Silica Brick for Coke Oven and Carbon Calciner
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
You Might Also Like
Specifications
Item brand
Bottom and other part
Wall brick brick
Sio2% >= 94
0. 2mpa rul c >= 1650
Linear c
Item brandBottom and other partWall brick brickSio2% >= 940. 2mpa rul c >= 1650Linear changeAfter re-heating% 1450c x2h <= 0 / + 0. 2A. p. % <= 22 24C. C. S. mpa >= 30 25B. D. g / ccm >= 2. 34 2. 35ThermalDilatation% 1000c <= 1. 28 1. 30
| Performance | |||||
| Item | Unit | 95 Al2O3 | 96 Al2O3 | 99 Al2O3 | |
| Physical Characteristics | Bulk density | g/cm3 | 3.6 | 3.6 | 3.9 |
| Water absorption | % | 0 | 0 | 0 | |
| Mechanical Characteristics | Flexural strength | Mpa | 320 | 340 | 360 |
| Hardness Vickers | Gpa | 12.2 | 13.5 | 15.6 | |
| Elastic modulus | Gpa | 280 | 320 | 370 | |
| Poisson’s ratio | - | 0.22 | 0.23 | 0.23 | |
| Thermal Characteristics | Linear expansion coefficient | (200C-5000C) 10-6/0C | 7.1 | 7.2 | 8 |
| Thermal conductivity | w/(m.k) | 16 | 24 | 32 | |
| Specific Heat | *10-3J/(kg*K) | 0.78 | 0.78 | 0.9 | |
| Electrical Characteristics | Dielectric constant (1MHZ) | - | 9 | 9.4 | 9.9 |
| Dielectric loss angle | *10-4 | 15 | 5 | 1 | |
| Dielectric strength | *106V/m | 12 | 15 | 15 | |
| Processing technology | |||||
| Process range (mm) | |||||
| Outside Diameter | 1---300 | ||||
| Inside Diameter | 0.5---300 | ||||
| Length | 0.5---1200 | ||||
| Accuracy of working (mm) | |||||
| Perpendicularity | 0.01 | ||||
| Concentricity | 0.01 | ||||
| Roundness | 0.005 | ||||
| Straightness | 0.005 | ||||
| Parallelism | 0.01 | ||||
| Planeness | 0.005 | ||||
| Roughness | 0.05 | ||||
| Fit clearance | 0.005 | ||||
- Q:Can iron oxide be used as refractory material?
- Iron oxide can not be used as refractory material, but it can be used as refractory additive. Iron oxide can be used as pigment
- Q:Because of the recent relates to this industry, by way of learning to name for all raw materials, I hope knowledgeable friends exhibitions, thank you.
- The main raw material is the main body of refractory. Auxiliary raw materials can be divided into binders and additives. The role of bonding agent is to make the refractory body in the production and use process has enough strength. There are commonly used lignin, phenolic resin, asphalt, cement, water glass, phosphoric acid and phosphate, sulfate, some main raw material itself has the effect of binder, such as clay; additive is to improve the production of refractory materials and construction technology, or strengthen the refractory material of some properties, such as stabilizer, water reducing agent, inhibitor, plasticizer, foaming agent, dispersing agent, bulking agent, antioxidant.
- Q:Brick
- An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.
- Q:Such purpose and scope please give me detailed points thank you
- Acid refractory brick is mainly composed of tridymite and cristobalite and quartz and a small amount of residual glass phase.
- Q:Physical solid waste disposal
- Too much addition will reduce the refractory and mechanical strength, increase porosity, so the amount of waste brick should not be too much.
- Q:The difference between clay refractory bricks and refractory brick in the application.
- The ability of alkali resistance is poor, the thermal shock stability is the worst, and it is scrapped at one time. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.
- Q:The hot blast stove when the temperature did not rise against the brick interface decreased
- Different insulation methods can be adopted according to the length of the stop time and the location and equipment of the overhaul. Gold, refractory material factory specializing in the production of various specifications of brick
- Q:The formula in the refractory brick, and firing curve, who knows?
- By silica powder, 81-85%, perlite 15-19%, plus the total weight of the main raw materials of the following accessories
- Q:How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?
- Mainly from the impurities to determine how much, generally less impurity single color brick.
- Q:What is acid refractory?
- Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.
1. Manufacturer Overview |
|
|---|---|
| Location | |
| Year Established | |
| Annual Output Value | |
| Main Markets | |
| Company Certifications | |
2. Manufacturer Certificates |
|
|---|---|
| a) Certification Name | |
| Range | |
| Reference | |
| Validity Period | |
3. Manufacturer Capability |
|
|---|---|
| a)Trade Capacity | |
| Nearest Port | |
| Export Percentage | |
| No.of Employees in Trade Department | |
| Language Spoken: | |
| b)Factory Information | |
| Factory Size: | |
| No. of Production Lines | |
| Contract Manufacturing | |
| Product Price Range | |
Send your message to us
Silica Brick for Coke Oven and Carbon Calciner
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
Similar products
Hot products
Hot Searches
Related keywords