High Alumina Brick - Fire Brick for High Temperature Furnace

High Alumina Brick - Fire Brick for High Temperature Furnace System 1

High Alumina Brick - Fire Brick for High Temperature Furnace

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t.

Supply Capability:: 1000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

High Alumina Brick ALP80

High Alumina Brick UAL75 - High Alumina Bricks

High Alumina Brick UAL65 - High Alumina Brick

$High Alumina Brick SK38 - High Quality Refractory Material$

High Alumina Brick SK38 - High Quality Refractory Material

High Alumina Bricks with Superior Resistance

$High Alumina Refractory Bricks for Electric Furnace$

High Alumina Refractory Bricks for Electric Furnace

$High Alumina Brick Refractory Fused AZS Glass Melting Oven$

High Alumina Brick Refractory Fused AZS Glass Melting Oven

$High Alumina Fireclay Refractory Bricks for Furnace$

High Alumina Fireclay Refractory Bricks for Furnace

CNBM conforms strictly to the requirements of ISO 9000 quality control system during the production. MSDS is also available if you want. The thermal insulation fire clay brick meet with the requirements of ASTM & JIS standards. So pls stay cool with our quality.

Brief discription for High Alumina Fire Brick

CNBM High Alumina Fire Brick are classified according to alumina content ranging from 48% to 90%.

CNBM High Alumina Fire Brick are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc.

Brief features for High Alumina Fire Brick

◆Low thermal conductivity

◆Excellent acid and base slag个ing resistance

◆High refractoriness

◆Excellent thermal shock resistance

◆Excellent mechanical strength

◆Good spalling resistance and wear resistance.

◆Good corrosion resistance.

◆High-temperature creep rate is quite low.

◆Good volume stability at high temperature.

◆Low bulk density, low thermal conductivity, good thermal insulation performance.

Technical data for high aluminia bricks

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

Why us

Professional fire brick manufacturer. We have being specialized in producing refractory fireclay brick for more than 40 years so that we can guarantee a stable quality.

Guaranteed quality. Our production process conforms strictly to the requirements of ISO9000 quality management system. Quality inspection is carried out in every links of our production. SGS third party inspection is available.

Sound after sales service. We provide sound after sales service. We provide 24 hours’ consultation service. We are ready to answer your consultations at any time.

High Alumina Bricks Fire Brick For High Temprature Furnance

Q: Application characteristics of high alumina brick: Refractoriness. High alumina brick products are advanced varieties of aluminium silicate refractory products, and their refractoriness increases with the increase of Al2O3 content, generally not less than 1750 - 1790 DEG C. If the content of Al2O3 is more than 95% of corundum brick, the refractoriness can be as high as 1900-2000 degrees.

Q: What is the standard size of high alumina brick?: The country has laid down a number of criteria for the use of refractory bricks to unify market demand.

Q: How to make refractory bricks and boiler wall adhesion more firm?: If the condition, the user heat-resistant steel welding grip nails, expansion joints can not be too big.. Also to use high temperature aluminum brick, high temperature resistance, but also to extend its use cycle.

Q: Difference between low creep high alumina brick and ordinary high alumina brick: Low creep and high alumina brick is based on the theory of "three stones". The combination of bauxite and clay as the main raw material, adding kyanite, andalusite and sillimanite, commonly known as the "three stone" control, physicochemical index and size composition, using alumina mullite corundum + + raw materials such as technical scheme. In the production process, first to detect and control indexes of raw materials, crushing, grinding, sieving process, according to the distribution ratio of ingredients, the size and moisture control of mud mixing after to meet the requirements of forming and molding machine, the use of qualified abrasives, blow molding control number, size and flash at the same time, the detection efficiency of semi-finished products and meet the requirements. Production process: high temperature calcination of high-grade alumina, adding small creep rate of high temperature materials, by high-pressure molding and high temperature firing. It has the characteristics of high strength, low creep rate and high use temperature. Widely used in high temperature furnace, hot air furnace hearth lining, brick and so on.

Q: Does the chimney have high acid resistance?: The acid resistant bricks used for chimney are usually made of custom-made trapezoidal acid proof bricks, and the physical and chemical indexes of acid resistant bricks need to be confirmed according to the chimney's actual emission. At this point, you can consult our kerei refractories.

Q: What is the difference between fireclay bricks and high alumina refractory bricks?: First of all, there is a difference in the material, one is clay, and one is high aluminum.Also known as clay brick brick, is a man-made small bulk building, clay brick clay (including shale, coal gangue powder) as the main raw material, through mud processing, molding, drying and roasting, solid and hollow.

Q: What is the difference between metal compounds and metal solid solutions?: Sigma phase belongs to Affirmative system, there are 30 atoms in the unit cell, two element alloy, sigma phase formation is related with the following conditions: (1) the atomic size difference, phase difference between the maximum sigma atomic radius of a tungsten cobalt, the atomic radius difference is 12%. (2) there is a set of cubic lattice elements (coordination number 8), and another component is face centered cubic or dense six square lattice (coordination number is 12). (3) appear in "average number of races" (s+d layer electron number) in the range of 5.7 ~ 7.5. The region of the presence of sigma in the two - element alloy is shown in table 3. In the three element system, the concentration and temperature range of the formation of the sigma phase are affected by the addition of third components. Usually in chromium stainless steel in Fe Cr phase, in Fe - Cr - Mn three yuan, sigma phase iron chromium and chromium can form Mn two element, when the addition of manganese in stainless steel, will promote the formation of sigma phase, and stabilizes the wide temperature range. Many of the Fe Cr alloy elements. The phase temperature range increases. In less than 820C stable Fe Cr phase, silicon promotes the formation of D phase and the stable temperature increased to 900 to 960 DEG C, manganese and molybdenum can improve the temperature stability of sigma phase to 1000 DEG C.

Q: What are the lining structures of lime rotary kilns and what are the requirements for refractories?: The physical and chemical properties of refractory materials used in rotary kiln are as follows: physical and chemical properties of refractory materials used in rotary kilnMaterial name: high temperature compressive strength (MPa), softening temperature (DEG C), thermal shock resistance (1100 DEG C, cold water), sub volume density (g/cm3)Magnesia spinel brick is greater than or equal to 50 is greater than or equal to 1700 = 12 = 2.95High alumina brick is greater than or equal to 75 = 1520 = 8 = 2.57High aluminum bricks more than 50 = 1700 = 12 = 1The clay brick is greater than or equal to 30 = 1400 = 12 = 2.30

Q: What are the categories of bricks?: Clay brick materials, cheap, durable, and fire prevention, heat insulation, sound insulation, moisture absorption and other advantages, is widely used in civil engineering. Waste brick can also be used as aggregate of concrete. In order to improve the shortcomings of ordinary clay bricks, such as small, self important and waste of soil, they are developing in the direction of light weight, high strength, hollow and big blocks.

Q: What should be used as binder for making high alumina bricks?: Bond for making high alumina brick: soft clay has good plasticity, so the high alumina brick is usually made of soft clay as bond. However, the free Al2O3 free SiO2 and bauxite clinker clay in under 1200 degrees occurred two times of Mullization reaction, generate large volume expansion, silicon porosity, strength reduction. Therefore, the amount of clay powder in the ingredient should be no more than 5%.

Send your message to us

*Email

*TEL

*Quantity

*Unit