High Alumina Brick - High Quality Low Price Anti-Strip Aluminum Brick

High Alumina Brick - High Quality Low Price Anti-Strip Aluminum Brick System 1

High Alumina Brick - High Quality Low Price Anti-Strip Aluminum Brick

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

high quality anti-strip alumina brick
low price alumina brick
supplier with 25 years' experience

Anti-Strip Aluminum Brick Introduction:

The Anti-stripping Aluminum Brick is produced with special bauxite chamotte by adding aragonite or Zro2 and molding under high pressure according to a certain proportion . Featured by strong anti-strip capacity, kalium, sodium, sulphure, chlorine and basic salt resistance and low thermal conductivity, it is an ideal material for the transition zone and decomposing zone of cement kiln.

Anti-Strip Aluminum Brick Specifications

1. Anti-strip alumina brick certified by ISO.
2. Strong anti-strip stability
3.low thermal conductivity

Anti-Strip Aluminum Brick Application:

Widely used in constructing the latter decomposition zone and transitional zone of the rotary cement kiln.

Physical and Chemical Indicators:

Items	Index
Items	YRS-70	YRS-75
Al2O3 %	70	75
ZrO2 %	6-8	-
Refractoriness (°C)	1790	1790
Bulk Density g/cm3 ≥	2.5	2.6
Apparent Porosity %≤	24	23
Cold Crushing Strength MPa≥	60	70
0.2MPCold Crushing Strength °C ≥	1470	1520
Thermal Shock Resistance, Times, [1100°C, water-cooling] ≥	30	25

High Quality Low Price Anti-strip Aluminum Brick

Q: What is the difference between corundum and high alumina??: The main component of high purity 99 corundum brick is corundum sand,90 corundum brick is mainly composed of corundum sand and a small amount of Suzhou soil, mullite.

Q: What is the standard size of high alumina brick?: The country has laid down a number of criteria for the use of refractory bricks to unify market demand.

Q: What is the density of a super high alumina brick and what is the price?: Of course, the transaction price, please choose refractory brick manufacturer is better.

Q: How to reduce porosity of high alumina brick: In order to reduce the porosity of high alumina brick, the corresponding measures should be taken from the selection of raw materials, batching, mixing, molding and firing.The water absorption rate of the first grade high alumina bauxite clinker should be less than 5%, and the water absorption rate of two grade high alumina material should be less than 7%. Fine grinding of soft clay and bauxite clinker with less than 4% water content. Mixed fine milling ingredients with this, can reduce the porosity of bricks.

Q: What are the high temperature refractory mortars made of?: Products used in metallurgy, building materials, machinery, chemical, power industry, industrial thermal furnace, for masonryBuilding clay brick, high alumina brick and corundum brick have the characteristics of full grey seam, good airtightness, high bonding strength, high temperature performance and suitable construction time

Q: What is spalling resistant high alumina brick?: Spalling resistant high alumina brick is a kind of high alumina brick. Antistripping high alumina brick with high grade bauxite and containing Zr02 synthesis as raw material, according to a certain proportion by high pressure molding system in sintering products, products with anti stripping ability, and have the anti erosion potassium, sodium, sulfur, chlorine and alkali salt, low thermal conductivity and other properties that is the transition zone of cement kiln and decomposition of ideal material with remarkable characteristics, the product is good thermal shock resistance, strong ability to adapt to the environment. It is used in the preheating or decomposing furnace, grate cooler and so on.

Q: The difference between ordinary and diatomite brick refractory brick: Insulation products made from diatomaceous brick and porous diatomite. The main raw material is natural porous diatomite, and then a small amount of clay and fuel are added. The volume density of diatomite brick was 0.7g/cm3, compressive strength at room temperature is 1 ~ 2MPa, the coefficient of thermal conductivity at 400 C for 0.13 ~ 0.20W/ (M - K), the apparent porosity is greater than 70%, the coefficient of thermal expansion (1280 degrees) 0.9 x 10 - 6 DEG -1, refractoriness is greater than 1250 DEG C. Mainly used in industrial kilns and other thermal equipment, thermal pipes insulation materials, generally withstand the hot surface temperature of about 1000 degrees celsius. Mainly used in industrial kilns and other thermal equipment, thermal pipes insulation materials, generally withstand the hot surface temperature of about 1000 degrees celsius.

Q: How are the grades of high alumina bricks differentiated?: High alumina brick: aluminium silicate refractory product with a content of three Al2O3 (two) and more than 48%

Q: How does the physicochemical index change when the high alumina brick is used at high temperature?: When the high alumina brick is used at high temperature, the physical and chemical indexes and other constants will not change if the temperature is in the physical and chemical indexes and the softening temperature of the load.

Q: The difference between clay bricks and clay bricks: According to the hole rate: solid brick (no hole or hole rate less than 25% bricks), porous brick (hole rate is equal to or greater than 25%), the size of the hole is small and the number of bricks, usually used in load-bearing parts, higher strength level. Hollow brick (hole rate equal to or greater than 40%, large pore size and small amount of brick, commonly used in non load parts, low strength grade).Solid bricks and porous bricks are mostly used for load-bearing structural walls. Hollow bricks are mostly used in non load bearing structures.

Send your message to us