Dense fused alumina ,compact fused alumina for refractory
1, High purity:99% min
2,Excellent performace

Dense fused alumina ,compact fused alumina for refractory

Description:

Dense corundum, with a-AL2O3, as main principle crystalline phase, gray, is characterized by high melting point,high bulk density, low apparent porosity,excellent wear resistance,slag resistance, steady volume and thermal shock resistance. It is an excellent refractory material in corundum series.

Advantages:

1) we are more specialized in the procuction.

2) we can offer more competitive price

3) we can produce as per customer's requirement

Chemical and physical analysis

CHEMICAL COMPOSITION	GRIT >0.1mm	TYPICAL VALUE	FINE POWDER ≤0.11mm	TYPICAL VALUE
AL2O3%≥	99	99.2	98.6	99.0
SiO2%≤	1.0	0.4	1.0	0.45
Fe2O3%≤	0.15	0.1	0.3	0.2
TiO2%≤	0.1	0.05	0.1	0.05
CaO%≤	0.1	0.05	0.1	0.05
MgO%≤	0.1	0.05	0.1	0.05
NaO2%≤	0.1	0.05	0.1	0.08
C%≤	0.1	0.08	0.12	0.1
Apparent Porosity%≤	2.0	0.8	2	0.8
Bulk density (g/cm³)%≥	3.90	3.93	/	/
True density (g/cm³)%≥	3.96	3.99	3.96	3.98

Packaging & Shipping

25kgs/bag 1MT /bag as per customer's requirement.

Our Services

1.We will keep the client informed about the cargo situation,from production time to the shipment.

2.We test samples picked up from the plant or loading port in our designated third party sample before every shipment to make sure each lot quality is good for our client.

3. we are reliable, Hope that friendly cooperation.

FACTORY:

$Dense Fused Alumina For Refractory$

Q: what's the application of fireproofing abs materials?: a kind of ABS alloy shell, a toy of child, low load bearing, refrigerator lining, it can be processed into various wear-resisting sheets, plates,and has good electrical performance, it can be used as electronic components or auto parts, all kinds of insulation materials, it's easy to machining on the surface, so it can be made into designated special products (such as electroplate), and easy coloring, it can be processed into colorful products, also can be used as a fireproofing electrical appliance outer covering, adding alloy to it will improve its comprehensive performance, etc

Q: What are some of the new refractories and what are their characteristics?: Refractory common AZS refractories are often used brick, corundum brick, magnesia chrome brick, silicon carbide, silicon nitride bonded silicon carbide, nitrides, silicides, sulfide, boride, carbide and other non oxide refractory materials; calcium oxide, chromium oxide, aluminum oxide, beryllium oxide and other refractory materials, Magnesium Oxide

Q: How about the prospect of refractory material?: is developing well. Many plants are required t o use fireproofing materials.

Q: What are included in wall fireproofing material?: External wall thermal insulation materials are divided into A and B according to combustion level. Grade A is incombustible material, while grade B is combustible material. A few years ago, fires in CCTV building and Shenyang hotel resulted from grade B material. Currently grade A is usually used, and some are even cheaper than the grade B material. Grade A is roughly divided into insulation mortar, phenolic board, rock wool board, foam cement board, etc. Insulation mortar is quite good. It is easy and convenient to construct, has low cost, but the production is too simple and it is easy to fake.

Q: What are the applications of refractory in petroleum?: It can be used in transportation of natural gas, filler of chemical equipment, security, insulation or even building materials.

Q: What are the standards of refractory concrete ?: General requirements (1) All the materials for compounding refractory concrete must meet the design requirements and they should be checked according to the relevant standard. (2) The compounding of refractory concrete should be done strictly in accordance with the compounding proportion (usually weight), and the using of various binders, aggregates, coagulant, and water should be accurately measured. Tolerance of difference of cement, powder and water should be not more than 1 %; weight of aggregates does not exceed 3%. (3) The mix of different varieties of concrete must be prevented. (4) A variety of raw materials should be piled separately according to different species, mark numbers, dates of manufacture. Do not mix with limestone, silica, railroad ballast, dirt and other harmful debris.

Q: What are the technical requirements for refractories?: To put it simply, physical indicators are pores, volume density, pressure resistance, slag resistance, thermal shock resistance, foot expansion coefficient, thermal conductivity, oxidation resistance and so on. If it is castable, the indicators are mobility, water rate, setting time, and anti bending strength. If it is coating mix, the bonding strength should be checked. Chemical indicators are loss of ignition and the content of aluminum, magnesium, silicon, calcium, chromium, titanium and carbon.

Q: Fire resistance and evaluation of refractory for casting: The products to be tested are broken and ground, adding organic binders (usually dextrin) that do not affect the refractoriness. Water is used to make standard sized test cones, as shown in figure 1-2-1. Test cone is positive, three edge cone, the bottom side length of 8.5mm, the top side length is 2mm.Test, the equivalent of high standard cone refractoriness of the 2 products to be high, No. 1 and No. 1 high temperature low standard cone of each one, and the 2 to be tested in accordance with regulations frustum cone plug made of high aluminum material, a cone prism and vertical 8 degrees. 1 degrees tilt angle. Then, the cone is heated in a high temperature furnace. When the test cone with a high temperature and bending down to the standard cone top contact cone, the high standard cone refractoriness refractoriness is running.

Q: On the problem of making refractory materials: Refractories mainly depend on their high melting point characteristics. The refractory market is mainly Magnesium Oxide material.