Mullite Brick - High Quality Mullite Bricks

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$Fireclay Brick for Coke Oven Refractory$

$High Quality Corundum Brick - Purity Corundum Refractory Bricks$

In mullite (3 2 sio2, al2o3) phase of high aluminum refractory material.General alumina content is between 65% ~ 75%.

Mineral composition in addition to the mullite, contain the alumina lower also contains a small amount of glass phase and

cristobalite;Containing alumina high contains a small amount of corundum.

High refractoriness, can reach more than 1790 ℃.The rul start temperature of 1600 ~ 1700 ℃.Room temperature compressive

strength of 70 ~ 260 mpa.Good thermal shock resistance.A sintered mullite bricks and two fused mullite brick.Sintered mullite brick

with high bauxite clinker as the main raw material, add a small amount of clay or raw bauxite as binder, forming, sintering and made.

Fused mullite brick with high alumina, alumina industry and refractory clay as raw material, adding charcoal or coke fine as a reducing agent,

reduction fused method is used to manufacture after forming.The crystallization of fused mullite is bigger than sintered mullite,

thermal shock resistance than sintered products.Their high temperature performance mainly depends on the content of alumina and

the uniformity of the distribution of mullite phase glass.It is mainly used for hot blast stove top, blast furnace and furnace bottom,

the regenerator of glass furnace, ceramic sintering kiln, petroleum cracking system corner lining, etc.

Q: Aluminum content 38, silicon content 55 What refractory bricks?: Semisilica brick: the content of Al2O3 is 15% ~ 30% of aluminium silicate refractory products. Manufacturing products are semi silica quartz containing impurities or native clay kaolin, refractory clay or kaolin beneficiation tailings and the pyrophyllite

Q: What are the properties of corundum mullite?: Lightweight materials have uniform internal structure, high compressive strength, corrosion resistance, heat shock resistance, oxidation resistance, high temperature and low thermal conductivity.

Q: What is the difference between mullite ceramics and alumina ceramics? Can you tell me something to do with floor tiles?: Mullite is formed by the reaction of alumina with silica. The main difference between him and alumina is that:Hardness: alumina is harder than mullite, but two are tough enough, and are not easy to break.Corrosion resistance: mullite acid is not alkali resistant. Alpha alumina ceramic acid, alkali resistance - for floor tiles, alumina corrosion resistance is too high, unnecessary.

Q: What is the price of refractory bricks?: The construction is superior, the light insulating brick has good machinability, and the construction is convenient and simple, and the labor intensity can be reduced, the construction efficiency can be improved, and the construction period can be shortened. The price is determined by the choice of material and volume density, from several hundred to 5000 yuan, mainly with the choice of material

Q: Mullite bricks in alumina alumina is what?: Mullite (3Al2O3 - 2SiO2) high alumina refractory materials as the main crystal phase. The general alumina content in 65% ~ 75%. In addition to mineral composition of mullite, alumina containing low also contain a small amount of glass phase and cristobalite; alumina containing high also contain a small amount of corundum.

Q: The introduction of mullite brick: General alumina content in 65% ~ 75% between. In addition to mullite, the mineral composition contains lower amounts of glass phase and square quartz, and alumina containing a small amount of corundum.

Q: Mullite brick: High refractoriness, up to 1790 degrees celsius. The softening start temperature is 1600~1700 degrees. The compressive strength at normal temperature is 70 ~ 260MPa. Good thermal shock resistance. The sintered mullite and fused mullite brick two. Sintered mullite brick with high bauxite clinker as the main raw material, adding a small amount of clay or raw bauxite as binder, after molding, sintering and made. Fused mullite brick with high bauxite, alumina and refractory clay as raw material, adding charcoal or coke fines as a reducing agent, formed by reduction of electric melting method to manufacture. The crystallization of fused mullite is larger than that of sintered mullite, and the thermal shock resistance is better than that of sintered products. Their high temperature performance mainly depends on the content of alumina and the uniformity of the phase distribution of mullite and glass. [1]

Q: The difference between the high aluminum corundum brick and corundum mullite brick: Wall tiles and floor tiles are collectively referred to as ceramic tile flooring

Q: What are the varieties of polycrystalline mullite?: Performance comparisonWe used chemical method to produce a microcrystalline structure, excellent thermal stability, temperature exceeds the 300~400. C.The small fiber diameter uniform, slag ball trace, bulk density for 1/2~1/3 products.The large amount of fiber products, high porosity, low coefficient of heat conductivity.It has large surface area, is the ideal material for high temperature catalytic carrier.

Q: Refractory bricks (mullite bricks) can be used on the walls of buildings?: In many architectural design, high-rise fire rating is placed in the important position of the topic, especially when the floor height is more than 20 layers, we have more stringent requirements for the choice of fire resistant materials. The building wall, kitchen flue, boiler flue, flammable zone must use a firewall barrier, in many refractory refractory brick is the product of choice for fire resistance of refractory brick masonry is more stable.