$Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh System 1$
$Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh System 2$

$Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh$

$Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh System 1$

$Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh System 2$

Raw Materials for Refractory:Abrasive White Fused Alumina (WFA) for Sand Blasting 36 Mesh

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Packaging & Delivery

Packaging Detail:	25kg/plastic bag, 1mt/jumbo bag or as you require
Delivery Detail:	within 7 days after sign the contract or your deposit

Specifications

white fused alumina
Direct Manufacturer
lapping & polishing media
Ceramic grinding wheels

36 mesh abrasive white fused alumina (WFA) for sand blasting

White Fused Alumina/ WFA

White Fused Alumina, a kind of high-grade refractories, was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.

Advantages

Flexible price policy

Equipped full line of test method.

Brilliant produce&supply&delivery ability

We passed the certification of ISO9001:2000

White fused alumina has Al2O3 content 99% min

All products will be supplied according to customers different requirement.

The laboratory is certified by government Inspection Bureau, that assures its quality stability.

Technical Data:

Application	specification		major chemical content %
Application	specification		AL2O3	Na2O	SiO2	K2O	Fe2O3
abrasive	F	8#-60#	99.5min	0.26max	0.08max		0.06max
		60#-100#	99.5min	0.26max	0.09max		0.06max
		120#-150#	99.5min	0.26max	0.10max		0.06max
		180#-220#	99.5min	0.26max	0.12max		0.10max
		230#-800#	99.3min	0.32max	0.15max		0.10max
		1000#-3000#	99.1min	0.35max	0.18max		0.10max
refractory	Section sand	0-1mm	99.5min	0.29max	0.30max	0.02max	0.06max
		1-3mm
		3-5mm
		5-8mm
		10-20mm
		0.3-1mm
		0-0.3mm
		1-2mm
		0.5-1.5mm
	Fine powder	100#-0	99.0min	0.40max	0.30max	0.03max	0.20max

Moh's hardness	≥9.0
true density(g/cm3)	≥3.95
propotion	≥3.6
porosity	≤8.5

As refractoriness

White Fused Alumina is the main starting material to produce high-grade unshaped and shaped refractoriness and is widely used in the field of iron-steel industry,ceramics,petrochemical industry etc. It is the ideal material to produce the unshaped refractoriness such as large ladle castables,medium and high grade BF trough castables,gunning material,pre-cast shapes and is the main material to produce alumina products such as corundum bricks, corundum and mullite-corundum sagger,refined porous plug bricks, monolithic lance composite nozzle, lining material for high temperature industrial furnaces,etc.

As abrasives

White Fused Alumina can be used as consolidation & coating abrasives, wet or dry sprayed grit, suitable for ultra-precise grinding and polishing in the crystal and electronic industry and can be used to produce high-grade refractoriness. It is suitable to machine high stiffness &high tensile strength materials such as chilled steel, alloyed steel, high-speed steel, high carbon steel, etc. In addition, it can be used as catalyst, insulator, precise foundry sand, etc.

Size available:

Abrasive tool: F10-F220,F230-F1200;P12-P220;

Refractory : 0-1mm,1-3mm,3-5mm,5-10mm;100mesh,325mesh;

Other size is available as required;

Packing:

25kg/bag,40bags/big bag;

1000kg/big bag;

1000kg/big bag with pallet packing;

Other packing is allowed as required.

abrasive white fused alumina (WFA) for sand blasting 36 mesh

Q:What types does soft fire prevention materials have?: 1. In new fire retardant coatings, expanded vermiculite, expanded perlite heat insulation material and cenosphere adiabatic powder are an integral part of thick film type fire-retardant coating. They are also the main factors influencing the fire fire retardant coating performance level. And fireproof heat insulation performance of fire retardant coating is based largely on the back fire coating surface temperature factors, and also related to the fire resistance. If the time of reaching the same temperature is longer, it means its insulating fire stays is better, so the fire resistance is higher. 2. The new type of fire prevention board. Now new type of fire prevention board are welcomed by the people is mostly due to its environmentally friendly. And with an increasing number of high-rise building, the fire and strength requirements are constantly improved. It is a big test for plate performance and the standard. Now fire prevention board mainly adopts siliceous materials or calcareous materials, and then stick with the fiber material, light aggregate, binder and the mixture of chemical additives. In this way, it can not only act as fire prevention, but also can improve the thermal insulation performance, and with light quality, good bearing capacity, good durability, no aging problem. More importantly, it is environmental protection. 3. The new flame retardant materials. New flame retardant material currently focus on in polymer composite material, which performance is good with very good high temperature resistance and heat resistance, therefore it's not easy to deform after the fire. At high temperature, it also can use for a long time, so as to ensure the safety.

