Magnesia Bricks Refractory Magnesite Bricks for Glass Kiln

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t.

Supply Capability:: 10000000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

magnesia bricks

1.The products are fused magnesia as main raw material, after a reasonable size distribution, high pressure forming, high-temperature sintering. The product has strong resistance to slag corrosion ability and high temperature dimensional stability. Mainly used in glass furnace regenerator, the upper part.

2.The regular magnesia bricks are made from dense dead burned magnesia that makes the bricks in good refractoriness, corrosion-resistance, and widely used in checker chamber of glass tank, lime kiln, non-ferrous metallurgical furnaces, open heart furnace, iron mixer and EAF of steel-making, and also ferro-alloy furnace, etc.

The bricks with MgO 95% or more in content take the secondary-burning dead burned magnesia or electrofused magnesia as the raw material and bured under the condition of ultra high temperature. They have the features of highly directly bonded and corrosion-resistance and widely used in various kinds of high temperature kilns and furnaces

$Magnesia Bricks Refractory Magnesite Bricks for Glass Kiln$

physical and chemical index:

			Quality Magnesia Brick
	MZ-91	MZ-92	MZ-95	MZ-96	MZ-97	MZ-98
MgO %	≥91	≥92	≥94.5	≥95.5	≥96.5	≥97.5
SiO2 %	≤3.5	≤3.0	≤2.0	≤1.5	≤1.0
CaO %	≤3	≤2.5	≤2.0	≤1.8	≤1.5	≤1.2
Apparent Porosity %	≤18	≤18	≤18	≤18	≤17	≤17
Cold Crushing Strength Mpa	≥58	≥60	≥60	≥60	≥60	≥60
Bulk Density g/cm3	≥2.9	≥2.9	≥2.95	≥3.0	≥3.05	≥3.1
0.2Mpa Refractoriness Under Load T0.6	≥1550	≥1600	≥1650	≥1650	≥1700	≥1700
Thermal Stability 950°C Wind cycles			≥20	≥20	≥20	≥20
Reheat liner change 1650°C×2h %	≤0.5

FAQ

Q2: What`s the lead time for my order?

A2: It depends on customers’ requirements and our production schedule. And usually we need 30-60 days for refractory bricks,10-25 days for unshaped refractory materials and 10-20 days for ceramic fiber blankets.

Q3: Can you offer Door-to-Door delivery?

A3: Yes, but only for some countries such us U.S., UAE, Saudi Arabia, Iran, and Russia, etc.

Q: What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?: Different grades of burned magnesia brick is mainly made of magnesia binder with different taste, there is not a big difference. However, the physical and chemical properties of binders should be controlled well!

Q: The index of magnesia brick: Room temperature compressive strength≥（MPa）（15－25－）24.5－24.5－24.5－24.5－40－40－40

Q: High purity magnesia brick masonry mortar for what?: High purity aluminum is 99.99, the first is not pollution, the stove is high magnesia brick masonry, 95% and 97% purity magnesia brick is for a long time did not find a good bit of fireclay, do not know what to build, now used light burned US powder and heavy burned magnesium plus brine built, with 2 months a griddle doesn't stick on magnesium brick, a touch off, there is no good sintering

Q: Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?: Manufacture of various refractory magnesia brick Magnesium Oxide, mainly from magnesite.

Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it

Q: Magnesia brick: Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclase. General can be divided into sintered magnesia brick (also called burnt magnesia brick) and chemically bonded magnesia brick (also known as the two major categories of not burned magnesia brick). Purity and high firing temperature of magnesia, due to the direct contact of periclase grains, known as direct bonded magnesite brick; made of fused magnesia bricks called electrically fused magnesite brick.

Q: How to identify the fused magnesia brick and sintered magnesia brick: Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying.

Q: How do you differentiate between the two clearly? Where is the key? Thank you: Burnt magnesia brick is made of high quality sintered magnesia as main raw materials, paper pulp as binder. After mixing and high pressure molding, it is fired in a high temperature tunnel kiln over 1550 degrees celsius. It has good thermal stability, corrosion resistance and spalling resistance. Widely used in converter, arc furnace and other industrial furnace lining refractory.Fused magnesia brick brick has compact structure, high mechanical strength, low impurity content, mainly used for the storage of large glass kiln

Q: Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.: If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position

Q: Combined with the ordinary clay brick and magnesia brick as an example, the existence of impurities in minerals and refractories production main components of the formed liquid relative what affect the performance.: Also known as clay brick brick, is a man-made small bulk building, clay brick clay (including shale, coal gangue powder) as the main raw material, through mud processing, molding, drying and roasting, solid and hollow.