Oven Use Refractory Brick SK34 Standard Size of Brick Types of Fire Bricks
Product Description
Clay Brick for Coke Oven and Metallurgy Use | ||
N-2a | N-1 | |
Refractoriness (℃) | 1730 | 1750 |
Refractoriness Under Load (0.2MPa ℃) | 1350 | 1400 |
Reheating Linear Change (1500℃* 2h) | +0.1/-0.5 | +0.1/-0.4 |
Apparent Porosity (%) | ≤24 | ≤22 |
Atmospheric Pressure Strength(MPa) | ≥25 | ≥30 |
High Alumina Brick | ||||
Lz-75 | Lz-65 | Lz-55 | Lz-48 | |
Al2O3 (%) | ≥75 | ≥65 | ≥55 | ≥48 |
Refractoriness (℃) | ≥1790 | ≥1770 | ≥1770 | ≥1750 |
Refractoriness Under Load (0.2MPa ℃) | 1520 | 1500 | 1470 | 1420 |
Reheating Linear Change (1500℃* 2h) | +0.1/-0.4 | +0.1/-0.4 | +0.1/-0.4 | +0.1/-0.4 (1450℃*2h) |
Apparent Porosity (%) | ≤23 | ≤23 | ≤22 | ≤22 |
Atmospheric Pressure Strength(MPa) | ≥54 | ≥49 | ≥44 | ≥40 |
Our Services
1. We will reply to you immediately.
2. Our products will be made according to your index.
3. Other details could be discussed according to customers’ requirements.
Production & Quality
1.Production Process
Crushing→Mixing→Shaping→Drying→Firing→Inspection→Packing shipment
2.Quality Control
a.According to the chemical content,raw materials are classified into different levels to ensure quality of brick first.
b.During the production,every brick will be weighed twice strictly to reduce the error of weight .
c.Before delivery, the inspectors will inspect the size,appearance,physical and chemical properties of brick again in factory.
F&A
Q1.Are you a manufacture or trader?
A:To be honest we are a trader,but we have stable cooperation factories.And we can supply good pre-sale service, after-sales service.
Q2.Can we visit your company?
A:Sure,welcome at any time,seeing is believing.
Q3. Do you provide samples?
Yes, samples are available.
Q4. Do you accept OEM?
Yes, we can do OEM.
Q5.What's the MOQ of trial order?
A:No limit,We can offer the best suggestions and solutions according to your condition.
Q6.What are the payment terms?
Usually T/T,but L/C,Western Union etc are available for us.
Q7. How long is delivery time?
The delivery time will be determined according to the quantity of the order.
Q8.How are your products’ quality?
The products will be strictly inspected before shipment, so the quality could be guaranteed.
Q9.How to slove the quality problems?
A:If the products are not confirmed to customer samples or have quality problems,our compay will be responsible to make compensation for it.
Q10.What is the service life of your bricks?
A:The service life of different bricks is unlike.It also depends on your using condition and method.
Q11.How about your company's certification?
A:ISO9001 and Test Report,also we could apply other necessary certification.
- Q: What is fireproof concrete?
- According to the different properties of fire resisting and heat resisting concrete, they can be divided into silicate, aluminate, phosphate, sulfate, chloride, sol and organic substance, fireproof and heat-resisting concrete, etc.. The following are mainly used silicate, aluminate, phosphate, sulfate fire, heat-resistant concrete.
- Q: What are the reasons for the spalling of refractory bricks in the production of lime kiln?
- Therefore, the choice and masonry of refractory bricks are of vital importance. If there is a brick kiln kiln off block process of reproduction, is now because of the use of refractory brick kiln material mostly three grade high alumina bricks. The content of AL2O3 is about 55%, of which the content of Fe2O3 is about 2%, which is weak, and the alkali corrosion resistance is a little worse. In a containing three grade high alumina bricks in the composition of AL2O3, Si2O3, and other elements also contain K, Na trace, were the most, thus causing the system of the low melting point is very low, even at 1400 DEG C has been liquid phase, and generate CaAL12O19 limestone and calcium feldspar etc.. Form corrosion loss. Therefore, a long time will cause the loss of block. On the one hand, it may be caused by construction.
- Q: What is the standard size of high alumina brick?
- Standard brick: 230 x 115 x 65; four points: 230 x 115 x 40; three points: 230 x 115 x 30; 150 x 120: Brick gable. Light weight brick 1 to 1.7 kilograms; heavy clay superscript brick weighs 3.75 kilograms; light 30 plates 0.79 kilograms; light 40 plates, 1.05 kilograms.
- Q: What are the common thermal insulation materials for thermal conductivity?
- Aerogels are known to be the lightest solid materials in the world. It is made of nanometer silica aerogel as main material and is compounded by special process. The utility model has the advantages of high temperature resistance, low thermal conductivity, small density, high strength, green environment protection, waterproof and non inflammable performance. At the same time, with excellent sound insulation and shock absorption performance, it is now widely used in metallurgy, chemical, national defense, aerospace and other fields, is an indispensable high-performance insulation materials.
- Q: What materials are used for roof insulation?
- The other one is inorganic insulation materials, such as Portland, rare earth insulation, the thickness should be 5 cm or more, up to the high cost of auxiliary materials of construction, to reinforce, new inorganic insulation material, the material thickness, on the line of 2-3 cm, direct smear on the top of the house, without auxiliary material, than the price of wool, high aluminum silicate cotton.
- Q: What are the specifications for bricks?
- Thecompressive node as a new type of building energy-saving wall materials, which can be used for masonry walls, but also has good thermal properties, in line with the construction of the building module, reduce the loss in the process of construction, improve work efficiency; the hole rate reached more than 35%, can reduce the weight of the wall, save the foundation engineering cost. Compared with common sintered porous brick, it has the characteristics of heat preservation, heat insulation, light weight, high strength and high construction efficiency. The product is made of shale as raw material. It is produced by high vacuum extrusion molding machine and one yard firing process
- Q: The difference between ordinary and diatomite brick refractory brick
- To say the difference, the material is the biggest difference. There are diatomite brick density, compressive strength of small brick kiln belongs to the outer thermal insulation, and heavy refractory brick kilns for multi village in direct contact with the flame, high temperature resistance, good compressive strength, but no insulation. Hope to help you.
- Q: How to reduce the harm caused by two times mullite in high alumina refractory material
- Prolong the sintering time and adjust the aluminum content of the high alumina brick.
- Q: Use of high alumina refractory bricks?
- High alumina brick refractory than clay refractory bricks and brick refractory degree are higher, up to 1750~1790 DEG C, which belongs to high-grade refractory materials.
- Q: What is the difference between fireclay bricks and high alumina refractory bricks?
- First of all, there is a difference in the material, one is clay, and one is high aluminum.Also known as clay brick brick, is a man-made small bulk building, clay brick clay (including shale, coal gangue powder) as the main raw material, through mud processing, molding, drying and roasting, solid and hollow.
Send your message to us
High Alumina Brick - Oven Use Refractory Brick SK34 Standard Size
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 3000 pc
- Supply Capability:
- 50000 pc/month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords