High Alumina Brick - AZS Alumina Firebrick Supplied by CNBM

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Packaging Details:

Plywood tray

AZS firebrick

1)-The different content of ZrO2 led to three model:

	Item	Index
	Item	33#	35#	40#
Chemical Composition(%)	Al2O3	49	49	49
	ZrO2	32.0-34.5	35.0-37	40.0-42.0
	SiO2≤	15.5	14	13
	Fe2O3≤	0.1	0.1	0.1
	TiO2≤	0.05	0.05	0.05
	Na2O≤	1.5	1.4	1.3
Physical Composition	Apparent Porosity(%)	2	1.5	1.3
	Bulk Density(g/m³)	3.8	3.89	4.12
	Cold Crushing Strength(MPa)	350	350	350
	Refractorlness(°C)	1710	1710	1730
	0.2MPa Softening temp. Under load(°C)	>1700	>1700	>1700
	Exudation temp. of Glass Phase(°C)	>1400	>1420	>1430
	Corrosion Resistance of Glass Melt (mm/24h)	1.3	1.2	1.1
	Thermal Expansion(%)	0.8	0.8	0.8
	Glass Phase(%)	20	19	18
Bulk Density(g/m³)	PT.QX	3.4	3.45	3.55
	ZWS	3.6	3.65	3.9
	WS	3.7	3.78	3.92

AZS alumina firebrick supplied by CNBM

Q: What are the grades of high alumina bricks?: According to the size of high aluminum brick is divided into: standard brick, special-shaped brick.

Q: Application characteristics of high alumina brick: Reheating line change. If the firing temperature of high alumina brick products is enough and the firing time is enough, the volume is stable, the change of the reheating line is small; on the contrary, the residual shrinkage of clay brick products is caused by recrystallization.

Q: What's the price of high alumina refractory bricks?: Their refractory bricks are of good quality and low ex factory prices. Special high alumina refractory brick factory price of 1900 yuan / ton, a high alumina brick factory price of 1650 yuan / ton... This price applies to standard size, size 230*114*65mm, more products, prices go to see.

Q: Difference between low creep high alumina brick and ordinary high alumina brick: The question is good, these two belong to the high aluminum brick products, when many manufacturers buy, I do not know how to distinguish.

Q: Which is faster for heat transfer between corundum bricks and high alumina bricks?: There must be a difference. They vary in color from the amount of aluminum, the weight, the temperature, and the color.

Q: What are ordinary bricks, refractory bricks, hollow bricks?: Light yellow or brownish. The utility model is mainly used for laying smelting furnaces, and can withstand high temperature between 1580 DEG C and 1770 DEG C. Also called brick. Refractory material of a certain shape and size. According to the preparation process can be divided into bricks, brick, electric melting brick (Rong Zhuzhuan), the refractory insulating bricks; according to the shape and size can be divided into standard brick, brick, brick and other specific type. It can be used as high temperature building materials and structural materials for construction kilns and various thermal equipments, and can undergo various physical, chemical and mechanical changes at high temperature. For example, refractory clay brick, high alumina brick, brick, brick etc..

Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?: The super high alumina brick in high alumina refractory brick has the highest refractoriness, and the corresponding production cost is higher.

Q: What is the difference between high alumina brick and clay brick?: Light clay brick, refractory material is a kind of high porosity, low density, low thermal conductivity of refractory material, refractory materials called lightweight refractories, it includes insulating refractory products, refractory fiber and refractory fiber products. Heat insulation refractory material is characterized by high porosity, general 40%-85%, low volume density, lower than 1.5g/cm3, low thermal conductivity, generally lower than 1.0W (m.K). The utility model has the function of heat insulation of an industrial furnace, and can reduce the heat dissipation loss of the kiln, save energy, and can reduce the quality of the thermal engineering equipment. The mechanical strength, wear resistance and slag resistance of insulating refractory material are poor, and it is not suitable for the load-bearing structure of kiln and direct contact with slag, burden, molten metal and other parts.

Q: How to reduce the harm caused by two times mullite in high alumina refractory material: Two times mullite refers to the content of aluminum is about 70%, in high temperature sintering, the expansion coefficient is large, the thermal expansion rate is high.

Q: How can the refractory brick blast furnace be pulverized and pulverized enough not to be taken away by the wind?: Because the hot air outlet of the top burning hot blast furnace is high, the installation requirement of the hot air manifold is high, and the requirement of the strength of the pillar structure is higher, so the rectangular arrangement of the hot blast stove is arranged. The top burning hot blast stove is located on the furnace top because of burner and hot air valve,Therefore, operation, maintenance and installation all require mechanization and automation. Also, because these water cooled valves are mounted with a high elevation,Therefore, the demand for cooling water supply pressure should be improved accordingly, the use of large top burning hot blast stove, the key lies in the design of high-power high-efficiency short flame burner. The top combustion hot blast furnace absorbs the advantages of internal combustion and external combustion hot blast stoves, and overcomes some of their shortcomings,Its structure can meet the requirements of modern blast furnace for high temperature, high pressure and large scale development,Combustion capacity, while meeting production requirements, has been successfully reduced by many devices,