1. Structure of Metallurgical Coke of Coke Strength after Reactivity 64 Description：
Coke is made by high temperature metallurgical coke for blast furnace smelting, casting and gasification. Occurring in the process of coking after recovery and purification of coke oven gas is a high calorific value of fuel, is an important industrial raw material in organic synthesis.
Coke is mainly used for blast furnace ironmaking and used for copper, lead, zinc, titanium, antimony, mercury and other non-ferrous metal smelting of blast furnace, reducing agent, compound and the function of stock column frame.
Blast furnace with Coke instead of charcoal, which laid a foundation for the large-scale of modern blast furnace, is a major milestone in the history of metallurgy.
On China's coke production distribution, the regional distribution imbalance of coking enterprises, mainly distributed in north China, east China and northeast China.
2. Main Features of the Metallurgical Coke of Coke Strength after Reactivity 64：
• Quality assurance
• Mutual benefit
• Preferential price
• Various choice
3. Metallurgical Coke of Coke Strength after Reactivity 64 Images:
4. Metallurgical Coke of Coke Strength after Reactivity 64 Specification:
Parameters | Guarantee | Rejection |
Total Moisture (As received basis) | 5% max | |
Ash (dry basis) | 12.5% max | > 13.5% |
Volatile Matter (dry basis) | 1.5% max | > 1.8% |
Sulphur (dry basis) | 0.65% max | > 0.75% |
Phosphorus (dry basis) | 0.035% max | > 0.045% |
M10 | 7% max | > 9% |
M40 | 84% min | ＜82% |
CSR | 64% min | ＜62% |
CRI | 26% max | > 28% |
Size 30-90 mm | 90% min | |
+90 mm | 5% max | > 8% |
-30mm | 5% max | > 8% |
5. FAQ
How to guarantee the quality of the products？
We have established the international advanced quality management system，every link from raw material to final product we have strict quality test；We resolutely put an end to unqualified products flowing into the market. At the same time, we will provide necessary follow-up service assurance.
- Q: Coke can be used to do what carbon black can be used to do?
- Carbon black in plastics industry is the first use of carbon black pigment coloring, is cheap. Second carbon black in plastics industry use is to have good ultraviolet absorption effect, its application shows quite obvious protective effects in plastic. Third carbon black in plastics industry use is conductive.
- Q: Standard grade two grade coke standard
- Quality index of cokeCoke is a solid product of high temperature carbonization, the main component is carbon, is a crack and irregular pore structure (or porous). The number of cracks has a direct impact on the strength and crushing strength of the coke, the index is generally measured in terms of crack degree (the number of cracks in the unit volume coke). The index of pore structure is mainly expressed by the porosity rate (the percentage of the total volume of coke), which affects the reactivity and strength of coke. Different uses of different coke porosity index requirements, the general requirements of metallurgical coke porosity in the 40 ~ 45%, 35 ~ 40% in coke, coke export demand in about 30%. Coke crack degree and the porosity level, and the coking coal has a direct relationship, such as coal based coke refining, crack, high porosity, low strength; with coal as the foundation of the coal refining coke crack less, low porosity and high strength. The strength of coke is usually represented by two indices of crushing strength and abrasion resistance. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10 value method, commonly used in our country the German migon drum test.
- Q: Ask: coking coke tower tower and what is the relationship?If you can give a working principle to explain what is better!Coking tower in oil coking plant
- Coking plant production capacity on the exclusion of the tower is also on the two: first, the coal tower; the two is coke bin;
- Q: Coke belongs to the coal industry
- Classification and code (2002 Edition) code 25 petroleum processing, coking and nuclear fuel processing industry classification and code (2002 Edition) A agriculture, forest, animal husbandry and fishery 23 printing and record medium reproduction 4900 building decoration 01 24 agricultural stationery and sporting goods manufacturing 50 other building 02 forestry 25 oil processing and coking and nuclear fuel processing F transportation
- Q: What is the sample quantity of coke moisture test? What is the test time? How many degrees? That is the national standard.
