Raw Materials for Refractory Silica Brick Used in Glass Kiln
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 20 m.t.
- Supply Capability:
- 5000 m.t./month
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
You Might Also Like
General Information:
CMAX brand Silica bricks are made from high quality quartz tail sand, lime and mineralizing agent through the process of crashing, screening, mixing, pressing, drying and sintering.
Features of Refractory silica bricks for Glass Kiln:
1. high volume density of 2.34 g/cm3
2. high SiO2 content of 96%
3. low iron content of 0.8%
4. low melting point of 5%
Applications of Refractory silica bricks for Glass Kiln:
Because of the high temperature resistant performance significantly, long service life characteristics (as long as more than eight years) of refractory silica brick for Glass Kiln, it can significantly improve the quality of glass, so the refractory silica bricks are widely used in all kinds of glass furnace melting department, regenerator and other important parts.
Physical and chemical index of refractory silica bricks for glass kiln:
Item Brand | CMAX-96A | CMAX-96B | ||
SiO2 % ≥ | 96 | 96 | ||
Al2O3+2(K2O+Na2O) % ≤ | 0.5 | |||
Fe2O3 % ≤ | 0.8 | 1 | ||
Refractoriness °C ≥ | 1710 | 1710.0 | ||
0.2MPa Refractoriness under load °C ≥ | 1680 | 1670 | ||
Apparent porosity % ≤ | Brick with weight no less than 20kg | 20 | 20 | |
rick with weight less than 20kg | 22 | 22 | ||
CS MPa ≥ | 35 | 35 | ||
Bulk desity g/cm3 ≤ | 2.34 | 2.34 | ||
Starndard Size:
230*114*64mm
230*114*76mm
- Q: What advantage and disadvantages it has compared to common fire insulation materials
- Advantage and disadvantages of A-level heat perserving materials of equal effectiveness 1, the component materials of A level thermal insulation materials are inorganic materials, so it is high temperature resistant, non-combustible, fire-resistant; 2, good durability, aging resisitant, and having the same service life as buildings; 3, a level thermal insulation material can be well combined without using polymeride to bond, coat mortar, reinforced net, needing only few construction procedures. It is anti seepage with few quality problems; 4, absorb few water, and can bond firmly with the cement mortar, tile adhesive tile, safe and reliable; 5, a level thermal insulation material have the same service life as buildings, without the need to increase the cost on maintenance and renovation during its life span, and can maximize resource conservation.
- Q: Can anyone tell me what material the first rate fire resistant door is?
- Material of Class A fire doors mainly are steel, wood, steel and wood, and other materials. Fire door is one of the measures of the building fire separation, usually used on the firewall, entrance and exit of staircase or tube well openings, which is required to hane the abilities of smoke insulation and fire insulation. Fire door plays an important role in prevention of the spread of smoke and fire and the reduction of fire loss. Therefore, we must have strict requirements. Fire doors are divided into class A, class B and class C, whose properties of fire-resistant thermal insulation and fire-resistant integrity should be no less than the following values: Class A should be1.50h; class B should be1.0h; Class C should be 0.5h. - stipulations in article 4.5.1.2 in "The New Standard of Fire Doors" GB12955-2008. I hope my answer can help you. Thank you.
- Q: What is the best refractory company?
- Chinese brick trading network, is the most authoritative third party service platform, brought together more than 3000 refractory enterprises, working day experts online to answer, to analyze and evaluate the refractory industry, at the same time, cooperation with some refractories Association, I hope to help you!
- Q: What are the materials for refractory materials? What are their names?
- Neutral refractory is mainly composed of alumina, chromium oxide or carbon. Corundum products containing more than 95% of alumina are a kind of high quality refractory materials with a wide range of uses. Chrome brick by using chromium oxide as the main component of the corrosion resistance of steel slag is good, but the poor heat shock resistance, high load low deformation temperature. Carbon refractories with carbon bricks, graphite and silicon carbide products, low coefficient of thermal expansion, high thermal conductivity, heat vibration performance, high strength, corrosion resistance to acid and salt, without wetting of the metal and slag, light. It is widely used as lining material of high temperature, and also used as lining of autoclave in petroleum and chemical industry.
- Q: Which industry does the metallurgy and thermal insulating and refractory material belong to?
- Building Materials
- Q: What defect does fused cast refractories have ?
- In glass production, in addition to refractory as a building material and consider its durability, we still must attach great importance to its influence on glass quality. In such cases, the impact on the quality of glass is mainly the defects that eroded down refractory materials mixed in the glass, thus being prodeced of grass products. Defects are mainly foreign body defects such as sand, knot and wave reinforcement. What may directly affect the quality of glass are the wall brick and brick kiln bottom.
- Q: What are the requirements for the performance of refractory materials?
- Performance requirements for electric furnace lining refractory: 1, sufficient refractoriness and softening point. Because of eletric arc, the inner surface temperature of lining can be as high as 1500 to 1800 degree. 2, strong resistance to slag. Because the dust penetrate into the furnace through pore lining, and the refractory material subject to loss, leading to spalling. 3, good thermal and shock resistance. Because during steelmaking, opening door and lifting of the furnace will lead to sudden changes in the temperature of the furnace lining refractory material, so spalling and cracking may occur, damaging the lining premature. 4, enough strength, because the lining is impact during charging, tilted when vibration,and eroded by metal, slag and airflow. 5, the thermal conductivity shall be small, and the conductivity shall be low. The commonly used furnace refractories are dolomite brick, magnesia brick, high alumina brick, silica brick and magnesia ramming etc.. Because of different working conditions of the various parts of the furnace, the refractory materials are not the same.
- Q: The performance of refractory material
- As for easticity modulus, you can serach for information on the Internet or specialized books.
- Q: what are the types of piping insulation material fire?rating?
- Pipe insulation material Fire rating: heat conductivity coefficient(at room temperature) 0.025 grade non-combustible Class A low temperature bending ≤ 5000 breaking elongation 5,000 specifications 5000 anti-bending?strength 5000 compressive?strength 5000 special brand of high use temperature -250 ~ 150 ℃ core material, phenolic foam, form, stratiform, shape,flake.
- Q: What kinds of fireproof materials does the safe use?
- The fireproof materials of safe, copper is one of the most widely used material of locks for its good mechanical performance, corrosion resistance and processibility and beautiful colors.
Send your message to us
Raw Materials for Refractory Silica Brick Used in Glass Kiln
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 20 m.t.
- Supply Capability:
- 5000 m.t./month
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
Similar products
Hot products
Hot Searches
Related keywords