High Alumina Special Magnesia Alumino-Chrome Brick

High Alumina Special Magnesia Alumino-Chrome Brick System 1

High Alumina Special Magnesia Alumino-Chrome Brick

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

Refractory Bricks magnesia chrome bricks are mainly made from sintered magnesia and chrome-oxide after high pressure shaped

Refractory Bricks magnesia chrome bricks are mainly made from sintered magnesia and chrome-oxide, by high pressure shaping and high temperature firing. According to different requirements, the contents of the Cr2O3 can be changed.

Features;
Magnesite-ferrum spinel brick and synthetic magnesite-ferrum-alumina spinel brick are made of high purified magnesite clinker and ferrum-alumina spinel clinker at strictly controlled temperature and sintered atmosphere,which enables the product to have good flexibility and temperature vibration. The performances of attaching kiln wall and corrosion resistance are better good quality magnesite chrome brick.the product is update product for lining of large dry cement rotary kilns.

Physical and Chemical Indicators:

Items		Index
Items		QB/RS-1	QB/RS-2	QB/RS-3
Chemical Composition	MgO, % ≥	88	86	85
	Fe2O3 %	3-5	5-7	3-5
	Al2O3 %	3-5	1.0	1.0
	SiO2 % ≤	1.0	1.0	1.0
Bulk Density(g/cm3)		2.95	2.95	2.95
Apparent Porosity, % ≤		16	16	16
Cold Crushing Strength, MPa ≥		80	80	80
Refractoriness Under Load,°C, [0.2MPa×0.6%] ≥		1700	1650	1680
hermal Shock Resistance, Times, [1100°C, water-cooling]		10	8	10

Special Magnesia Alumina Chrome Brick

Q: What are the high aluminum bricks made of?: The amount of refractory mud accounts for about 6% of the brick weight

Q: What are the grades of high alumina bricks?: According to the size of high aluminum brick is divided into: standard brick, special-shaped brick.

Q: What are the requirements for Rubble backfill height?: Backfill should be filled with large stones, big face, small face upward, the decoration is stable, and then use small stones leveling, the gap between the stones can be swept into the slag, gravel, so that the gap filled.

Q: The cloth blowing is not uniform on the lime kiln refractory brick is damaged it: Lining 1 yuan to prevent direct damage to the Sindh kiln high temperature flame or air, to protect the kiln carcass; 2, to prevent harmful substances (CO, SO2) erosion of the kiln body; 3, to prevent corrosion, material flow on the kiln body; 4, reduce the kiln temperature, kiln body to prevent oxidation 5, has the function of corrosion; thermal insulation; 6, to improve the coating performance.

Q: What kinds of minerals are there in the five major categories of ore crystal chemistry?: Sulphide. A total of more than 200~300 kinds, followed by the type of silicate minerals, the weight of 0.25% of the crust. Chang Fu is an important nonferrous metal deposit, which is an important source of copper, lead, zinc, antimony and so on. It is of great economic value. The main features are: metal luster, color, streak is deep, low hardness, good thermal conductivity, than the major. Another feature is that because sulfides are often associated with magma, it is very easy to oxidize under the surface supergene action. Except for pyrite (6 ~ 6.5 hardness), the hardness is very low. Such minerals pyrite, chalcopyrite, galena, FeS2 CuFeS2, PbS, Sb2S3, stibnite sphalerite molybdenite, cinnabar HgS MoS2.

Q: What are the high temperature refractory mortars made of?: Products used in metallurgy, building materials, machinery, chemical, power industry, industrial thermal furnace, for masonryBuilding clay brick, high alumina brick and corundum brick have the characteristics of full grey seam, good airtightness, high bonding strength, high temperature performance and suitable construction time

Q: What does refractory consist of?: According to the chemical characteristics of refractory raw materials can be divided into acidic refractory materials, such as silica, zircon etc.; neutral refractory raw material, such as corundum, bauxite, mullite (acidic) (acidic), Ge (alkaline) iron and graphite; alkaline refractory materials, such as magnesite, dolomite, magnesium sand calcium sand.

Q: How high can aluminum bricks expand at 80O degrees of heat?: The expansion of high alumina brick is not only related to temperature, but also related to its material composition. The refractory temperature of high alumina brick is above 1770 centigrade. The temperature of 800 DEG C has little influence on the expansion of high alumina brick.

Q: What is the difference between fireclay bricks and high alumina refractory bricks?: High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3.

Q: What is the difference between metal compounds and metal solid solutions?: Sigma phase belongs to Affirmative system, there are 30 atoms in the unit cell, two element alloy, sigma phase formation is related with the following conditions: (1) the atomic size difference, phase difference between the maximum sigma atomic radius of a tungsten cobalt, the atomic radius difference is 12%. (2) there is a set of cubic lattice elements (coordination number 8), and another component is face centered cubic or dense six square lattice (coordination number is 12). (3) appear in "average number of races" (s+d layer electron number) in the range of 5.7 ~ 7.5. The region of the presence of sigma in the two - element alloy is shown in table 3. In the three element system, the concentration and temperature range of the formation of the sigma phase are affected by the addition of third components. Usually in chromium stainless steel in Fe Cr phase, in Fe - Cr - Mn three yuan, sigma phase iron chromium and chromium can form Mn two element, when the addition of manganese in stainless steel, will promote the formation of sigma phase, and stabilizes the wide temperature range. Many of the Fe Cr alloy elements. The phase temperature range increases. In less than 820C stable Fe Cr phase, silicon promotes the formation of D phase and the stable temperature increased to 900 to 960 DEG C, manganese and molybdenum can improve the temperature stability of sigma phase to 1000 DEG C.

Send your message to us

*Email

*TEL

*Quantity

*Unit