- Test procedureDetermination of total moistureA, said the samples size less than 13mm with pre dried and weighed for about 500g (referred to 1g), smooth specimen,B, a sample tray is placed on the 170 a 180 C in the drying box, LH removed after cooling, weighing 5min. C, check dryness, each time 10min, until the two consecutive quality difference in LG, calculate the quality of the last time.Determination of moisture content of samplesA, with the weighing bottle drying to constant quality in advance and has quickly called weighing samples size less than 0.2mm uniform mixing of the 1 + 0.05g (referred to 0.0002g), flat on the weighing bottle.B, will be filled with a sample of the bottle to be placed in the 105-110 drying box drying 1H, remove the weighing bottle immediately covered with lid, put into the dryer to cool to room temperature (about 20min), weighing.C, check of dry, insult 15min, until two consecutive poor quality in 0.001g, take the quality of the last calculation, if quality is weight gain first calculated on the basis of.Five, the calculation of test resultsCalculation of total moisture content according to formula (L):
- Q: F.C Ash S V.M H2O SizeMore than 85 less than 15 less than 8 less than 0.8 less than 1.5 10-70mm over 90%,I would like to ask, what is the size of the corresponding coke? Metallurgical coke or something else, there is no relevant information about, thank youF.C = 85, Ash = 15, H2O = 8, S = 0.8, V.M = 1.5, Size:10-70mm 90% and above, so clear, like the product, the current price?
- Three metallurgical coke: fixed carbon 83-84.5%; calorific value 6500cal/kg; ash < 15%; volatile < 1.9%; all 6% "1%" water; sulfur;Maybe not, I'll give you a web site, find it yourself
- Q: With the number of 1 tons of steel smelting coke
- Because it can reduce energy consumption and reduce costs. So in the iron and steel enterprises coke rate decreased as the main goal of public relations, all the staff for the blast furnace coke rate reduction efforts. A few data in Liaoning, the average coke rate of Anshan and Benxi, Anshan Benxi is 330kg/t, is 360kg/t, that is to say a pig needs 330 360kg and coke production 2 saddle of the iron and steel enterprises. Shanghai Baosteel coke for the best in the country, can reach about 280kg/t. Is about 280kg per ton iron coke, the national leading level.
- Q: I see that there are metallurgical coke and coke on the Internet, what is the difference between them (I hope to be able to say in detail) and a level of two points, how is this going on?.. Where is the quality of coke in China? Hunan good coke plant which? Although the problem is a little bit more, I hope that insiders can give some useful information. Extremely grateful.
- Coke is a special and molten iron cupola coke. Coke is the main fuel cupola molten iron. Its role is to melt the burden and make the hot metal overheating, the support column to maintain good ventilation. Therefore, the foundry coke should have large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough
- Q: What's the connection between coking coal and coke
- Coke: the quality is hard and the hole is thick, the short hair will be wiped awayCoking coal is a kind of bituminous coal with medium caking property and strong caking property. The title of bituminous coal with high degree of coalification. Main coking coal.
- Q: What are the quality indicators of coke
- More than 83 of the fixed carbon; sulfur below the volatile content of less than 1.5; ash around 15 e:Mechanism coke: used in metallurgy; steel plantFiddle coke size 8cm-150cm: of molten iron for casting {;} of motor shell, radiator, mechanical counterweightCoal tar: molten iron; used in the casting of motor shell, radiator, mechanical counterweightLarge modified coke: {for ordinary casting; mechanical parts such as rough parts for 2-3.5 tons of furnace type}The shape of coke size 25cm:{is used for ordinary casting and slightly rigid casting products, such as water pump pipe fittings, such as fire fastener
Send your message to us
Met Coke of Coke Strength after Reactivity 64
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 1000 m.t.
- Supply Capability:
- 100000 m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches