General Information of Silica Brick For Hot Blast Stove----S95A
Our corporation produces a comprehensive range of silica bricks, with high silica content, all of these bricks exhibit excellent performance.
Our Silica bricks are the final result of blending excellent tridymite and cristobalite, as the main raw materials with cutting-edge technology, after mixing, drying, forming, in the high temperature shuttle kiln. There are also little quartz and vitreous within. We ensure you that the silica bricks made by us possess high quality standard and have gone through all the complicated quality control parameters. Their durability and strength adds life to the structure and they have the capacity of bearing high temperature.
Silica Brick For Hot Blast Stove---S95A | ||
Physical Properties: |
|
|
Permanent Linear Change(1500℃×4h)% | % | 0.2 |
Apparent Porosity, % | % | ≤23 |
Cold Crushing Strength | Mpa | 27 |
Refractoriness Under Load (T0.6) | ℃ | ≥1600 |
Thermal Expansion | % | ≤1.3 |
Density | g/cm3 | ≥2.35 |
Chemical Analysis: |
|
|
SiO2 | % | ≥95 |
Fe2O3 | % | ≤1.5 |
Al2O3 | % | ≤1 |
Residual Quartz | % | ≤1 |
Note: | ||
Feature of Silica Brick For Hot Blast Stove---S95A
Resistant to thermal shock, abrasion, chemical attack
High ability for anti-abrasion during work
Superior resistance to acids (including oxidizing)
Resistance to chlorine
Resistance to thermal shock and pressure changes
Low thermal and chemical expansion
Applications of Silica Brick For Hot Blast Stove---S95A
Silica brick for Hot Blast Stove is mainly used in hot-Blast Stove.
- Q: The introduction of silica brick
- Acidic silica brick refractory material, has good acid resistance and slag erosion, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature.
- Q: The hot blast stove when the temperature did not rise against the brick interface decreased
- Insulation of hot blast stove, key insulation silica brick hot stove, hot blast stove is shutdown or need repairing in blast furnace.
- Q: Common bond brick?
- When adding ingredients, the amount of lime added shall be converted to CaO, and the amount of addition varies depending on the product, usually fluctuating at 1.5~2.5%. For example, the production of coke oven silica brick, the dosage of CaO is 2.0~3.0%; the production of electric furnace top brick, the dosage of CaO is 1.4~1.75%.
- Q: The high thermal conductivity of silica brick and traditional brick what is the difference?
- Brick, high thermal conductivity has been greatly improved in terms of morphology, crystal structure, physicochemical index. The structure and morphology of high thermal conductivity of silica brick,Structure and morphology of high thermal conductivity and the traditional brick brick magnified 20 times were compared, high thermal conductivity silica pore size distribution is more uniform and finer.
- Q: Why is the three oxidation of two silicon is very harmful impurities in silica brick
- Heating calcination is the best way to extend this sort of impurity removal. Remove impurities
- Q: Can not use it two brick
- Acidic silica brick refractory material, has good ability in acid slag erosion
- Q: Brick
- The silica mineral phase is mainly composed of tridymite and cristobalite, there is a small amount of quartz and glass. Tridymite and cristobalite and quartz remaining at low temperature due to phase change, volume changes greatly, so the brick thermal stability at low temperature is very poor. In use, under 800 degrees Celsius, slowly heating and cooling, so as not to produce cracks. The use of temperature in blast furnace so should not be below 800 DEG on.
- Q: The chemical composition of silica brick and its physicochemical index?
- Brick refers to the refractory products in more than 93% of the content of SiO2
- Q: The formula in the refractory brick, and firing curve, who knows?
- Iron scale powder 0.45-0.55%, cement 0.9-1.1%, lime milk 6.5-7.5%, pulp 1.95-2.2%, the silica powder, perlite will be added to the wet mill in proportion, and then add iron scale powder, cement, dry roller 1-2 minutes later
- Q: Such purpose and scope please give me detailed points thank you
- Acid refractory brick is mainly composed of tridymite and cristobalite and quartz and a small amount of residual glass phase.
1. Manufacturer Overview
| Location | Hunan, China |
| Year Established | 2003 |
| Annual Output Value | Above US$ 50 Million |
| Main Markets | Taiwan; Germany; Italy; Turkey; France; England; Japan; Thailand; Vietnam; Idonesia; Egypt; Ukraine |
| Company Certifications | ISO 9001:2008 |
2. Manufacturer Certificates
| a) Certification Name | |
| Range | |
| Reference | |
| Validity Period |
3. Manufacturer Capability
| a) Trade Capacity | |
| Nearest Port | Shanghai; Shenzhen |
| Export Percentage | 20%-30% |
| No.of Employees in Trade Department | 3 People |
| Language Spoken: | English; Chinese |
| b) Factory Information | |
| Factory Size: | Twenty five thousand tons per year |
| No. of Production Lines | Above 8 |
| Contract Manufacturing | OEM Service Offered; Design Service Offered |
| Product Price Range | High; Average |
Send your message to us
Lime Silica Bricks for Hot Blast Stove - S95A
- Ref Price:
-
$404.61 - 494.53
/ m.t.
- Loading Port:
- China Main Port
- Payment Terms:
- TT or L/C
- Min Order Qty:
- 5 Tons m.t.
- Supply Capability:
- 1000 Tons Per Mon m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords