M 40 80% Metallurgical Coke

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 100 m.t.

Supply Capability:: 3000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Foundry Coke Ash 12%

Nut Coke with Size 10-30mm

Calcined Petroleum Coke with stable quality and FC 98.5% S 0.5% max

the NUT Coke of Size is 20 ---- 40 mm

The NUT Coke of Low Phosphorus

The Metallurgical Coke of Coke Strength after Reactivity 62

Metallurgical Coke of the size 30-80mm

Metallurgical Coke of size is 40-100 mm

1. Structure of M 40 80% Metallurgical Coke Description：

Coke is a hard texture, with carbon as the main component of irregular porous body, with cracks and defects in silver. The true density is 1.8 ~ 1.95 g/cm3, bulk density is 400 ~ 500 kg/m3, the porosity of 35% ~ 35%,.Coke all vertical and horizontal crack can be seen with the naked eye observation. The vertical and horizontal crack along the thick break, still is focal piece containing micro cracks. Separate focal piece of micro cracks along, namely coke porous body, also known as coke. Focal body consists of porosity and the pore wall, hole wall is also called the coke quality, its main component is carbon and minerals. How much coke crack directly affect the size and crushing strength of coke. Focal piece of micro cracks and holes spore structure of coke and abrasive resistance and high temperature reaction performance of coke has a close relationship. Spore structure usually use stomata average pore size and pore size distribution, specific surface area and pore wall thickness parameter.

2. Main Features of the M 40 80% Metallurgical Coke ：

• Quality assurance

• Mutual benefit

• Preferential price

• Various choice

3. M 40 80% Metallurgical Coke Images:

M 40 80% Metallurgical Coke

4. M 40 80% Metallurgical Coke Specification:

Parameters	Guarantee
Moisture (ARB)	5% max
Ash (DB)	12.50% max
Volatile Matter (DB)	1.4% max
Sulphur (DB)	0.7% max
Phosphorus (DB)	0.035% max
CSR	62% min
CRI	28% max
M40	80% min
Size 30-90 mm	90% min
Mean Size	52 mm

5. FAQ

We have organized several common questions for our clients，may help you sincerely：

1) How about your company？

Our company began to export coke when China cancelled 40% of coke export tariffs and quotas on January 1, 2013. We export many kinds of coke, such as CSR60 % and CSR 62% metallurgical coke (met coke), the NUT coke of 20 to 50 mm, coke breeze of 3 to 6 mm, and so on.

2) Main type

Metallurgical coke is blast furnace coke, coke, iron alloy and nonferrous metal smelting with coke. As more than 90% of the metallurgical coke for blast furnace ironmaking, so often called the blast furnace coke metallurgical coke.

Foundry coke is dedicated to cupola molten iron. Coke is the main fuel of cupola molten iron. Its role is hot metal melting furnace charge and overheating, support stock column maintain its good air permeability. As a result, coke blocks should have large, low reactivity, low porosity, with sufficient impact crushing strength, ash content and low sulfur content.

3) Application of coke

• Used for blast furnace ironmaking and used for copper, lead, zinc, titanium, antimony, mercury

• Other non-ferrous metal smelting of blast furnace,

• Reducing agent, compound

• The function of stock column frame.

Q: What is the difference between metallurgical coke and chemical coke: Quality index of cokeCoke is a solid product of high temperature carbonization, the main component is carbon, is a crack and irregular pore structure (or porous). The number of cracks has a direct impact on the strength and crushing strength of the coke, the index is generally measured in terms of crack degree (the number of cracks in the unit volume coke). The index of pore structure is mainly expressed by the porosity rate (the percentage of the total volume of coke), which affects the reactivity and strength of coke. Different uses of different coke porosity index requirements, the general requirements of metallurgical coke porosity in the 40 ~ 45%, 35 ~ 40% in coke, coke export demand in about 30%. Coke crack degree and the porosity level, and the coking coal has a direct relationship, such as coal based coke refining, crack, high porosity, low strength; with coal as the foundation of the coal refining coke crack less, low porosity and high strength. The strength of coke is usually represented by two indices of crushing strength and abrasion resistance. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10 value method, commonly used in our country the German migon drum test.

