Silica Brick S94 for Coke Oven

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 100000 pc/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Insulating Fire Brick - GJM23

Silica Brick S94 for Hot Blast Stove

Silica Brick for Refining Furnace

Silica Silicate Mullite Bricks for Industrial Furnace

$Zero Thermal Expansion Refractory Silica Bricks$

Zero Thermal Expansion Refractory Silica Bricks

Zircon Brick - China Fire Resistant Brick Manufacturer for Zircon Glass Kiln

$Silica Brick for Steel and Metallurgy - Aluminum Silica Refractory Brick$

Silica Brick for Steel and Metallurgy - Aluminum Silica Refractory Brick

Silica Brick with Superior Thermal Shock Resistance

General Information of SilicaBrick For Coke Oven

Our corporation produces a comprehensive range of silicabricks, with high silica content, all of these bricks exhibit excellentperformance.

Our Silica bricks are the final result of blendingexcellent tridymite and cristobalite, as the main raw materials withcutting-edge technology, after mixing, drying, forming, in the high temperatureshuttle kiln. There are also little quartz and vitreous within. We ensure youthat the silica bricks made by us possess high quality standard and have gonethrough all the complicated quality control parameters. Their durability andstrength adds life to the structure and they have the capacity of bearing hightemperature.

Feature of Silica Brick For Coke Oven

Resistant to thermal shock, abrasion, chemical attack

High ability for anti-abrasion during work

Superior resistance to acids (including oxidizing)

Resistance to chlorine

Resistance to thermal shock and pressure changes

Low thermal and chemical expansion

Applications of Silica Brick Coke Oven

Silica brick for Coke Oven ismainly used in Coke Oven.‍

Silica Brick For Coke Oven---S94
Physical Properties:
Permanent Linear Change(1450℃×2h)%	%	±0.5
Apparent Porosity, %	%	≤24
Cold Crushing Strength	Mpa	30
Refractoriness Under Load (T0.6)	℃	≥1630
Thermal Expansion	%	≤1.3
Density	g/cm³	-
Chemical Analysis:
SiO₂	%	≥95
Fe₂O₃	%	≤1.5
Al₂O₃	%	≤0.8
Residual Quartz	%	≤1
Note: Technical Data are typical average results from test pieces. The technical data is offered solely for your consideration. And we reserve the right to modify the technical data without any prior notice. Users of our products should make their own tests to determine the suitability of each product for their particular purposes.

Q: Physical solid waste disposal: Reduce crack production and improve yield. The amount of addition is related to the shape and weight of the brick. The bricks can be added to 20% weight less than 25kg; bricks above 25kg can be added to 30%; for the specific type of brick can be added 30%. into waste silica brick should pay attention to this problem

Q: The hot blast stove when the temperature did not rise against the brick interface decreased: How to keep the brick masonry temperature not lower than 600 DEG C, while the exhaust temperature is not higher than 400 DEG C.

Q: The specific content is what gb/t2608-2012 brick: The provisions of the brick classification, technical requirements, test methods,

Q: What is the main material of silica brickIt's common, the kind we see so often!: More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance.

Q: How much is the highest melting point of silicon?: Mainly used for partition, carbonization chamber of coke oven and combustion chamber open hearth furnace regenerator and a sediment chamber, soaking furnace, glass melting furnace refractories and ceramic kiln, kiln vault and other load-bearing parts. Also used for high temperature bearing part of hot blast stove and acid open hearth furnace

Q: Semisilica brick, clay brick, high alumina brick and what is the difference?: The share of A12O3 and SiO2 is different

Q: Can not use it two brick: The softening temperature is up to 1640~1670 DEG C, and the volume is stable at high temperature for a long time.

Q: What are the main constituents of refractory bricks?: (a) containing refractory brick brick, refers to more than SiO293%, is the main varieties of acid resistant brick. It is mainly used for coke oven building, also used in furnaces all kinds of glass, ceramic and carbon calciner, refractory brick arches and other load-bearing parts, is also used in high temperature bearing part of hot blast stove, but should not be used in thermal equipment below 600 DEG C and the temperature fluctuation in the.

Q: The difference between clay refractory bricks and refractory brick in the application.: Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use, but the anti alkali erosion ability, thermal shock stability is the worst, a scrap. The brick is generally used in the coke oven, glass kiln. Other industries basically do not use.

Q: Such purpose and scope please give me detailed points thank you: Mainly used for coke oven carbonization chamber and the combustion chamber wall, open hearth furnace regenerator and a sediment chamber, soaking furnace, glass furnace, refractory materials and ceramic brick kiln, kiln vault and other load-bearing parts. Also used for high temperature bearing part of hot blast stove and acid open hearth furnace.

Send your message to us

*Email

*TEL

*Quantity

*Unit