Q:What refractories have good mechanical property resistance and heat expansion and cold contraction property?

Explain that where you use it for and what requirements you have. Follow-up: I use it in metallurgical furnaces with the features of strong stirring and acidic residue.

Q:What kind of refractories do the anode baking furnace use?

Use refractory bricks.

Q:Who can tell me what is neutral refractory?

It is a material that can resist acidic and basic slag, flux and chemical erosion form other refractories at high temperatures. The main components include carbon, silicon carbide, aluminum oxide, chromium oxide and other trivalent oxides, such as carbon refractories and chrome refractories, etc. Strictly speaking, neutral refractories refer only to the carbonaceous refractories, including carbon brick and graphite silicon carbide products, etc. Sometimes, high alumina refractories with high Al2O3 content also belong to this material, such as some materials that are acidic but tend to be basic refractories, like sillimanite, mullite bricks and corundum bricks. Recently developed aluminum carbon bricks, zirconium carbon bricks alumina - silicon carbide - carbon bricks, silicon nitride bonded silicon carbide brick and so on are also neutral refractories. This material can be used in the bottom of blast furnace, the lining of hearth and bosh, and the lining of aluminum electrolytic cell, calcium carbide furnace, ferroalloy furnace, molten steel ladle, plating tank, reaction tank, and autoclave and so on.

Q:Concrete composition and function of magnesia bond used in refractory

According to the chemical composition and use can be divided into metallurgical magnesia, magnesia brick, magnesia brick, magnesia brick, magnesia calcium brick, magnesia brick and other varieties. Its performance is greatly affected by CaO/SiO2 ratio and impurities. High purity magnesia brick refractoriness under load and thermal shock resistance are better than the general magnesia brick. High refractoriness, has good resistance to alkaline slag and iron slag, is a kind of important senior refractories. Use of magnesia product production by sintering process, sintering temperature is 1500 ~ 1800 DEG C, in addition, you can also add chemical bond, made of brick and unshaped refractory material. Mainly used in open hearth furnace, electric furnace, converter, oxidation non-ferrous metal smelting furnace, cement kiln and alkaline refractory kiln etc..

Q:What is the most reasonable drying heating curve of magnesia refractories? Products of less than 0.5T

The material is very troublesome, it might crack horrendously if not baked well and all of them may be scraps after being took out from the furnace. Magnesia hydration is inevitable during the baking process. As volume expansibility of magnesite reaches 200%, so it is easy to crack. The key to bake is to quickly rule out the water vapor in furnace, especially within 150 degrees Celsius. After quickly ruling out the water vapor in furnace to avoid excessive reaction with magnesia of 150 degrees, it can be operated in accordance with convention. In addition, you should pay attention to the heat sources, for which i recommend electrical and coke to avoid generating a lot of water vapor during the natural gas combustion process which will worsen the situation.

Q:What is the main constituent of refractory brick?

There are several refractory bricks, including clay brick, carborundum brick and chromium-carbon. The type you said may be refractory bricks made from bauxite.

Q:Why the corundum can be used as refractory

Do you need white corundum Its main chemical element of corundum is the 99.3% aluminium oxide and it is sintered byelectric furnace, so it can be used as a refractory raw material, the other can also be used as grinding wheel. It is very useful

Q:Who knows about the fire endurance of sintered shaly hollow bricks?

1. after roasting at high temperature of more than 1200 degrees, shale burned bricks in construction works can be free from expanding with heat and contracting with cold. 2. masonry walls can be plastered with no needs of any anti-cracking, reinforcement measures, and walls will not bulge and crack, which can reduce the construction cost, as well as are preferred building materials of frame structural engineering. 3.They have good sound insulation and thermal insulation performances, are one of the green building materials that the state currently promotes. 4. They have high intensity. The average compressive strength of them is up to 15.8, which matches with M7.5 cement mortar that has advantages of low water absorption, and good anti efflorescence performance.

Q:what is the requirements of roofing insulation materials fire rating?

The fireproofing requirements of architectural design are regulated by architectural design fire?safety?rules, roofing insulation material only has the requirements of materials combustion performance, namely non-combustible material. No fire rating requirements.