High Alumina Bricks for Cement Kiln - High Alumina Brick

High Alumina Bricks for Cement Kiln - High Alumina Brick System 1

High Alumina Bricks for Cement Kiln - High Alumina Brick System 2

High Alumina Bricks for Cement Kiln - High Alumina Brick

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 2 m.t

Supply Capability:: 5000 m.t/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

High Alumina Brick ALP80

High Alumina Brick UAL65 - High Alumina Brick

$High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)$

High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)

High Alumina Brick Rectangular Cordierite Pizza Oven for Pizza Cooking

$High Alumina Brick - Refractory Bricks for Pizza Oven$

High Alumina Brick - Refractory Bricks for Pizza Oven

High Alumina Brick for Induction Furnace

$High Alumina Brick - Good Quality Refractory Bricks$

High Alumina Brick - Good Quality Refractory Bricks

$High Alumina Brick for High Temperature Refractory$

High Alumina Brick for High Temperature Refractory

Brief discription for High Alumina Bricks for cement kiln

CMAX High Alumina Bricks for cement kiln are classified according to alumina content ranging from 48% to 90%.

CMAX High Alumina Bricks for cement kiln are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotarykiln,regenerator, etc.

Brief features for High Alumina Bricks for cement kiln

◆Low thermal conductivity

◆Excellent acid and base slagging resistance

◆High refractoriness

◆Excellent thermal shock resistance

◆Excellent mechanical strength

◆Good spalling resistance and wear resistance.

◆Good corrosion resistance.

◆High-temperature creep rate is quite low.

◆Good volume stability at high temperature.

◆Low bulk density, low thermal conductivity, good thermal insulation performance.

Technical data for High Alumina Bricks for cement kiln

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

FAQ

Q1:Are you a manufacture or trader?

A:Factory+trade(mainly factories,at the same time,we operates other related products).

Q2:Can we visit your factory?

A:Sure,welcome at any time,seeing is believing.

Q3:What's the MOQ of trial order?

A:No limit,We can offer the best suggestions and solutions according to your condition.

Q4:Which payment terms can you accept?

A:T/T,L/C are available for us.

Q5:After an order is confirmed,when to deliver?

A:15-25days after deposit.

Q6:Is your company accept customization?

A:We have own factory and excellent technical team,and we accept OEM service.

Q: Is there a big difference between two high alumina brick and one high alumina brick?: The difference between the two kinds of high alumina bricks is great. I perennial in Zhengzhou was responsible for the production and sale of colt refractories

Q: What are the high aluminum bricks made of?: We specialize in the production of various LeiBao refractory refractory material, such as corundum, zirconia products, alumina hollow ball products, mullite products and so on.

Q: What are the characteristics of high alumina bricks?: A neutral refractory with an alumina content of more than 48%. Made from alumina or other raw materials of high alumina content; formed and calcined.

Q: What is spalling resistant high alumina brick?: Spalling resistant high alumina brick is a kind of high alumina brick. Antistripping high alumina brick with high grade bauxite and containing Zr02 synthesis as raw material, according to a certain proportion by high pressure molding system in sintering products, products with anti stripping ability, and have the anti erosion potassium, sodium, sulfur, chlorine and alkali salt, low thermal conductivity and other properties that is the transition zone of cement kiln and decomposition of ideal material with remarkable characteristics, the product is good thermal shock resistance, strong ability to adapt to the environment. It is used in the preheating or decomposing furnace, grate cooler and so on.

Q: The difference between light high alumina brick and heavy aluminum brick: Lightweight high alumina brick, also called high alumina insulation brick. Alumina content of 48% or more, mainly from mullite and glass phase or corundum composition of lightweight refractory. Volume density 0.4 - 1.35g/cm3. Porosity 66% - 73%, compressive strength 1 - 8MPa. Better thermal shock resistance. Usually, a high alumina clinker is added with a small amount of clay. After grinding, it is poured and shaped in the form of slurry by gas generation or foam method, and it is fired at 1300 - 1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.

Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: The super high alumina brick in high alumina refractory brick has the highest refractoriness, and the corresponding production cost is higher.

Q: How high can aluminum bricks expand at 80O degrees of heat?: When an object is heated, the particle moves faster and thus occupies additional space. This phenomenon is called dilation.

Q: How does the physicochemical index change when the high alumina brick is used at high temperature?: If the range of softening temperature exceeds the load, the constants of other physical and chemical indexes will also increase or decrease.

Q: What are the lining structures of lime rotary kilns and what are the requirements for refractories?: The current configuration of domestic calcining active lime rotary kiln refractories are as follows: the discharge end of low cement high alumina castable with 3% steel fiber; the cooling zone and the firing zone: dry magnesia spinel brick with high aluminum brick with high temperature; preheating: high alumina brick; low temperature preheating zone: clay brick light clay brick; feeding end: low cement high alumina castable with 3% steel fiber; in addition, brick size also have the corresponding requirements; dimensional tolerances: dimensional tolerances used in different parts of the requirements are not the same, the general control in 2mm; corner damage: general permit edge damage 40mm and 5mm deep within angle loss in the hot and cold surface is allowed to have only one, three edges and the length of not more than 50mm; there are cracks parallel to the use of surface crack is not allowed, cracks of brick surface are allowed.

Q: What are the categories of bricks?: Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels.

Send your message to us

*Email

*TEL

*Quantity

*Unit