MET COKE 40-100MM
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
You Might Also Like
Parameters | Guarantee |
Moisture (ARB) | 5% max |
Ash (DB) | 12.50% max |
Volatile Matter (DB) | 1.4% max |
Sulphur (DB) | 0.7% max |
Phosphorus (DB) | 0.035% max |
CSR | 62% min |
CRI | 28% max |
M40 | 82% min |
M10 | 8% max |
Size 30-90 mm – 90% min | ON SQUARE MESH SCREEN |
+100 mm | 5% max |
-40mm | 5% max |
Mean Size | 55 mm |
- Q: What is the concept, relationship and difference between coke and coke? The main difference and contact, thank you
- 6, the horizontal type coke oven drying machine(7) gas purification circulating water.... supporting technology(8) dry cooling technology of interlayer water-cooled steam.(9) microcomputer precise dosing system
- Q: Coke is how to produce, what is its purpose?
- Natural coke. Coke can be obtained by high-temperature carbonization of coal:
- Q: What is the use of petroleum coke
- According to the quality can be divided into two kinds of primary and qualified products. Qualified products are divided into six grades. Used in the manufacture of electrodes, calcium carbide, corundum and so on and used as a filling tank, also used as insulating materials and fuel, etc..
- Q: What is the reasonable ratio of coal to coke
- According to the proportion of each unit type, different operation, different existing coal and different coke quality requirements are different and so on, can be said to suggest that the landlord can look at the altar of the myriads of changes, in some aspects of the coal blending, grasp some general principles, and then develop the proportion according to the actual situation.
- Q: Who knows the proportion of pig iron and coke used in Cupola
- Raw material inputs: the main raw material for casting pig iron, scrap steel, manganese, etc.. Under normal circumstances after the melting of ordinary cast iron scrap iron and scrap steel ratio of 9:1 or so, the drying enterprises use pig iron and scrap ratio of about 6:4, according to the requirements of the product. Because pig iron and scrap carbon content is not the same, the higher the carbon content of pig iron is about 4 ~ 4.3, low carbon steel scrap, about 0.8.
- Q: Why is coke used in blast furnace steelmaking?Why not use coal?
- The reason of coke used in blast furnace steelmaking:Coke is the product after the desulfurization of coal, because the removal of sulfur in coal, coal tar and other harmful substances, no longer in the process of steelmaking, the impact on the quality of steel, the formation of unnecessary ingredients.
- Q: The difference between coke and coal
- Coke is a product of wood processing, not the same
- Q: How many degrees of coke ignition temperature can ignite coke
- The average specific heat capacity is 0.808kj/ (KGK) (100 DEG C), 1.465kj/ (KGK) (1000 DEG C);The thermal conductivity is 2.64kj/ (MHK) (room temperature), 6.91kg/ (MHK) (900 DEG C);Ignition temperature (450-650) in air;
- Q: What is coke and how is coke classified?
- Coke definitionBituminous coal in the absence of air is heated to 950-1050 DEG C, after drying, pyrolysis, melting, bonding, curing and contraction of the final stage of this process is made of coke, coking high temperature (high temperature carbonization). By high temperature coking coke for blast furnace smelting, casting and gas generated in the process of coking. After the recovery and after the purification of coke oven gas is not only a high calorific value of fuel, and is an important raw material for organic synthesis industry. Metallurgical coke is coke, coke, iron alloy coke and non-ferrous metal smelting coke for metallurgical coke collectively. More than 90% were used for blast furnace ironmaking blast furnace coke, so often referred to as metallurgical coke is coke. The special cupola molten iron and coke. Coke is the main fuel cupola molten iron. It is melting charge and molten steel overheating, the support column to maintain its good permeability. Therefore, coke should have Large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough.
- Q: What are the national standards for grade two coke?
- Two national standards for metallurgical coke: total sulfur: 0.61 - 0.80; ash: 12.01 - 13.50
Send your message to us
MET COKE 40-100MM
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
Quality Product, Order Online Tracking, Timely Delivery
OKorder Financial Service
Credit Rating, Credit Services, Credit Purchasing
Similar products
Hot products
Hot Searches
Related keywords