materials, has not only depends on whether the refractoriness at 1580 DEG. Refers to the current refractories used in metallurgy, petrochemical, cement, ceramics and other production equipment with inorganic non-metallic materials.
Send your message to us
Silica Brick - Lightweight Refractory Silica Brick
- Ref Price:
-
- Loading Port:
- Shanghai
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 15 m.t.
- Supply Capability:
- 30000 m.t./month
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
Similar products
Hot products
Hot Searches
Related keywords