Corundum-Mullite Brick - High Quality Refractory Material

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$High Alumina Brick SK38 - High Quality Refractory Material$

$Corundum Brick - Low Apparent Porosity Refractory Bricks for Hot Surface Lining Furnace$

General Information

CMAX corundum-mullite bricks use the high-purity corundum as the main raw material, and are produced by advanced technology.

Feature
Low thermal conductivity
High strength
Good thermal shock resistance

Application
Industrial furnace lining
Glass furnace

Q: Mullite bricks in alumina alumina is what?: Mullite (3Al2O3 - 2SiO2) high alumina refractory materials as the main crystal phase. The general alumina content in 65% ~ 75%. In addition to mineral composition of mullite, alumina containing low also contain a small amount of glass phase and cristobalite; alumina containing high also contain a small amount of corundum. Highrefractoriness, up to over 1790 DEG C 1600. Load softening start temperature to 1700 DEG C. Compressive strength at room temperature is 70 ~ 260MPa.. The thermal shock resistance of sintered mullite and fused mullite brick two. Sintered mullite brick with high bauxite clinker as the main raw material, adding a small amount of clay or alum clay as binder, forming and sintering made of fused mullite bricks with high alumina and bauxite, refractory clay as raw material, adding charcoal or coke fines as a reducing agent, formed by reduction of electric melting method to manufacture. The crystallization of fused mullite than sintered mullite, thermal resistance Shock resistance than sintered products. The uniformity of content in alumina mainly depends on their high temperature properties and mullite phase and glass distribution. Mainly used in blast furnace, furnace top and bottom furnace, glass furnace regenerator, sintering kiln, petroleum cracking system dead lining.

Q: What are the properties of corundum mullite?: Lightweight materials have uniform internal structure, high compressive strength, corrosion resistance, heat shock resistance, oxidation resistance, high temperature and low thermal conductivity. Dongshin refractories manufacturers manufacturers supply, price is appropriate

Q: Corrosion mechanism of iron on refractory materials: Iron oxide can not be used as refractory,

Q: Which is faster for heat transfer between corundum bricks and high alumina bricks?: There must be a difference. They vary in color from the amount of aluminum, the weight, the temperature, and the color. For example: 75 high aluminum and 43 clay bricks, 75 single weight 4.5kg or more

Q: 2000 degree of high temperature materials, which belong to high temperature insulation materials?: What can withstand 2000 degree high temperature materials on the market? What are the materials belong to high temperature materials? High temperature insulation material the most common are the following: calcium silicate shell, aluminum silicate cotton felt, glass surface, diatomite, vermiculite, foamed cement etc.. Among them, the first three are the most common, especially the aluminum silicate cotton felt, which can withstand 650 degrees of high temperature.

Q: What material is heat insulated and not afraid of fire?: Industrial production of perlite as insulation materials began in the United States in 1964Arizona, while China's expanded perlite began production in the late 60s. Expanded perlite includes perlite and pineRock and obsidian (three of which are close to the water content), due to the high temperature in 1000-1300C0, the volume of rapid expansion of 4 - 30 times, so collectively referred to as expanded perlite. Its characteristics are: low thermal conductivity, fire resistance and sound insulation performance is good, non-toxic, cheap, but have very strong water absorption, thermal conductivity due to water is much higher than that of pearlite, water will cause its insulation performance degradation, inorganic porous material, low strength, easy to break; therefore in thermal insulation applications when the need to enhance the hydrophobic and expanded perlite.

Q: What are the high temperature insulation materials?: The most thermal insulation is a variety of cotton fiber insulation, but the temperature is not very high. Alumina polycrystalline fiber cotton, about 1600 degrees, mullite polycrystal, mixed polycrystal, lower temperature. Zirconia material is said to be capable of high temperature because zirconia has a melting point of 2700 degrees, 700 degrees higher than alumina. But it's not used. It's not clear.

Q: What kind of refractory material is used in the hearth of reverberatory furnace?: The alumina fiber has a maximum resistance of 1700 degrees, and the zirconium fiber is generally 1700 to 2200 degrees

Q: What material is good for refractory bricks?: Is the main varieties of acidic silica brick, refractory brick. It is mainly used for coke oven building, also used in furnaces all kinds of glass, ceramic and carbon calciner, refractory brick arches and other load-bearing parts, is also used in high temperature bearing part of hot blast stove, but should not be used in thermal equipment below 600 DEG C and the temperature fluctuation in the.