$High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory System 1$
$High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory System 2$

$High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory$

$High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory System 1$

$High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory System 2$

High Quality Black Silicon Carbide 1-10mm Raw Materials for Refractory

Ref Price:

Loading Port:: China main port

Payment Terms:: TT OR LC

Min Order Qty:: 25 m.t.

Supply Capability:: 2000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

Black silicon carbide 99%
1.Sic 99% F.C. 0.35%
2. Fe2O3 0.5%
3.Ture density:3.9
4.Hardness(mohs):9.15

Black Silicon Carbide 1-10mm 90%

It is produced in a high temperature electric resistance-type furnace from a mixture of quartz sand and petroleum coke. The hardness of black silicon carbide is greater than fused alumina but less than synthetic diamond. Its mechancial intensity is greater than fused alumina, but is brittle and very sharp. The mineral has some electrical and heat conductivity. Black silicon carbide is typically used for machining or finishing cast iron ,non-ferrous metals, stone, leather, rubber, and other materials where sharp cutting characteristics are important. The mineral is also used widely as a refractory material or metallurgical additive. More detailed specifications can be supplied on your request.

Black silicon carbide Chemical Composition(%)

Grit Size	SiC	FC	Fe2O3
F12-F90	98.50	<0.20	0.60
F100-F150	98.50	<0.30	0.80
F180-F220	97.00	<0.30	1.20
F230-F400	96.00	<0.40	1.20
F500-F800	95.00	<0.40	1.20
F1000-F1200	93.00	<0.50	1.20
P12-P90	98.50	<0.20	0.60
P100-P150	98.00	<0.30	0.80
P180-P220	97.00	<0.30	1.20
P230-P500	96.00	<0.40	1.20
P600-P1500	95.00	<0.40	1.20
P2000-P2500	93.00	<0.50	1.20

Black Cilicon Carbide 1--10mm 90% with High Quality

Q: Who know what kind of fire shutter fire rating are there?: There is no national standard for fire protection performance of fire roller shutter in China, and now the executive standard of GB14102-2005 "fire shutter": F1, fire-resistant time 1.50h; F2, fire-resistant time 2.00h; F3, fire-resistant time 3.00h; F4, fire-resistant time was 4.00h before the national standards of fire shutter grading is introduced, expert advice that fire resistance test be made according to national standard, to reach back fire surface temperature rise requirements, if the refractory limit is greater than or equal to 3.0h, it is said to be super fire shutter, if test not inspect unexposed surface temperature rise as a judgement of the conditions, the door is referred to as ordinary fire shutter doors. I hope my answer can help you

Q: How long is the fire resistant limit for ultra thin fire retardant coating?: There is no detailed stipulation for ultra-thin fire retardant coating, and the thickness of the inside is the fire resistance limit shall reach certain time(at least). In engineering, the thickness of the fire retardant coating is generally determined according to the manufacturer's testing report. We use thin fire retardant coating for steel structure: if the fireproof limit is 2.5 hours. the thickness should be 4.9mm. If fire-resistant limit is 2 hours, the thickness shall be 3.5mm. If the refractory limit is 1.5 hours, the thickness shall be 1.75mm. If the limit is 1.0, the thickness is 1.17mm hope my answer can help you

Q: How to deiron refractory?: Deironing refractory can take physical methods into consideration, such as magnetic?separation, reselection, etc. And it can also take chemical methods, such as flotation.

Q: What is refractory aggregate?: Refractory aggregate is fire-resistant product improved with low temperature binder, chemical?compound and normal temperature strength.

Q: How long is the fire-resistant time of fireproof wooden door?: The fire-resistant time of fireproof wooden door is about 1 hour. Fireproof wooden door refers to the door whose door frames, skeleton of the door leaf, door panels are made of timber or timber work and fire endurance reaches the provisions of "GB50045-95 design of tall buildings for fire protection". Fireproof door is one of devices for fire?prevention and separation of the building, generally used on the firewall, entrance and exit between stairs pipe shaft opening, which plays an important role in the reduction of fire losses.

