$Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China System 1$
$Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China System 2$

$Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China$

$Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China System 1$

$Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China System 2$

Raw Materials for Refractory:Insulation Rotary Kiln Bauxite for Castable Aggregate in China

Ref Price:

Loading Port:: China main port

Payment Terms:: TT OR LC

Min Order Qty:: 25 m.t.

Supply Capability:: 2000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Quick Details

Place of Origin:	Hebei, China (Mainland)	Shape:	Powder, powder	Material:	bauxite
SiO2 Content (%):	7-14%	Al2O3 Content (%):	80-87%	MgO Content (%):	0.3%
CaO Content (%):	0.3%	Refractoriness (Degree):	1770°< Refractoriness< 2000°	CrO Content (%):	3%
SiC Content (%):	2.4%	Model Number:	CNBM	Brand Name:	Banyue
color:	white,khaki	Dimensions:	120mesh,200mesh,325mesh	Application:	refractory product
Chemical Composition:	Al2O3, CaO, Fe2O3

Packaging & Delivery

Packaging Details:	50kg/bag, or according to customer requirements customized.
Delivery Detail:	10 days

Product Description

Content	1	2	3	4
Al2O3	80%min	85%min	86%min	87%min
SiO2	14%max	9%max	8.5%max	7%max
Fe2O3	2.5%max	2.0%max	2.0%max	2.0%max
TiO2	4.0%max	4.0%max	4.0%max	4.0%max
CaO+MgO	0.6%max	0.6%max	0.6%max
K2O+Na2O	0.3%max	0.3%max	0.4%max	0.6%max
B. D.	2.6g/ccm min.	3.10g/ccm min.	3.10g/ccm min.	3.0-3.10g/ccm
H2O				0.5%max
Refractoriness	1770° < Refractoriness< 2000°
NO.	Size		Size Distribution
1	0-1mm		0-0.5mm 60%max
2	1-3mm		90% min
3	3-5mm		90% min

$refractory insulation rotary kiln bauxite for castable aggregate in China$

Our Service:

1. Your inquiry related to our products or prices will be replied in 24hours.

2. Manufacturer with large capacity, ensure the fast production cycle after confirmed the order.

3. Our professional technicians will answer your entire enquiry in patient.

4. To meet the refractory solutions, we can serve as your instructions.

5. Protection of sales area and private information for our entire customer.

If you’ve kind enquiries, please don’t hesitate to let us know. ^_^

Q:which kind of fire?bulkhead is better?: Fire bulkhead also known as non-combustible fire retardance board, and it's made by various incombustible?material after the scientific pressing, and has good flame resisting properties, it's non-combustible time can reach over 3 hours, high mechanical strength,it has characteristics of non-explosive, water and oil resistance, good chemical corrosion resistance and non-toxic. As for the combustion test of YD-Ba-type inorganic fire?bulkhead, it's best to be deformation under the flame temperature of 1000 ℃, the indicators comply requirements of GA161-1997, combustion performance reaches A level standards of GB8624(non-flammable). J fire bulkhead is mainly applicable to the fireproofing protection and fireproofing isolation of cables with all kinds of voltage?classes laid on scaffold or bridge. It's widely used in cable project fireproofing and fire?retardant in the places with crowded cables, such as various power plants, chemical companys, iron and steel smelting enterprises, mines,etc. It's also the best fireproofing and fire?retardant materials of fireproofing and fire?retardant projects in indoor decoration of public places, such as large shopping malls, hotels, guesthouses, sports hall, closed clothing market, light industrial markets, theaters and so on. Construction method: Fire?bulkhead products can be cut by saw, according to the shape required to be made in the construction site, using steel brackets or expaned anchor bolt to fix it while assembling, steel brackets should be coated with fire-resistant coating for steel structure. You can also use various cable and fireproofing trays made of fire bulkhead, and used in the board gaps.

Q:Who knows the roofing fireproofing and waterproof material?: Many waterproof materials are suitable for civil engineering, and almost used in the roof waterproof layer, such as: Paint categories: 911 two-component polyurethane waterproof coating single component polyurethane waterproof coating polymer cement-based waterproof coating JS composite waterproof coating and so on. . Coil categories: single-sided waterproof roll double-sided self-adhesive waterproof roll modified asphalt waterproof roll (SBS, APP) polypropylene, polyester, polymer waterproof roll, PVC waterproof roll, EPDM waterproof roll

Q:Who knows the refractoriness of high temperature lightweight firebricks?: pores of high temperature lightweight refractory bricks is made by lightweight aggregate such as combustibles, foaming?agent, and hollow?sphere production with better thermodynamic stability. Refractoriness reaching 1200 ℃ or more is first grade refractories. fire resistance of building blocks of 100mm thick can reach 225 minutes, 200mm thick brick 480 minutes.

