High Alumina Brick - Wholesale Firebrick Prices
- Ref Price:
-
- Loading Port:
- China main port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 1000 pc
- Supply Capability:
- 100000 pc/month
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
Quick Details
| Place of Origin: | Shandong, China (Mainland) | Shape: | Brick | Material: | Alumina Block |
| SiO2 Content (%): | 20% | Al2O3 Content (%): | >65% | MgO Content (%): | 0.5% |
| CaO Content (%): | 0.01 | Refractoriness (Degree): | 1770°< Refractoriness< 2000° | CrO Content (%): | 0.1~0.3% |
| SiC Content (%): | 0.1~1.4% | Model Number: | SK38 STD | Brand Name: | CNBM |
| Name: | firebrick | AL2O3 content: | 65% | Density: | 2.4g/cm3 |
| Size: | 230*114*65mm | Refractoriness: | ≤1790℃ | Packing: | wood pallet |
| Standard: | ASTM,JIS | AL2O3+SIO2: | 95% | Porodity: | 23% |
| Working temp: | 1520C |
Packaging & Delivery
| Packaging Details: | Standard export wooden pallet with PET strap fixed, paper or non-woven fabrics between layers, finally wrapped with plastic shrink film from outside. |
| Delivery Detail: | 20 days |
wholesale high alumina firebrick prices
Product Description
High alumina bricks for general uses are mainly made from super quality Bauxite, bonding chamotte and additives, being high pressure pressed and sintered in high temperature.
Application:
They were widely used in all parts of furnace lining of metallurgic, petroleum, construction materials, machinery and militaries, etc.
Features and advantages:
1. The dimensions are more exactly.
2. Low iron content and impurities
3. Good thermal stability;
4. High refractoriness,
5. anti alkaline /acid erosions,
6. Mechanical and chemical properties are very good.
7. Strong thermal shock resistance.
Firebrick Technical Index
Item | High Alumina Brick | |||
DKS-36 | DKL-36 | DKS-38 | DKL-38 | |
Al2O3 | ≥48 | ≥55 | ≥65 | ≥75 |
Refractoriness °C | ≥1750 | ≥1770 | ≥1790 | ≥1790 |
Refractoriness under load°C | ≥1420 | ≥1470 | ≥1500 | ≥1520 |
Permanent liner change% | 0--0.2 | 0.1--0.4(1500°C×2h) | ||
Apparent Porosity % | ≤22 | ≤22 | ≤23 | ≤23 |
Cold crushing strength Mpa | ≥39.2 | ≥44.1 | ≥49.0 | ≥53.9 |
Bulk Density g/cm3 | 2.25-2.6g/cm3 | |||
Common sizes:
Straight type | Arch type | Wedge type |
L×W×H (mm) 230×114×65 230×114×75 230×114×32 220×110×60 220×110×50 220×110×40 220×110×30 | L×W×H/h (mm) 230×114×65/55 230×114×65/45 230×114×65/59 220×110×65/50 220×110×75/65 220×110×60/40 | L×W×H/h (mm) 230×114×65/55 230×114×65/45 220×110×75/65 220×110×60/40 |
Other sizes according to customer requirements
| ||
- Q: Introduction of high alumina brick
- High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.
- Q: What is the standard classification of high alumina bricks and high alumina bricks?
- Refractory brick is non-metallic materials can be classified according to a kind of inorganic material, high aluminum brick, clay brick, magnesia brick, corundum brick, mullite bricks, silicon carbide materials such as brick, high alumina brick is used as a relatively wide range of products in accordance with the refractory brick high alumina refractory materials by high aluminum brick is generally divided into Al2O3 content three: I - II - >75% Al2O3 content; the content of Al2O3 is 60 ~ 75%; III - Al2O3 content from 48 to 60%.
- Q: What is the price of the first grade high alumina brick?
- The specifications and different prices, relatively large fluctuations of the main push of the refractory Dongxin high alumina brick high alumina brick prices generally around 3000 have various levels of Dongxin refractories
- Q: How are the high alumina bricks fired?
- Generally, the high alumina bauxite is added with a small amount of clay. After being ground, the gas is injected and shaped in the form of slurry by the way of gas attack or foam, and it is burnt at 1300~1500 DEG C. Sometimes industrial alumina can be used to replace part of bauxite clinker. Used for lining and thermal insulation of masonry kilns, as well as for areas where there is no high temperature, high melting material erosion and erosion effects. When touching the flame directly, the touch temperature shall not be higher than 1350 degrees.
- Q: Aluminum content 38, silicon content 55 What refractory bricks?
- Semisilica brick: the content of Al2O3 is 15% ~ 30% of aluminium silicate refractory products. Manufacturing products are semi silica quartz containing impurities or native clay kaolin, refractory clay or kaolin beneficiation tailings and the pyrophyllite
- Q: Which is faster for heat transfer between corundum bricks and high alumina bricks?
- 75 high aluminum and 43 clay bricks, 75 single weight 4.5kg or more. 43 3.65kg or so, the use of temperature 75, high aluminum in about 1520, 43 of brick 1430 or so, the color of 75 pan white, 43 of the Loess color. In short, the difference is great.
- Q: How to reduce porosity of high alumina brick
- In order to reduce the porosity of high alumina brick, the corresponding measures should be taken from the selection of raw materials, batching, mixing, molding and firing.
- Q: How to distinguish the good or bad of the high aluminum brick?
- In the procurement of high alumina brick, the first color, high quality aluminum brick, brick surface smooth, yellow color pale, four sides equal, no broken angle, no cracks.
- Q: How high can aluminum bricks expand at 80O degrees of heat?
- The expansion of high alumina brick is not only related to temperature, but also related to its material composition. The refractory temperature of high alumina brick is above 1770 centigrade. The temperature of 800 DEG C has little influence on the expansion of high alumina brick.
- Q: Use of high alumina refractory bricks?
- Because of the high Al2O3 high aluminum products, low impurity content, the formation of fusible vitreous body less so than the clay brick high load softening temperature, but because mullite crystallization has not formed the network organization, so the load softening temperature is not high silica brick.
Send your message to us
High Alumina Brick - Wholesale Firebrick Prices
- Ref Price:
-
- Loading Port:
- China main port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 1000 pc
- Supply Capability:
- 100000 pc/month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords