$Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh System 1$
$Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh System 2$

$Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh$

$Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh System 1$

$Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh System 2$

Raw Materials for Refractory - Abrasive White Fused Alumina (WFA) for Sand Blasting 230 Mesh

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Packaging & Delivery

Packaging Detail:	25kg/plastic bag, 1mt/jumbo bag or as you require
Delivery Detail:	within 7 days after sign the contract or your deposit

Specifications

white fused alumina
Direct Manufacturer
lapping & polishing media
Ceramic grinding wheels

230 mesh abrasive white fused alumina (WFA) for sand blasting

White Fused Alumina/ WFA

White Fused Alumina, a kind of high-grade refractories, was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase alpha-Al2O3.The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.

Advantages

Flexible price policy

Equipped full line of test method.

Brilliant produce&supply&delivery ability

We passed the certification of ISO9001:2000

White fused alumina has Al2O3 content 99% min

All products will be supplied according to customers different requirement.

The laboratory is certified by government Inspection Bureau, that assures its quality stability.

Technical Data:

Application	specification		major chemical content %
Application	specification		AL2O3	Na2O	SiO2	K2O	Fe2O3
abrasive	F	8#-60#	99.5min	0.26max	0.08max		0.06max
		60#-100#	99.5min	0.26max	0.09max		0.06max
		120#-150#	99.5min	0.26max	0.10max		0.06max
		180#-220#	99.5min	0.26max	0.12max		0.10max
		230#-800#	99.3min	0.32max	0.15max		0.10max
		1000#-3000#	99.1min	0.35max	0.18max		0.10max
refractory	Section sand	0-1mm	99.5min	0.29max	0.30max	0.02max	0.06max
		1-3mm
		3-5mm
		5-8mm
		10-20mm
		0.3-1mm
		0-0.3mm
		1-2mm
		0.5-1.5mm
	Fine powder	100#-0	99.0min	0.40max	0.30max	0.03max	0.20max

Moh's hardness	≥9.0
true density(g/cm3)	≥3.95
propotion	≥3.6
porosity	≤8.5

As refractoriness

White Fused Alumina is the main starting material to produce high-grade unshaped and shaped refractoriness and is widely used in the field of iron-steel industry,ceramics,petrochemical industry etc. It is the ideal material to produce the unshaped refractoriness such as large ladle castables,medium and high grade BF trough castables,gunning material,pre-cast shapes and is the main material to produce alumina products such as corundum bricks, corundum and mullite-corundum sagger,refined porous plug bricks, monolithic lance composite nozzle, lining material for high temperature industrial furnaces,etc.

As abrasives

White Fused Alumina can be used as consolidation & coating abrasives, wet or dry sprayed grit, suitable for ultra-precise grinding and polishing in the crystal and electronic industry and can be used to produce high-grade refractoriness. It is suitable to machine high stiffness &high tensile strength materials such as chilled steel, alloyed steel, high-speed steel, high carbon steel, etc. In addition, it can be used as catalyst, insulator, precise foundry sand, etc.

Size available:

Abrasive tool: F10-F220,F230-F1200;P12-P220;

Refractory : 0-1mm,1-3mm,3-5mm,5-10mm;100mesh,325mesh;

Other size is available as required;

Packing:

25kg/bag,40bags/big bag;

1000kg/big bag;

1000kg/big bag with pallet packing;

Other packing is allowed as required.

abrasive white fused alumina (WFA) for sand blasting 230 mesh

Q:What are unshaped fire-resisitance materials?: Refractory castable, refractory plastic material, usually classified according to construction and manufacture method, unfired bricks precast block, refractory pressed into material, refractory cast material, refractory coating, refractory ramming material there are many classification methods

Q:What things and cement mixed can act as refractory?: Cement acts as cementing material. Itself works by refractory aggregate and stir the refractory material for its gelling refractory aggregate both should be fire-resistant.

Q:Where is the production of refractory manganese alloy manufacturers? Manganese is recommended between 63 and 70!: The cut is relatively transparent if you jam, we have also used silicon manganese alloy

Q:Who knows the refractoriness of high temperature lightweight firebricks?: Refractoriness refractory bricks with different melting points, the melting point is liquid and solid crystal phase at a temperature equilibrium. The vast majority of bricks are made of heterogeneous materials. No fixed melting point, it begins to appear to be melting and becomes complete liquid gradually, solid and liquid coexist over a wide temperature range, fusion and softening of refractory is messured by its performance at high temperature. Therefore, refractoriness is the temperature at which the multiphase reaches a certain degree of softening. Refractoriness is an important technical indicator in evaluating refractory bricks, but it can not be seen as the temperature ceiling. GB / T 7322 "Test Methods for high alumina brick refractoriness" alumina brick refractoriness test standards. refractoriness of some commonly used refractory bricks as follows: 1, clay brick 1610? 1750 ℃ ??2,silicon brick 1690? 1730 ℃ 3, crystalline silica 1730? 1770 ℃ 4, hard paste1750? 1770 ℃ 5, high alumina brickx26gt; 1770? 2000 ℃ 6, magnesite refractory bricksx26gt; 2000 ℃ 7, dolomite refractoryx26gt; 2000 ℃

Q:How to understand qualitative and qualitative refractory materials?: Such as amorphous refractory castable, referred to as bulk loading, cast material, ramming material, refractory clay etc., utensils and other special products. Amorphous refractory material products, refractory heat insulating bricks and experimental and industrial crucible, spraying materials, such as burning bricks, electric melting brick, turn it into required shape and process heat treatment in where it is used.

Q:For refractory knowledge. What is the ratio of clay ramming?mass?: Soil aggregates, dispersing agent, water reducing agent, plasticizer, binding agent and powder! ~ Bone meal feed approximately 6, OK

Q:How about the prospect of refractory material?: is developing well. Many plants are required t o use fireproofing materials.

Q:What are included in fireproofing materials?: Incombustible?material of construction fire-proof material Grade A: Cement, stone, steel, coat, glass, aluminium alloy, ceramic tile, etc.; nonflammable material Grade B1: Fireproof?panel, rock wool.

Q:What is the criterion of entry of refractory clay industry?: Refractory clay refers to clay which has a refractoriness of more than 1580 ℃ and can be used as refractory material and bauxite which used as refractory material . In addition to a higher refractoriness, they can keep the stability of volume under high temperature conditions and have slag resistance and thermal shock resistance and mechanical strength, so they are extremely firm after calcination.

Q:Can anyone tell me which materials are fire-proof high temperature resistant material?: Fireproof high temperature resistant materials such as: Quartz, tridymite, cristobalite, chalcedony, flint, opal, quartzite, White silica sand, diatomaceous earth, the silicon oxide (SiO2) contained in these siliceous materials is at least 90% . The silicon oxide in some pure raw material can be above 99 %. Siliceous materials are acidic in high-temperature chemokinesis. when existing metallic oxide or contact with metallic oxide, they will conduct chemical actions and conbine into fusible silicates. Therefore, if the siliceous raw material contains a small amount of metal oxide, its heat resistance will be seriously affected..

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range