Q: Standard grade two grade coke standard: Evaluation of coke quality1, sulfur content in coke: sulfur is a harmful impurity of iron smelting, which reduce the quality of pig iron. The sulfur content in the pig iron is more than 0.07%. 11% of the sulfur from the blast furnace charge into the furnace comes from the ore, and the other comes from the limestone; the other is from the coke, so the coke is the main source of sulfur in the charge of the 82.5% of the charge. Sulfur content in coke directly affects the production of blast furnace. When the sulfur content in coke is greater than 1.6%, sulfur increased 0.1%, the amount of coke increased 1.8%, limestone amount increased 3.7%, 0.3% increase in amount of ore blast furnace output to reduce the sulfur content under 1.5 - 2.0%. metallurgical coke is not greater than 1%, the use of large and medium-sized metallurgical coke content in blast furnace is less than 0.4 - 0.7%.

Q: Coke is how to produce, what is its purpose?: Under the condition of air isolation, the bituminous coal is heated to 950-1050 DEG C, which is finally made into coke by drying, pyrolysis, melting, bonding, solidification and shrinkage. Coke oven gas produced in the process of coking and recovery is not only a high calorific value of fuel, but also an important industrial raw material for organic synthesis.

Q: The chemical composition of coke is m10.m25: Quality index of cokeThe quality index of coke coke [] is a solid product of high temperature carbonization, the main ingredient is carbon, is the pore structure has a crack and irregular (or pore porous). The crack number directly affects the coke strength and crushing strength, the index of general degree (refer to how to crack crack length unit the volume of coke in the measure.) to measure the pore structure of the main indicators for the porosity (coke pore volume only percentage of the total volume) that it affects the coke reactivity and strength

Q: The total amount of heat released by the fully burnt 200g coke is 60% by mass of 10kg water absorption [q coke =3.0 * 107J/kg, C water =4.2 * 103J/ (kg = C)], q:(1) how much heat is absorbed by water?(2) if the initial temperature of water is 10 degrees C, then, after absorbing heat, the temperature will rise to how much?: At a standard atmospheric pressure, the boiling point is 100 DEG C, the temperature of the water rises to a temperature of 100 DEG C, and the temperature will not change,So the water temperature can be increased to 100;Answer: (1) the heat absorbed by water is 3.6 * 106J;(2) after absorbing heat, the temperature of the water will rise to about 100 degrees centigrade

Q: After the long-term use of non stick pan, oil stains can not be effectively removed, over a long period of time in the non stick coating on the formation of a layer of coke, the effect of losing non stick. As a result of this layer of coke is relatively dense and smooth, scouring cloth has been ineffective, steel ball can not be used to damage the coating, what chemical or physical methods to remove this layer of coke?: After high temperature sintering, and carbonization of things, glued to the pot, often with chemical methods.The most effective way to do this is by hand:

Q: What is the difference between coking plant and coke plant: Production equipment and production processes are complex.Coke plant, generally only the coal into coke on it, so simple.

Q: F.C Ash S V.M H2O SizeMore than 85 less than 15 less than 8 less than 0.8 less than 1.5 10-70mm over 90%,I would like to ask, what is the size of the corresponding coke? Metallurgical coke or something else, there is no relevant information about, thank youF.C = 85, Ash = 15, H2O = 8, S = 0.8, V.M = 1.5, Size:10-70mm 90% and above, so clear, like the product, the current price?: Three metallurgical coke: fixed carbon 83-84.5%; calorific value 6500cal/kg; ash < 15%; volatile < 1.9%; all 6% "1%" water; sulfur;Maybe not, I'll give you a web site, find it yourself

Q: Listen to a lot of people say that steel is now coke is not true?: But at present, the iron making technology without coke has not yet been relatively mature, and it is not dominant compared with the traditional ironmaking technology. Coke industry still has development prospects.