Q:What are the applications of refractory in petroleum?: It can be used in chemical filler.

Q:What is the the best ratio of mortar in refractory cement?: The ratio of refractory cement are: M10 the ratio of cement and mortar: cement: Sand= 346kg: 1631kg M7.5 ratio of cement and mortar: cement: Sand =274kg: 1631kg M5 The mix proportion of cement and mortar: cement: Sand = 209kg: 1631kg M10 mix proportion of composite mortar: cement: Sand: Lime =306kg: 1600kg: 29kg M7.5 mix proportion of composite mortar: cement: Sand: Lime =216kg: 1600kg: 64kg M5 The mix proportion of composite mortar: cement: Sand: Lime =205kg: 1600kg: 100kg

Q:What are the applications of refractory busway?: Fire-resistant busway has excellent insulation property, and it can not only be used continuously in a normal environment, but also be used continuously when catching fire for more than one hour. It can be used in high buildings and important facilities in replace of fire-resistant cables to transmit and distribute electricity.

Q:What kind of refractory materials are used in metallurgy industry?: Argon-blowing rod, siliceous dry vibrating materials, desulfurizer, slag-stopping ball, stainless steel thermal insulating agent with high efficiency, dry vibration material, sizing nozzle heat-insulating panel, chrome refractory , refractory carstables for ladles, magnesia carbon refractory, package castable, siliceous drainage agent, tundish block, iron trough, deoxidizer, compound deoxidizer,silicon manganese alloy , stemming, floating plug,slagging agent. The main materials are as follows: recarburizer, covering agent, intermediate frequency furnace burden, mould fluxes, insulation thin slag agent, skimmer repair material, joint sealant.

Q:What's the difference of fire-resistant material's density, specific gravity and bulk specific gravity?: It usually used to test lightweight refractory. Density can be divided into apparent density (usually called as density) and true density: apparent density includes blow hole inside the sample; Unit weight is using quality to divide volume of sample and specific weight is used to represent liquid.

Q:what's the classification of fireproof materials?: Fireproof materials are used in construction, in various forms and it has played an absolute role in modern fireproofing, common fireproofing materials include fireproof?panel, fire door, fireproofing glass, fire?retardant?coating, fireproof bag,etc Or the material itself has a high temperature resistance, heat-resistant, flame-retardant properties. Most of them are used for the construction industry.

Q:Are fire materials poisonous after burning?: High temperature oxide materials in refractory special applications, such as aluminum oxide, lanthanum oxide, beryllium oxide, calcium oxide, zirconium oxide, refractory compounds, such as carbides, nitrides, borides, silicides and sulfides; high temperature composite materials, including metal ceramics, high temperature inorganic coatings and fiber reinforced ceramics.

Q:How to count the construction costs of refractories?: In winter, the temperature of the the fire-resistant masonry, fire-resistant plastic, sodium silicate, phosphoric?acid castable should be maintained above 5 ℃. Usually greenhouses in which heating facilities are installed to maintain the appropriate temperaturere for the construction environment should be erected in refractory masonry. The temperature around the construction site of the industrial furnace and refractory masonry shall not be lower than 5 ℃.

Q:Is the linear change on reheating the same as heating permanent linear change of refractory material?: “+”represents expansion. the afterexpansion and aftercontraction after cooled to be at room temperature. The change may significantly damage the masonry of thermal kiln. There are regulations on the linear change on reheating of common refractory material in the national standard. Some physical chemical changes may continue. It is defined as the change from being heated to the specified temperature of refractory material sample. Heat preserving for a while till afte cooling to be at room temperature, then the residual will expand or contract in its length, heat preservation for a while, organization vitrification, the irreversible changes of its length refers to heating the firing refractory to be at high temperature, so as to make the volume of refractory materials expand or contract, due to the influence of uneven temperature or lack of time, otherwise it will cause the deformation of the refractory ball and make this indicator within standard even reach smaller value, so firing control must be strengthened in product production. But it is should not be too high. For refractory materials with same chemical composition, the linear change on reheating is produced in the heating process. Properly increasing sintering temperature and prolonging the holding time is an effective process measures, make its firing inadequate. When subjected to high temperature, it can reduce the thermal shock resistance. Minus sign "-" represents contraction. The permanent line rate refers to heating the fire refractory ball to the specified temperature. Linear change on reheating, also known as residual linear change, is an important indicator to assess the quality of refractory in the long time use. To control the permanent line rate within the standard or reach the minimum value.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range