Magnesite Chrome Brick - Direct-Bonded Magnesia-Chrome Brick FAM-6
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
Description:
It is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate. The domestic so called magnesia –Chrome bricks .
The refractoriness of magnesia chrome bricks are more than 2000°C,and the refractory under load is a above 1550°C.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks
Specifications:
Direct-Bonded Magnesia-Chrome Brick
Main Application:It’s mainly applied to line the sintering zone of the new dry-processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
DBMGe-8A | ≥74 | ≥8 | ≤1.5 | ≤18 | 2.98 | ≥40 | 1660 |
DBMGe-8B | ≥74 | ≥8 | ≤2.0 | ≤18 | 2.98 | ≥35 | 1600 |
DBMGe-12A | ≥66 | ≥12 | ≤1.5 | ≤18 | 3.1 | ≥40 | 1660 |
DBMGe-12B | ≥66 | ≥12 | ≤2.0 | ≤18 | 3.1 | ≥35 | 1600 |
DBMGe-16A | ≥60 | ≥16 | ≤1.5 | ≤18 | 3.15 | ≥40 | 1660 |
DBMGe-16B | ≥60 | ≥16 | ≤2.0 | ≤18 | 3.15 | ≥35 | 1600 |
Rebonded Magnesia-Chrome Brick
Main Application:
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
RBMG-16A | ≥65 | ≥16 | ≤1.2 | ≤16 | 3.1 | ≥45 | 1750 |
RBMG-16B | ≥60 | ≥16 | ≤1.6 | ≤16 | 3.1 | ≥40 | 1700 |
RBMG-20A | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥45 | 1750 |
RBMG-20B | ≥60 | ≥20 | ≤1.2 | ≤16 | 3.15 | ≥40 | 1700 |
Semi-Rebonded Magnesia-Chrome Brick
Main Application:It’s widely used for every industrial furnaces of the metallurgical and building materials industry.
Chemical & Physical Data
Brand | MgO % | Cr2O3 % | SiO2 % | A.P. % | BDg/cm3 | CCS.MPa | R.U.L °C |
SBMG-16A | ≥60 | ≥16 | ≤1.5 | ≤17 | 3.1 | ≥40 | 1750 |
SBMG-16B | ≥60 | ≥16 | ≤1.8 | ≤17 | 3.1 | ≥35 | 1700 |
SBMG-20A | ≥55 | ≥20 | ≤1.5 | ≤17 | 3.15 | ≥40 | 1750 |
SBMG-20B | ≥55 | ≥20 | ≤1.8 | ≤17 | 3.15 | ≥35 | 1700 |
The bricks are packed on wooden pallet with papers in each layer and PP film wrapped outside of the whole pallet.
- Q: What are the differences between magnesium chrome bricks, such as direct bonding, re bonding, semi bonding, CO sintering and chemical bonding? Hope expert advice..
- Direct bonded magnesia chrome brickThe loose effect caused by the expansion of spinel when the oxide of magnesia brick is directly reacted with the oxide of iron can also be used to make magnesia chromite brick with synthetic common sintered material. In addition, there are non burned magnesia chrome bricks, for example, non burned magnesia chrome bricks combined with inorganic magnesium salt solutions. The unfired magnesia chrome brick has the advantages of simple production process, low cost and good thermal stability, but the strength of the high temperature is far less than that of the burnt brick. In the late 50s, a so-called "direct bonding" magnesia chrome brick was developed. The characteristics of this brick raw material is pure, high firing temperature, periclase and spinel phase with high temperature directly, silicate and other low melting point phase for island distribution, therefore, significantly improve the high temperature strength and slag resistance of brick.
- Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?
- High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees.
- Q: What are the environmental hazards of magnesia chrome refractory bricks?
- Magnesia chrome brick with MgO and Cr2O3 as the main component of this kind of brick, high refractoriness, high strength, anti alkaline slag corrosion resistance, excellent thermal stability, has certain adaptability in industry wide application of now high temperature acid slag
- Q: Magnesia chrome brick
- Magnesia chrome brick to Magnesium Oxide (MgO) and chromium oxide (Cr2O3) as the main ingredient, refractory periclase and spinel as main mineral components of products. The bricks have high refractoriness, high temperature strength, strong resistance to alkaline slag, good thermal stability, and certain adaptability to acid slag. The main raw materials for making magnesia chrome bricks are sintered magnesia and chromite. The purity of magnesia raw materials should be as high as possible, chrome iron ore chemical composition requirements: Cr2O3:30 - 45%, CaO = 1 ~ 1.5%.
- Q: How many kinds of refractory bricks are there?
- Dolomite brick: coating performance, good erosion resistance, but how many bricks f-CaO, yasumizu, it is difficult to transport and storage, production with less.
- Q: Magnesium chrome brick price?
- Magnesia brick factory with strong technology foundation as the basis, has developed more than 40 varieties of products, including building materials, non-ferrous metals, iron and steel and other fields, won the national high-tech products nearly a dozen, four patents, including magnesia spinel brick reached the world advanced levelFrom July 2006 to now won the high-tech enterprises in Liaoning province; National Standardization Management Committee issued the "adopting international standard product certificate" enterprises; in 2009 passed the ISO9001 quality management system certification; the famous brand products of Liaoning Province certificate certificate and certificate management, the reliable guarantee for the quality of products.
- Q: What are the types of magnesia chrome bricks for industrial use?
- It is possible to judge by the concrete kiln. The magnesium chrome bricks produced by real gold company are very good. Our factory purchased them the year before last, and their technicians were very professional, and gave us very good suggestions.
- Q: With different capacitance magnesia brick brick
- Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius. It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.
- Q: What is the difference between magnesia chrome brick and direct bonded magnesia chrome brick?
- The performance of direct bonding magnesia chrome brick is better than that of common magnesia chrome brick.
- Q: What are the main raw materials of magnesia chrome bricks?
- Magnesium alloys are alloys based on magnesium and other elements. Its characteristics are: small density (1.8g/cm3 magnesium alloy or so), high specific strength, high modulus of elasticity, good heat dissipation, good shock resistance, greater impact load capacity than aluminum alloy, good resistance to organic and alkaline corrosion. The main alloying elements are aluminum, zinc, manganese, cerium, thorium, and a small amount of zirconium or cadmium.
Send your message to us
Magnesite Chrome Brick - Direct-Bonded Magnesia-Chrome Brick FAM-6
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords