• Silica Brick for Coke Oven - Best Seller System 1
Silica Brick for Coke Oven - Best Seller

Silica Brick for Coke Oven - Best Seller

Ref Price:
get latest price
Loading Port:
China Main Port
Payment Terms:
TT OR LC
Min Order Qty:
-
Supply Capability:
-

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

silica bricks for coke oven passed ISO certified
1.good resistance to acid slag and good heat conductivity
2.RUL 1620

 best-selling silica bricks for coke oven passed ISO certified .it is made of quartz stone material,the content od Sio2 is above 93%,it has good resistance to acid glad and good heat conductivity,and the refractoriness is 1690-1710.C,RUL is beyond 1620.C

items

Furance bottom/

furancre wall

rests

allow deviation

SiO2 %

≥94.5

-

Al2O3 %

≤1.2

-

Fe2O3 %

≤1.2

-

CaO %

≤2.5

-

0.2MPa RUL (°C)

1650

-10

True density (g/cm3)

≤2.33

≤2.34

+0.01

Residual quarlz%

≤1.0

-

AP%

≤22

≤24

+1

CCS(MPa)

≥40

≥35

10%

PLC(1450°C *2h) %

0~0.2

-

Thermal expansion(1000°C)  %

≤1.28

≤1.30

+0.03




Q: The hot blast stove when the temperature did not rise against the brick interface decreased
Insulation of hot blast stove, key insulation silica brick hot stove, hot blast stove is shutdown or need repairing in blast furnace.
Q: Why will expand when heated brick
Because the production of raw materials are silica brick, brick with SiO2 content of not less than 95% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system
Q: What is acid refractory?
Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.
Q: Why is the new trend of the high thermal conductivity of silica brick
The use of high thermal conductivity of silica brick, reducing coke fuel consumption, reduce emissions of pollutants such as NOx, with considerable economic benefits and social benefits, is the future direction of the new technology of using coke oven refractory.
Q: Which material is good for furnace refractory?
Neutral refractory is mainly composed of alumina, chromium oxide or carbon. Corundum products containing more than 95% of alumina are a kind of high quality refractory materials with a wide range of uses. Chrome brick with chromium oxide as its main component has good corrosion resistance, but its thermal shock resistance is poor, and its deformation temperature is lower at high temperature. Carbon refractories with carbon bricks, graphite and silicon carbide products, low coefficient of thermal expansion, high thermal conductivity, good thermal shock resistance, high strength, resistance to acid and salt corrosion, especially weak acid has good resistance, without wetting of the metal and slag, light. It is widely used as lining material of high temperature, and also used as lining of autoclave in petroleum and chemical industry.
Q: Why is the three oxidation of two silicon is very harmful impurities in silica brick
Heating calcination is the best way to extend this sort of impurity removal. Remove impurities
Q: How to improve the thermal conductivity of the coke silicabrick rate?
To improve the thermal conductivity of silica brick for coke oven rate method:Manufacture of high density and high thermal conductivity of silica brick, adding additives such as CuO, Cu2O, TiO2, Fe2O3, (FeO), can improve the thermal conductivity of silica brick.
Q: Why is the highest brick coke oven temperature measuring point temperature not exceeding 1450
That is because the brick load softening point the maximum temperature is 1450 degrees.
Q: The difference between clay refractory bricks and refractory brick in the application.
Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.
Q: High temperature refractory material?
Many kinds of refractory materials, usually by refractoriness level is divided into ordinary refractory materials (1580 to 1770 DEG C), advanced refractories (1770 to 2000 DEG C) and special refractories (more than 2000 DEG C); according to the chemical characteristics into acid refractory material, refractory materials and basic refractory materials. In addition, the refractory material used for special occasions.Now the definition of refractory materials, has not only depends on whether the refractoriness at 1580 DEG. Refers to the current refractories used in metallurgy, petrochemical, cement, ceramics and other production equipment with inorganic non-metallic materials.