Intermediate Strength Proppan Monolithic Refractories for Cement Industry

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$Monolithic Refractories Insulating Castable Polyurethane Cement for Cement Industry$

Monolithic Refractories Insulating Castable Polyurethane Cement for Cement Industry

$Refractory Gunning Castable$

Refractory Gunning Castable

$Monolithic Refractories for Iron and Steel Industry - Acid Ramming Mass for Induction Furnace Lining$

Monolithic Refractories for Iron and Steel Industry - Acid Ramming Mass for Induction Furnace Lining

$Monolithic Refractories for Iron and Steel Industry - Calcined Petroleum Coke Supply with Large Quantity$

Monolithic Refractories for Iron and Steel Industry - Calcined Petroleum Coke Supply with Large Quantity

$Monolithic Refractories for Iron and Steel Industry:Calcined Petroleum Coke as Carbon Raiser$

Monolithic Refractories for Iron and Steel Industry:Calcined Petroleum Coke as Carbon Raiser

Low Nitrogen Carbon Raiser Graphite Petroleum Coke

Melt Extract Stainless Steel Fiber - Copper Coated Steel Fiber by CNBM International

Melt Extract Stainless Steel Fiber - End-Hooked Steel Fiber for Shotcrete

Technical Specification		Unit/Testing Method		Parameter		Unit/Testing Method		Parameter
Physical Properties	Typical Sieve Analysis Wt.-%-Retained	US mesh	Microns	16/30	20/40	US mesh（mesh）	Microns	30/60	40/70
		+16	+1180	1	0	+20	+850	0	0
		-16+18	-1180+1000	32	----	-20+30	-850+600	2	0
		-18+20	-1000+850	53	3	-30+60	-600+250	95	89
		-20+30	-850+600	15	64	-60+70	-250+212	3	9
		-30+40	-600+425	0	33	-70	-212	0	2
	Median Particle Diameter	mm inches		0.925 0.036	0.658 0.023	mm inches		0.370 0.013	0.310 0.011
	Crush Resistance (% by weight fines generated)	@10000(psi) 69 MPa @12500 (psi) 86 MPa		3.3 6.2	2.3 5.2	@10000(psi) 69 MPa @12500 (psi) 86 MPa		2.3 ---	2.0 ---
	Bulk Density	g/cm³ Ibs/ft³		1.88 117		g/cm³ Ibs/ft³		1.88 117
	Apparent Specific Gravity	g/cm³		3.30		g/cm³		3.30
	Acid Solubility	Weight loss%		5		Weight loss%		5
	Roundness /sphericity	/		0.9		/		0.9
	Absolute Volume	Gal/lb		0.037		Gal/lb		0.037
Chemical composition (Weight %)	Al₂O₃	%		＞71
	SiO₂	%		≤13
	TiO₂	%		≤5
	Fe₂O₃	%		≤10
	Others	%		≤1

Remark: （1）All the technical parameters are typical. (2)Other sizes like 16/30 mesh, 30/50meash, 40/70mesh are available etc according to customer’s requirement.

Q: The research direction of unshaped refractory for cement kiln: In fact, the classification of refractory refractories is very much, and specific, you are to use in which part of the cement kiln, different parts of the refractory used are not the same