Q:What's the frequently used refractory material?: Refractory material is generally used in industrial departments like metallurgy, glass, cement, ceramics, machinery, hot working, petrochemical industry, power and national defense. Frequently used common refractory: silica?brick, semi-silica brick, clay brick, high alumina brick, magnesia brick, etc. Frequently used special refractory: AZS brick, corundum brick, direct-bonded?magnesia-chrome?bricks, carborundum brick, calcium oxide, chromium hemitrioxide, alumina, magnesium oxide, etc. Frequently used fireclay insulating refractory: diatomite product, asbestos product, insulation?board, etc. Frequently used unshaped refractory: ramming refractory, refractory castable, plastic refractory, refractory mortar, gun-mix refractory, refractory coating, lightweight refractory?castables, etc.

Q:Which one is better, fire-resistant wood or steel?: Rebar would weaken and quickly collapse in the fire, and the fire resistance of a heavy log is much better than steel. In many ways, the fire resistance of a large log is equal to reinforced concrete. The heat transfer capacity of wood is 400 times smaller than steel, 8.5 times smaller than concrete. When burning, wood will form a layer of carbon in the surface, and as long as the cross-section of the timber is over a certain size, this layer of carbon it will become an excellent flame retardant layer to protect the interior of the wood from burning. So the United States and Japan and other European countries allow and encourage the use of wood structure with a large section (beam column of 8 inches or more) to construct public buildings without the need for fire treatment applied to wood surface. I hope my answer will be helpful to you.

Q:What are the fire resistances of grc partition panels?: A-level fireproofing which can last for 4 hours.

Q:Who knows how many fire heat preservation material are there?: There are many kinds of fire proof materials. The major material used in construction industry is fire proof and thermal insulation material, mainly include vitrified micro bead insulation board, class A expanded bead fiber board, rock wool board, plastic extruded sheet, polyurethane insulation board

Q:What are included in wall fireproofing material?: Wall fireproofing materials include dry wall and gypsum block. Dry wall is made into board material through process by using building plaster as main material, adding an appropriate amount of additive and fiber to make board core and using tailor-made board paper as protection surface. Dry wall ia characterized by light weight, sound insulation, heat insulation, strong processing performance and easy construction method. Gupsum block is lightweight building plaster product made by using building plaster as main raw material, adding water, stirring, moulding by casting and drying. Fiber reinforced material or lightweight?aggregate are allowed to add during the production and foaming?agent can also be added. It is soundproof, fireproof, convenient to construct and many other advantages. It is a kind of new wall material with low carbon, environmental protection, health and in line with the development requirements of the times.

Q:What are the commonly used admixture for alumina-magnesia refractory? What are the impacts on its performance?: 2, form Mg-SiO2 coagulation and combination, CA cement bond? Bricks can generally be made by combing with phenolic resin, castable use 1, combined with silicon powder; 3, can also combined with brine MgCl is binding agent

Q:How to distinguish the fire resistant level of the rubber and plastic thermal insulation material?: Fire?rating grading of external wall thermal insulation materials. 1, China's national standard GB8624-97 divides the combustion performance of building materials external insulation materials into the following grades. Level A: Incombustible materials: Almost no burning materials. Level B1: Incombustible materials: Flame-like material has good fire-retardant effect. In case of fire in the air or at high temperature, it is difficult to fire and doesn't spread quickly, and when the fire source is removed after combustion, it stops immediately. Level B2: Incombustible materials: Combustible materials have a certain flame resistance. In case of fire in the air or at high temperature, it will immediately burst into flames, and easily leads to the spread of fire, such as poles, wooden frame, wooden beams and wooden stairs,ect. Level B3 : Incombustible materials: No flame-retardant effect, hidhly flammable and high fire risk. 2, The external wall thermal insulation materials could be divided according to the fire?rating. 1) thermal insulation material that has the level A combustion performance: Spraying inorganic fiber, glass wool, foam glass, ceramic foam, rock wool, foam cement and perlite obturator, and so on. 2), The thermal insulation material that has level B1 combustion performance: Special processed extruded polystyrene board (XPS) / special processed polyurethane (PU), phenolic and polystyrene powder. 3), Thermal insulation materials that have level B2 combustion performance: Molded polystyrene board (EPS), extruded polystyrene board (XPS), polyurethane (PU), polyethylene (PE), etc.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range