High alumina textile ceramic rollers
-Wear resistance
-Textile ceramic component
-99% alumina textile ceramic wire roller

Performance
Item		Unit	95 Al₂O₃	96 Al₂O₃	99 Al₂O₃
Physical Characteristics	Bulk density	g/cm³	3.6	3.6	3.9
Physical Characteristics	Water absorption	%	0	0	0
Mechanical Characteristics	Flexural strength	Mpa	320	340	360
	Hardness Vickers	Gpa	12.2	13.5	15.6
	Elastic modulus	Gpa	280	320	370
	Poisson’s ratio	-	0.22	0.23	0.23
Thermal Characteristics	Linear expansion coefficient	(20⁰C-500⁰C) 10^-6/⁰C	7.1	7.2	8
	Thermal conductivity	w/(m.k)	16	24	32
	Specific Heat	10^-3J/(kgK)	0.78	0.78	0.9
Electrical Characteristics	Dielectric constant (1MHZ)	-	9	9.4	9.9
	Dielectric loss angle	*10^-4	15	5	1
	Dielectric strength	*10⁶V/m	12	15	15
Processing technology
Process range (mm)
Outside Diameter	1---300
Inside Diameter	0.5---300
Length	0.5---1200
Accuracy of working (mm)
Perpendicularity	0.01
Concentricity	0.01
Roundness	0.005
Straightness	0.005
Parallelism	0.01
Planeness	0.005
Roughness	0.05
Fit clearance	0.005

High alumina textile ceramic rollers

99% alumina textile ceramic wire roller.
alumina ceramic.
alumina ceramic a smooth surface.
Long service life.
a best price.

Alumina ceramic , Textile ceramic eye ,Textile ceramic part ,Spinning ceramic parts

alumina textile ceramic component

alumina textile ceramic part for textile manufacturing machine

Do not wear easily, low friction

Suitable for using in textile machine and fine spinning and knitting machine.

Customized produciton is avaiable.

We can supply the products according to customer's drawings, samples and performance requirement

High Alumina Textile Ceramic Rollers

Q: What are the production methods of calcium silicate board material?: The two reaction method (also called combined method) is the most complete and easy to obtain process of high temperature, light weight and high strength calcium silicate products and calcium silicate boards, but its disadvantages are long process, high energy consumption and large investment.

Q: What kind of insulation material can withstand 350-600 degrees of high temperature?: GB 50264-97 code for design of thermal insulation engineering for industrial equipment and pipelines98T901 cold storage Atlas of piping and equipment

Q: Which is better, asbestos free calcium silicate and aluminium silicate refractory fiber?: Aluminum silicate fiber can be divided into many kinds according to the aluminum content, the use temperature range is relatively large, the heat insulation property is good, but the price is more expensive.

Q: What is the difference between calcium silicate board and cement fiber board?: Fiber cement pressure plate is cement, fiber and other raw materials, after pulping, molding, thousands of tons of press. Calcium silicate board is made of silica and calcium plus fibrous material after pulping and formed by chemical reaction in high temperature environment. Therefore, the difference between the two is very large, mainly in the following aspects:1, from raw materials, calcium silicate board and fiber cement pressure plate difference is mainly calcium silicate board cement content is little, with sand and fly ash instead of cement.2, fiber cement pressure plate is a physical product, calcium silicate board is a chemical product.3, fiber cement pressure plate has press, calcium silicate board has no press; calcium silicate board has autoclaved Fu, fiber cement pressure plate no..4. The density of the fiber cement pressure plate is higher than that of the calcium silicate board, the density of the fiber cement pressure plate is above 1.5g/cm3, and the density of the calcium silicate board is about 1.2g/cm3.5, fiber cement pressure plate thickness can do 2.5-100mm, calcium silicate board can not do less than 4mm of ultra-thin plates and more than 30mm super thick plate, general calcium silicate board manufacturers can only do 6-12mm thickness.6, the normal production of fiber cement pressure plate color is cement color, calcium silicate board color is white.

Q: What are the high temperature resistant insulation materials at 400?: Thermal insulation materials for thermal equipment and pipes are mostly inorganic insulation materials. This kind of material has the characteristics of no decay, no burning, high temperature resistance and so on. For example: asbestos, diatomite, perlite, glass fiber, foam glass concrete, calcium silicate and so on.

Q: What heat preservation material is used for thermal insulation of steam pipe in power plant? How thick is the bag? Please advise!: Steam pipe in power plant thermal insulation rock wool board thickness, according to the temperature in the pipeline to choose, the higher the temperature insulation thickness is generally 80 to 150 mm.

Q: What are the main use of lime?: Lime stabilized soil mixes lime powder or lime powder with various crushed or formerly loose soil, and is obtained by mixing, compacting and curing. It is called lime stabilized soil. It includes lime soil, lime stabilized gravel soil, lime crushed stone soil and so on. Lime stabilized soil has a certain strength and water resistance. Widely used as a building foundation, ground cushion and road base.

Q: What's the use of low carbon steel insulated nail hooks for power plants?: Low carbon steel nail insulation (aka: insulation pins) material: low carbon steel wire for power plants or stainless steel wire products: insulation nail. Hook nail is a power plant by mechanical processing of special insulation nail models: nail diameter: 3 mm with 3.5mm with 4 mm with 5 mm with 6 mm etc.

Q: What's the difference between white cement and ordinary cement?: The main chemical composition of Portland cement clinker is calcium oxide, silica, alumina and iron oxide. Calcium oxide mainly derived from calcareous raw materials, such as limestone, chalk, marl; alumina and silica from aluminum silicate containing substances, such as clay, blast furnace slag and fly ash; iron oxide is used in sulfuric acid production of sulfur iron slag. For the content of calcium oxide production of Portland cement lime materials in 52%; silicon oxide content of clay in raw materials up to about 57%, the alumina content is less than 20%. In order to reduce the calcination temperature and to produce part of the melt during calcination, a small amount of iron oxide is often added. Of raw materials but also control the content of alkali and Magnesium Oxide, Magnesium Oxide is content in the cement clinker should be less than 5%, total alkalinity (Na2O+K2O) for general cement should be less than 1.2% of low alkali cement should be less than 0.6%.

Q: Eterpan with calcium silicate is sold on the market are the same thing? Non asbestos calcium silicate board is Eterpan it: Eterpan is calcium silicate board there is a famous brand. Non asbestos calcium silicate board has many kinds, Aitken is just one.

Send your message to us

*Email

*TEL

*Quantity

*Unit