Silica Brick G96 for Coke Oven

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: 500000 pc/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Insulating Fire Brick - GJM23

Silica Brick S94 for Hot Blast Stove

Silica Mullite Wear Resistant Brick

Silica Brick for Refining Furnace

Zircon Brick - China Fire Resistant Brick Manufacturer for Zircon Glass Kiln

$Silica Brick for Steel and Metallurgy - Aluminum Silica Refractory Brick$

Silica Brick for Steel and Metallurgy - Aluminum Silica Refractory Brick

Silica Brick for Hot-Blast Stoves S-96

Alumina Silica Brick Super Duty Silica Brick for Glass Melting Tank 93

Product Description:

General Information of Silica Brick For Coke Oven-G96

Our corporation produces a comprehensive range of silica bricks, with high silica content, all of these bricks exhibit excellent performance.

Our Silica bricks are the final result of blending excellent tridymite and cristobalite, as the main raw materials with cutting-edge technology, after mixing, drying, forming, in the high temperature shuttle kiln. There are also little quartz and vitreous within. We ensure you that the silica bricks made by us possess high quality standard and have gone through all the complicated quality control parameters. Their durability and strength adds life to the structure and they have the capacity of bearing high temperature.

Our competitive Advantage:

1.Competitive Price. Make the products competitive in your market.

2.Abundant Experience. Prevent cracks and twist in bricks.

3.Different Moulds. Save mould fees for you.

4.Lower ferric Oxide,porosity,higher refractoriness,density,higher CCS and exact tolerance.

5.Strict Quality Control. Meet clients’ quality requirement.

6.Safty packing,prompt delivery time,and excellent after-sales services.

7.Large stocks. Guarantee prompt delivery.

Silica Brick For Coke Oven---G96
Physical Properties:
Permanent Linear Change(1500℃×4h)%	%	0.2
Apparent Porosity, %	%	≤24
Cold Crushing Strength	Mpa	30
Refractoriness Under Load (T0.6)	℃	≥1680
Thermal Expansion	%	≤1.3
Density	g/cm³	-
Chemical Analysis:
SiO₂	%	≥95
Fe₂O₃	%	≤0.8
Al₂O₃	%	≤1
Residual Quartz	%	≤1
Note: Technical Data are typical average results from test pieces. The technical data is offered solely for your consideration. And we reserve the right to modify the technical data without any prior notice. Users of our products should make their own tests to determine the suitability of each product for their particular purposes.

Q: Common bond brick?: Manufacturing for silica brick binder hi-li sulfate pulp waste liquid and lime milk. When lime milk is used as a bond, it acts as a plasticizer. To increase the strength of lime brick in the drying process, as mineralizer in the firing, promote the transformation of quartz.

Q: Why will expand when heated brick: In the process of SiO2 drying, the four crystalline transformation points of 117, 163, 180~270 and 573 DEG C are found, among which the volume expansion caused by the 180~270 is the largest.

Q: The specific content is what gb/t2608-2012 brick: The provisions of the brick classification, technical requirements, test methods,

Q: What is acid refractory?: Acid refractory material usually refers to refractories with SiO2 content greater than 93%. Its main characteristic is that it can resist acid slag corrosion at high temperature, but it is easy to react with alkaline slag.

Q: How much is the highest melting point of silicon?: . True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. The total volume of heating to 1450 DEG about 1.5~2.2% expansion, the residual expansion will make cutting seam sealing, ensure masonry tightness and good structure strength, so that the brick load softening temperature will reach 1750 degrees Celsius above 1620 degrees in the case of the highest melting point.

Q: The United States of our brick anti-dumping duties?: At present of our brick anti-dumping rate is 73.10%

Q: How to judge the quality of brick, clay brick, high alumina brick furnace from the appearance?: Mainly depends on the color and density of brick. Another black clay brick and brick with iron oxide formation and how much the size of bricks

Q: Why is the three oxidation of two silicon is very harmful impurities in silica brick: Can generate the material needs is the best way to see the impurity problem!! the first consideration is whether can get the material impurities with what method choice after the time! Miscellaneous reactions cannot have new impurity formation! Selected cannot and need material reaction reagent!

Q: Common bond brick?: Manufacturing for silica brick binder hi-li sulfate pulp waste liquid and lime milk. When lime milk is used as a bond, it acts as a plasticizer. To increase the strength of lime brick in the drying process, as mineralizer in the firing, promote the transformation of quartz.

Q: Such purpose and scope please give me detailed points thank you: Acid refractory brick is mainly composed of tridymite and cristobalite and quartz and a small amount of residual glass phase.

Send your message to us

*Email

*TEL

*Quantity

*Unit