Raw Materials for Refractory:Calcined Bauxite 75-90 Grade Size 1-3mm

Ref Price:

Loading Port:: China main port

Payment Terms:: TT OR LC

Min Order Qty:: 25 m.t.

Supply Capability:: 10000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Quick Details

Place of Origin:	Shanxi, China (Mainland)	Shape:	Block	Material:	Alumina Block
SiO2 Content (%):	<8%	Al2O3 Content (%):	75%-90%	MgO Content (%):	<0.5
CaO Content (%):	<0.5	Refractoriness (Degree):	1770°< Refractoriness< 2000°	CrO Content (%):	0.0
SiC Content (%):	0.0	Model Number:	75,80,85,86,87,88,90	Brand Name:	CNBM
Fe2O3:	3.0 max	K2O+NA2O:	0.3 max	TIO2:	0.4 max
CaO+MgO:	≤0.5	shapes:	granula and powder	bulk density:	≥2.70
H.S.code:	2508300	Moisture:	0.03% max	color:	yellow,black and white granula and powder
application:	abrasive ,cement ,chemical, metallurgical, and refractory and so on

Packaging & Delivery

Packaging Details:	25kg/Bag,1Mt/Bag,1.25Mt/Bag; Or as per Client's request
Delivery Detail:	7-15 days upon receipt of prepayment by TT or L/C

Specifications

Calcined bauxite:
14 years producing experience;
self-owned mines;
SGS or BV report.

Calcined bauxite specification:

Grade	AL2O3	FE2O3	TIO2	K2O+Na2O	CaO+MgO	Bulk density
75	75min	≤3.0	≤4.0	≤0.3	≤0.5	≥2.70
80	80min	≤3.0	≤4.0	≤0.3	≤0.5	≥2.80
85	85min	≤2	≤4.0	≤0.3	≤0.5	≥3.00
86	86min	≤2	≤4.0	≤0.3	≤0.5	≥3.10
87	87min	≤2	≤4.0	≤0.3	≤0.5	≥3.20
88	88min	≤1.8	≤4.0	≤0.25	≤0.5	≥3.25
90	90min	≤1.8	≤4.0	≤0.25	≤0.5

Size: as buyer’request

Packing: usually we packing in big bag, 1.25mt/bag; we could pack as buyer’request

Calcined bauxite is one of the principal ore of aluminum. Calcined bauxite contains hydrous aluminum oxides and aluminum hydroxides, formed through the laterization of aluminous rocks in tropical and subtropical areas .calcined bauxite is obtained by calcining (heating)superior grade bauxite at high temperature (from 85OC to 1600C) .this removes moisture thereby increasing the alumina content. compared to an alumina content of about 57%to 58%in raw bauxite, calcined bauxite has an alumina content of 84%to88%.the heating is carried out in rotary kilns.

Applications

calcined bauxite is typically calssified according to its intended commercial application,such as abrasive ,cement ,chemical, metallurgical, and refractory .as raw material for use in high alumina and super duty refratory bricks and shapes ,plastics ,castable refratory, motors, gun mixes, ramming mixes, abrasive grains and other products.

$refractory grade size 1-3mm calcined bauxite 75,80,85,86,87,88,90$

Q:what's the seal of fireproofing material?: Organic fire-proof caulking is made by taking organic synthetic?resin as bond and compressing the components together after adding fireproofing agent, filler. The putty won't solidify after a long time usage and has good plasticity, can be sealed arbitrarily. This kind of putty is mainly applied in opening's fireproofing and sealing project of construction pipe and electric wire and cable, and it's used with ATD-AB and fire retardant bag together. ATD-AB is a kind of gray powder material, after mixed with water, it can be used for the opening sealing of electric wire and cable or fire resisting wall of wire tunnel. The fire proof blockage is non-toxic, and no smell, has good water resistance and oil resistance with simple construction methods. It's oxygen index is 100 and it belongs to incombustible?material. it's refractory time can reach 3 hours, or above or below. as for some projects for perpetual usage, WXY-II will save the project fee and make the project solid. A kind of fireproofing material that can automatically expand and foam and sealed by opening after injecting the foam into opening. Sealing strip is a product or flexibility coiled material mede by fireproofing material with certain geometry shape. Sealing gum is a kind of liquid fireproofing material that has a function of fireproofing and sealing. Fire retardant bag is soft and windable tape-shaped product made by fireproofing material, it is winded on the external surface of plastic pipe and fixed with steel belt or other proper methods, it's the expansion, squeezing and softening pipe after contacting with fire, opening left by burning or soften of seal plastic pipe. Fire retardant ring

Q:What is refractory aggregate?: It includes two categories: coarse aggregate and fine aggregate.

Q:Is it normal for caable fire resistant material to catch on fire?: Abnormal, preventive measures: 1 take fire preventive measures. Measures taken for fire retardant measures of cable: (1) seal closely with fire resistant materials holes ran by cables through walls, shafts to prevent the cable fire, high temperature gas diffusion and spread when cables are on fire. (2) to wrap the cable with the insulation refractory material, when the cable is surrounded with fire, warpped cable is insulated by the insulation material from fire, so it will not be burned. If the cable itself is on fire, fire will be extinguished thankes to lack of oxygen in warpped cable, to avoid the fire to spread out. 2 to strengthen the cable circuit switch and regular protective check and maintenance, to ensure that the action is reliable. 3 to strengthen the cable operation and monitoring, to avoid the overload of the cable operation. . 4 regularly clean dust on the cable, to prevent cable from catching on fire due to the accumulation of dust. 5 to ensure the construction quality, the quality the cable must be strictly in line with the requirements and standards. 6 cable laying should maintain enough distance form the heat pipe, control cable is no longer than 0.5 meters; power cable is no longer than l meters. Control cable and power cable should be divided into slots, be layered and seperated instead of being overlapped . For the parts that do not meet the requirements, measures must be taken to insulate heat and fire. 7 regularly teat cable , abnormal problem should be handled in a timely manner. 8 install fire alarm so that fire will be discovered on time, and cables will not catch on fire. 9 the cable trench should be kept dry to prevent the cable from being affected with damp, or leading to declined insulating function and short circuit.

Q:What is the quote of fireproof and soundproof materials used in KTV?: acoustic material, aluminum foil glass wool, sound-deadening material, glass wool, cinema / KTV dedicated glass wool: The classification of glass fiber products: The category of glass wool felts: The level of insulation cotton: A-level brands: New applications: The origin of GB/T13350-2008: The coefficient of thermal conductivity(room temperature): 0.035 bending at low temperature≤： 0.02 elongation at break: ≤80kPa flexure strength： ≤120kpa Compressive strength: ≤150kpa application temperature: 700 Core material: The shape of glass wool: Fibrous shape: Coil Specifications: Complete quote is 23 Yuan per cubic meter. glass wool board, KTV sound insulation core material: The shape of glass wool: The level of rectangular glass wool: A-level non-combustible brands: Kunnai material: The origin of glass fiber: Guangzhou, Shijiazhuang, Wuhan, the quote there is 8.8 Yuan per cubic meter.

Q:What are the types of steel refractory materials: Large steel ladle usually made with magnesia carbon brick, of course, it contains a intermediate layer (such as good a little high alumina castable), heat insulation layer and heat preservative materials Alumina-magnesia castable is OK for small steel ladle

Q:What are the best refractory materials in 2,400 Celsius degree?: and carbon fiber or nanomaterials.

Q:What does refractory mean?: What is refractory material?Refractory material generally refers to the inorganic refractory degree over 1580oC non metallic materials. It includes natural ore and various products in accordance with certain requirements after a certain process. With the volume stability of high temperature mechanical properties, a good, is the necessary equipment for all kinds of high temperature materials.

Q:What are the specific steps of stirring the steel ladle castable?: Steps are as follows. 1 Compulsory mixer is used to stir the castable and bags, rope and other debris can not mix in the castable when stirred. 2, Castable should be unpacked on the scene. Stirred volume depends on the capacity of the mixer. Castable should be accurately measured and put into a blender. 3 The process of first dry mixing and then wet mixing is adopted. After the castable is added to the mixer, it is dryly mixed for 2 minutes, add about 5.2 to 5.5 percent of water and continue to add water while stirring. Water that is 80% of the total should be added, and then decide whether to continue to add or not depending on the consistence (noting that the water must be clean water and sewage can not be used). Then it is wetly mixed for 4 minutes and stirred for not less than 6 minutes at one time, until castable is even. In general, the bottom is slightly dry and the wall of the ladle is slightly dilute (the amount of water is only for reference). 4, The amount of water and mixing time should be controlled strictly when stirred to ensure that the needs of the consistency are met. If castable is too thin, it will seriously affect the quality of the material. The stirred volume, stirring time and water that is added should be consistent and they can not suddenly be thick or suddenly be thin. If the consistency does not meet the requirements, the castable should be put back to the mixer and stirred with appropriate water or dry materials. 5, It should be stirred evenly and casting should finish in 20 minutes, in order to avoid sclerosis, affecting structural strength of ladle lining 6, After each completion of construction, varieties of castable should be changed and the mixer should be cleaned 7, Stirring can stop in halfway. If the mixer breaks down and it can be repaired in a short time, some of the materials have to be removed before the machine is opened. If the machine can be repaired on time, castable refractory should all be removed.

Q:How to make use of waste refractory materials whose main elements are alumina and mullite?: Crushing and pressing refractory bricks, or refractory parts . Such as welding positioner tracks use disposable tools.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range