Corundum Brick with Al2O3 Content more than 90%

Corundum Brick with Al2O3 Content more than 90% System 1

Corundum Brick with Al2O3 Content more than 90%

Ref Price:

Loading Port:: Shanghai

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t.

Supply Capability:: 30000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

98% Corundum High Alumina Brick

$High Alumina Brick SK38 - High Quality Refractory Material$

High Alumina Brick SK38 - High Quality Refractory Material

Corundum Brick Corundum Bricks

$Corundum Brick Refractory Carborundum Kiln Brick$

Corundum Brick Refractory Carborundum Kiln Brick

High Alumina Brick and Insulation Brick for Kinds of Glass Furnaces

Cement Kiln Magnesite Bricks

Fireclay Brick for Hot Blast Stove

High Chrome Magnesite Chrome Brick for Glass Industry

General Information
CMAX corundum bricks use compact electrosmelted corundum and alumina powder as main raw materials., shaped under high pressure after machine-blending and fired at high temperature.Alumina content in more than 48% of a neutral refractory material. By alumina or other higher raw material forming and calcined alumina content. Thermal stability, high refractoriness in more than 1770 º C. Good slag resistance, used for building steel-making furnace, glass furnace, cement rotary kiln lining.

Feature
Low porosity
High compressive strength
Good chemical stability

Application
Linings of high-temp industrial kilns and furnaces

Technical Data

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

Corundum Brick with Al2O3 Content more than 90%

Q: What is the main component of corundum?: Corundum is the main component of Al2O3, often containing trace impurities such as Cr, Ti, Fe, V and so on.

Q: What are the advantages of refractories?: Special refractories are new inorganic non-metallic materials developed on the basis of traditional ceramics and refractory materials. For example, AZS brick, corundum brick, magnesia chrome brick, silicon carbide, silicon nitride bonded silicon carbide, nitrides, silicides, sulfide, boride, carbide and other non oxide refractory materials; calcium oxide, chromium oxide, alumina, Magnesium Oxide, beryllium and other refractory materials. Often used insulation refractories are diatomite products, asbestos products, insulation panels and so on

Q: What does refractory consist of?: According to the shape of the product is shaped and unshaped refractory materials two categories, according to the chemical properties of acidic, neutral and alkaline refractory materials three categories, commonly used as refractory material of alkaline and neutral, such as magnesia, alkaline burned magnesia brick, magnesia chrome brick, magnesia calcium brick, high alumina brick, corundum neutral brick, clay brick, including: unshaped castable, ramming material, gunning material, coating material, dry vibration material etc..

Q: What equipment is used for producing diamond blanks? How much is the investment?: Plus all the cables fifty thousand. Steel 10000 yuan. Corundum bricks; insulating bricks; clay bricks, these three require more than ten thousand. The electrode is about one hundred thousand. It's just an investment in an electric furnace. Together with the rear section processing and raw materials need hundreds of thousands of.

Q: Wave tile and throwing glaze, tile which good?: These two tiles have their respective advantages and disadvantages, in fact, to say which kind of good, mainly depends on the decoration of personal preferences and the location of the shop. If it is only the shop wall, then design and pattern rich whole glazed tile is good, it can make the room impressive, improve decorative effect, make the decoration style to fit the characteristics of his personality. In addition, clean up is relatively easy, not easy to contaminated with oil stains and other pollutants. If it is laying floor tiles, tile Douglas suggested the use of tiles, tiles of good antiskid effect, water absorption rate is relatively low, so the kitchen toilet bathroom and other wet places is not easy to water seepage, improve the convenience of life.

Q: What is the difference between corundum and high alumina?: The main components of high alumina brick are high alumina bauxite, mullite and partial corundum sand.The difference between them lies in the content of alumina and the alumina refractory products with alumina content higher than 48%The content of Al2O3 is higher than 90%, which is called corundum brick.

Q: High temperature refractory material?: Many kinds of refractory materials, usually by refractoriness level is divided into ordinary refractory materials (1580 to 1770 DEG C), advanced refractories (1770 to 2000 DEG C) and special refractories (more than 2000 DEG C); according to the chemical characteristics into acid refractory material, refractory materials and basic refractory materials. In addition, the refractory material used for special occasions.

Q: What kind of refractory material will be used in the glass kiln?: High temperature & glass corrosion performance of the brick is slightly lower than that of chromium oxide, also by isostatic pressing forming method, its technical indicators ZrO2>65%, <2.0% porosity, volume density of about 4.25g/cm3, the temperature in E glass is higher than 1370 DEG C have erosion. Used in the E glass melting pool unit kiln glass temperature slightly lower at the end of the transition path, forming the bottom of the pool and forming path path flow tank and bushing support brick etc.. In addition, the dense zirconia brick is used as the backing brick of the dense chrome brick.

Q: What is the difference between T3 refractory bricks and high alumina refractory bricks?: High aluminum refractory brick brick is all in one type of material classification, the material is AL2O3 high bauxite content above 55%, refractory brick by material into clay bricks, high aluminum brick brick brick corundum brick

Q: What kind of rock is corundum produced?: If Ti4+ and Fe2+ containing a small amount of blue, a sapphire; containing six symmetrically distributed acicular rutile or other inclusions in some crystals, can produce six star awn, known as star ruby or sapphire stars, are precious stones. Corundum is vitreous luster with no cleavage, but cracks occur because of the presence of poly twin crystals that are often formed by the base or face of a face. Specific gravity 3.98. Of relatively low silicate igneous and metamorphic rocks and common in alluvial deposits. The U.S. state of North Carolina and Georgia, Russia's Ural mountains, South Africa as the main origin of the transvaal.

Send your message to us

*Email

*TEL

*Quantity

*Unit