Q: Why should graphitic refractory materials be used now that graphite can burn?: In theory, any substance can burn as long as certain temperature is reached. Graphite is turned from diamond under anaerobic condition and at high temperature of 2 000 ~ 3 000 ℃. that is to say, ignition point of graphite (lamellar graphite ) under anaerobic condition will be at least above 3 000 ℃. There are many types of graphite, and their ignition points are also different. Ignition point of pyrolytic graphite is much low. Except for a few cutting-edge areas, fire endurance demand for most areas in daily life (eg. brake pad will add a certain amount of graphite) is under 1000 ℃. Therefore, graphite can be used as refractory material. That is, graphite can both burn and can be used as refractory material, which are not contradictory.

Q: Does anyone know about the A-level fireproof materials?: A-level decorative integrated plates of thermal insulation, water- and fire-proofing mainly can prevent fire and insulate heat with A-level fireproofing glass fiber as thermal insulation materials. The classification of A1-level external wall materials of thermal insulation, fire- and water-proofing: First, external wall thermal insulation materials: 1. silicate?thermal?insulation?materials 2. gelatine powder polyphenyl granules 3. steel wire gauze picking cement cystosepiment (grs board) 4. extruded sheets; Second, roofing materials: 1. xps extruded sheet 2. EPS foam board 3. perlite and perlite brick 4, vermiculite and vermiculite bricks; Third, heating and air conditioning materials: Polyurethane, rubberplastic sponge, polyethylene, polystyrene foam, glass wool, rock wool; Four, steel structure materials: Polystyrene, extruded sheet, Polyurethane board, glass wool roll mat, etc.

Q: What material is used for making refractory stone bowl?: Stone pot, to make it easy, is pot made of stone. Stone pot is carved from high-quality natural refractory stone with a professional way. It has attractive and diverse appearance, and it is hard, heat fast, not stick food and the cooked food is attractive and delicious. And it is rich in a variety of trace elements which is beneficial to the human body. High quality

Q: What's the fire resistance test method of doors and roller shutters?: Fire resistance test method of doors and roller shutters: This standard specifies the fire resistance test method for roller shutter doors under standard fire conditions. The method is used to test the fire resistance of the ventilating duct when bearing the external fire (A duct) and internal fire (B duct). Fire resistance test of vertical ducts may be conducted referring to this standard. 1.Test specimen1.1 The test specimen is obtained by cutting from any part of the qualified metal tube unless otherwise relevant standard or mutual agreement specifies the cutting position of the metal tube. 1.2 Length of the specimen: L≈2.5D+50mm (D: outer diameter of the metal tube). The cut surface of the specimen must be perpendicular to the axis of the metal , and the seamed edge of the cut should be round off. Test method GB243-82 of metal tube necking 2. Test procedures 2.1 In the test, punch or press the metal tube into the tapered conical seat (see Figure) with a hammer or press machine, and make it uniformly diminished to the regulated shrinkage X which is calculated according to the following formula: Test method GB243-822 for metallic pipe necking: The inner wall of the seat cover used in the test should be polished, and has certain hardness and is coated with lubricating oil. Its conicity is 1:10, 1:5 or others in accordance with relevant standard provisions. If there is no provision, then adopt the conicity of 1:10. This standard is not suitable for: a) The pipeline whose fire resistance depends on the fire resistance of the ceiling; b) The pipeline with access door, unless otherwise the access door is included into the pipeline and tested together; c) The pipeline with two or three sides; d) Fume exhaust pipes;

Q: What are the main materials in concrete fireproofing material?: it can be roughly divided into: fire-resistant coating for steel structure, finishing fire retardant paint, tunnel fire coatings, concrete fire?retardant?coating, cable refractory coating. fire-resistant coating for steel structure is divided into: Indoor ultra-thin fireproof coatings for steel structure, indoor thin steel structure fireproofing coating, indoor thick steel structure fireproofing coating, outdoor ultra-thin fireproof coatings for steel structure, Outdoor thin steel structure fireproofing coating, outdoor thick steel fireproofing coating. I hope it can help you. Hope to adopt my opinion Thank you! )